scholarly journals Drop test reliability of lead-free chip scale packages

2008 ◽  
Author(s):  
Andrew Farris ◽  
Jianbiao Pan ◽  
Albert Liddicoat ◽  
Brian J. Toleno ◽  
Dan Maslyk ◽  
...  
Keyword(s):  
Drop Test ◽  
Test Reliability ◽  
Lead Free

Analysis Methods for Characterizing Drop Test Robustness of Lead-Free FBGAs

2005 ◽  
Author(s):  
J. Walter ◽  
R. Fischer ◽  
C. Birzer
Keyword(s):  
Crack Detection ◽  
Printed Circuit Boards ◽  
Ion Beam ◽  
Drop Test ◽  
Test Reliability ◽  
Lead Free ◽  
Detection Methods ◽  
Lead Free Solder ◽  
Analysis Methods ◽  
Free Solder

Abstract During the last few years the drop test has become more and more important for electronic handheld components. Drop test reliability for lead-free solder interconnects is an extreme challenge today. Thus, the need for improved micro structural diagnostics of new material combinations and crack detection methods has increased. The target of this paper is to summarize detection and analysis methods for solder joint cracks, material characterization [1] and preparation methods of assembled printed circuit boards (PCB) after a drop test to completely understand lead-free solder interconnect reliability in fine pitch ball grid array packages (FBGA). In particular, we will introduce the outstanding advantages of embedded cross-sections combined with ion beam polishing (IBP), dye- or rather resin-penetration, selective tin etch and micro-hardness measurements.

Effect of Solder Composition and Substrate Surface Finish on Board Level Drop Test Reliability

2005 ◽  
Author(s):  
Don-Son Jiang ◽  
Joe Hung ◽  
Yu-Po Wang ◽  
C. S. Hsiao
Keyword(s):  
Solder Joint ◽  
Substrate Surface ◽  
Drop Impact ◽  
Drop Test ◽  
Test Reliability ◽  
Lead Free ◽  
Lead Free Solder ◽  
Snagcu Solder ◽  
Free Solder ◽  
Board Level

For handheld or portable telecommunication devices such as mobile phone, PDA, etc., board level joint reliability during drop impact is a great concern to simulate mishandling during usage. In general, solder composition and substrate surface finish would principally determine the solder joint reliability. Board level drop test reliability of two solder compositions (SnPb and lead free SnAgCu) and surface finishes (Ni/Au and OSP) were examined in this study. The result indicated SnAgCu lead free solder showed poorer reliability life than Sn-Pb solder during drop impact. The crack path in SnPb solder joint almost went through bulk solder near substrate side. However, another IMC/Ni interfacial failure mode near substrate side was found in SnAgCu solder to cause lower reliability. This difference could attribute to higher strength of SnAgCu solder and deformation with higher strain rate in drop test. Comparison between two surface finishes indicated Ni/Au is better than OSP in both SnPb and SnAgCu lead free solder joints. In SnAgCu lead free solder joint with OSP, there are thicker Cu6Sn5 IMC and many large Ag3Sn IMC plates in interface to degrade the interfacial bonding, so drop impact would easily cause the all cracks through IMC/Cu interface and then reduce the reliability.

Lead-Free Chip Scale Packages: Assembly and Drop Test Reliability

2006 ◽  
Vol 29 (1) ◽  
pp. 1-9 ◽  
Author(s):  
Y. Liu ◽  
G. Tian ◽  
S. Gale ◽  
R.W. Johnson ◽  
L. Crane
Keyword(s):  
Drop Test ◽  
Test Reliability ◽  
Lead Free

Failure Analysis of the Solder Joints in Flip-Chip BGA Packages under Free-Drop Test

2014 ◽  
Vol 936 ◽  
pp. 628-632 ◽  
Author(s):  
Guo Zheng Yuan ◽  
Xia Chen ◽  
Xue Feng Shu
Keyword(s):  
Flip Chip ◽  
Solder Joints ◽  
Ball Grid Array ◽  
Test Method ◽  
Drop Test ◽  
Test Reliability ◽  
Internal Crack ◽  
The Real ◽  
Plastic Ball ◽  
Free Drop

The failure of plastic ball grid array under intense dynamic loading was studied in the project. This paper presents the drop test reliability results of SnPb flip-chip on a standard JEDEC drop reliability test board. The failure mode and mechanism of planar array package in the drop test was comprehensively analyzed. High acceleration dropping test method was used to research the reliability of BGA (ball grid array) packages during the free-drop impact process. The model RS-DP-03A drop device was used to simulate the falling behavior of BGA chip packages under the real conditions, The drop condition meets the JEDEC22-B111 standards (pulse peak 1500g, pulse duration 0.5 ms) when dropping from the 650mm height . In the testing, according to the real-time changes of dynamic voltage, the relationship between drop times and different phases of package failure was analyzed. With the dye-penetrated method and optical microscopy, it was easy to observe the internal crack and failure locations. The growth mechanism of the cracks in solder joints under the condition of drop-free was analyzed and discussed.