Impact of Inductively Coupled Plasma Etching Conditions on the Formation of Semi-Polar ( 11 2 ¯ 2 ) and Non-Polar ( 11 2 ¯ 0 ) GaN Nanorods

The formation of gallium nitride (GaN) semi-polar and non-polar nanostructures is of importance for improving light extraction/absorption of optoelectronic devices, creating optical resonant cavities or reducing the defect density. However, very limited studies of nanotexturing via dry etching have been performed, in comparison to wet etching. In this paper, we investigate the formation and morphology of semi-polar (112¯2) and non-polar (112¯0) GaN nanorods using inductively coupled plasma (ICP) etching. The impact of gas chemistry, pressure, temperature, radio-frequency (RF) and ICP power and time are explored. A dominant chemical component is found to have a significant impact on the morphology, being impacted by the polarity of the planes. In contrast, increasing the physical component enables the impact of crystal orientation to be minimized to achieve a circular nanorod profile with inclined sidewalls. These conditions were obtained for a small percentage of chlorine (Cl2) within the Cl2 + argon (Ar) plasma combined with a low pressure. Damage to the crystal was reduced by lowering the direct current (DC) bias through a reduction of the RF power and an increase of the ICP power.

Batch Fabrication of Silicon Nanometer Tip Using Isotropic Inductively Coupled Plasma Etching

This work reports a batch fabrication process for silicon nanometer tip based on isotropic inductively coupled plasma (ICP) etching technology. The silicon tips with nanometer apex and small surface roughness are produced at wafer-level with good etching homogeneity and repeatability. An ICP etching routine is developed to make silicon tips with apex radius less than 5 nm, aspect ratio greater than 5 at a tip height of 200 nm, and tip height more than 10 μm, and high fabrication yield is achieved by mask compensation and precisely controlling lateral etch depth, which is significant for large-scale manufacturing.

Nanocone Structures Enhancing Nitrogen-Vacancy Center Emissions in Diamonds

In this study, nitrogen-vacancy center emissions from nanocone structures fabricated on diamond surfaces by gold film annealing and inductively coupled plasma etching techniques were characterized. First, the diamond substate deposited with gold film was annealed to form a nano-sized dot mask. Second, through inductively coupled plasma etching, nanocone-shaped structures were fabricated using optimized gold dots as masks. Finally, the as-fabricated nanocone and planar structures were investigated with photoluminescence experiments at temperatures ranging from room temperature to 80 K, with the results showing approximately two-fold higher emission values for nitrogen-vacancy centers from nanocones.