Thin Film Phosphate Based Bioactive Substrates

1995 ◽  
Vol 414 ◽  
Author(s):  
S Langstaff ◽  
M Sayer ◽  
L Weaver ◽  
S Pugh ◽  
T Smith
Keyword(s):  
Thin Film ◽  
Thin Films ◽  
Calcium Phosphate ◽  
Tricalcium Phosphate ◽  
Sintering Temperature ◽  
Sol Gel ◽  
Crystalline Phases ◽  
Sintering Conditions ◽  
Quartz Substrates ◽  
Osteoclast Resorption

AbstractCalcium phosphate based thin films prepared by colloidal sol-gel slow draw dipping of quartz substrates are bioactive to both osteoclast resorption and osteoblast deposition. The bioactivity is related to the presence of mixed crystalline phases in the films generated under different sintering conditions. As the sintering temperature was increased from 800°C to 1000°C, a transition in film composition from calcium hydroxylapatite to alpha-tricalcium phosphate is achieved.

Preparation of YSZ Thin Film on Porous Electrode of SOFC

1998 ◽  
Vol 547 ◽  
Author(s):  
H. Nagamoto ◽  
H. Ikewaki
Keyword(s):  
Thin Film ◽  
Thin Films ◽  
Hydrogen Permeation ◽  
Sintering Temperature ◽  
Sol Gel ◽  
Porous Electrode ◽  
Gel Method ◽  
Sol Gel Method ◽  
Ysz Thin Film ◽  
Gas Tight

AbstractPorous electrode substrate of La0.7Sr0.2MnO3 was used as the support for the deposition of YSZ thin films. The porosity of the electrode substrate was controlled by sintering temperature and particle size of powders. Thin films of YSZ were fabricated on the electrode by sol-gel method. The YSZ film fabricated by 10-fold coating with 0.05M YSZ sol containing TEA was continuous and crack-free one of 5 mm in thickness. However, hydrogen permeation measurement showed that there was a very small leakage of hydrogen in the fabricated film. In addition to sol-gel method, another technique such as EVD should be employed to make the film completely gas-tight.

Lower crystallization temperature of sol-gel PbTiO3 on Ti/Pt-coated substrates

1999 ◽  
Vol 14 (6) ◽  
pp. 2369-2372 ◽  
Author(s):  
R. E. Avila ◽  
T. P. Velilla ◽  
P. J. Retuert
Keyword(s):  
Thin Film ◽  
Thin Films ◽  
Refractive Index ◽  
Sintering Temperature ◽  
Perovskite Phase ◽  
Sol Gel ◽  
Second Phase ◽  
X Ray Diffraction ◽  
Range Analysis ◽  
X Ray

PbTiO3 (PT) thin films have been deposited by sol-gel on Pt/Si, SiO2/Si, Pt/Ti/SiO2/Si, and Ti/Pt/Ti/SiO2/Si and annealed for 45 min in the 400–670 °C range. Analysis by x-ray diffraction (XRD) and spectroscopic ellipsometry shows that the Ti overlayer promotes early crystallization in the tetragonal perovskite phase, reducing the presence of a second phase, tentatively identified as pyrochlore, starting by 450 %C. The refractive index and extinction coefficient (n, k) of the PT film increase rapidly with the sintering temperature in the range of 450–570 °C and saturate by 570 °C to values of n varying from 2.4 to 2.9, and k from 0.03 to 0.3, over the 1.65–2.95 eV range. Most of the increase of n is related to thin film densification.

Epitaxial Growth of Sr0.3Ba0.7Nb2O6 Thin Films Prepared by Sol-Gel Process

1999 ◽  
Vol 606 ◽  
Author(s):  
Keishi Nishio ◽  
Jirawat Thongrueng ◽  
Yuichi Watanabe ◽  
Toshio Tsuchiya
Keyword(s):  
Thin Film ◽  
Thin Films ◽  
Epitaxial Growth ◽  
Raw Materials ◽  
Substrate Surface ◽  
Sol Gel ◽  
Tungsten Bronze ◽  
Monomethyl Ether ◽  
Tetragonal Tungsten Bronze ◽  
Sol Gel Process

AbstructWe succeeded in the preparation of strontium-barium niobate (Sr0.3Ba0.7Nb2O6 : SBN30)that have a tetragonal tungsten bronze type structure thin films on SrTiO3 (100), STO, or La doped SrTiO3 (100), LSTO, single crystal substrates by a spin coating process. LSTO substrate can be used for electrode. A homogeneous coating solution was prepared with Sr and Ba acetates and Nb(OEt)5 as raw materials, and acetic acid and diethylene glycol monomethyl ether as solvents. The coating thin films were sintered at temperature from 700 to 1000°C for 10 min in air. It was confirmed that the thin films on STO substrate sintered above 700°C were in the epitaxial growth because the 16 diffraction spots were observed on the pole figure using (121) reflection. The <130> and <310> direction of the thin film on STO were oriented with the c-axis in parallel to the substrate surface. However, the diffraction spots of thin film on LSTO substrate sintered at 700°C were corresponds to the expected pattern for (110).

Effects of Annealing Temperature on Morphology and Dielectric Property of BiFeO3 Films

2012 ◽  
Vol 512-515 ◽  
pp. 1736-1739
Author(s):  
Li Li Zhang ◽  
Guo Qiang Tan ◽  
Meng Cheng ◽  
Hui Jun Ren ◽  
Ao Xia
Keyword(s):  
Thin Film ◽  
Thin Films ◽  
Dielectric Property ◽  
Annealing Temperature ◽  
Raw Materials ◽  
Sol Gel ◽  
Frequency Range ◽  
Annealing Temperatures ◽  
Pure Phase ◽  
Lower Loss

Fe(NO3)3•9H2O and Bi(NO3)3•5H2O were used as raw materials. BiFeO3 thin films were prepared by sol-gel method. The effects of annealing temperatures on the morphology and dielectric property of the thin films were studied. XRD results show that the multi-crystal thin films with pure phase are obtained when annealed at 500°C and 550°C. But annealing at 580°C will lead to the appearance of Bi2.46Fe5O12 phase.AFM images show that as the increase of annealing temperatures the surface toughness of the thin film is decreased, but the surface undulation of the thin films is decreased gradually. Within the frequency range of 1KHz~1MHz, the dielectric constant of BiFeO3 thin films is kept over 125 and it does not change very much from 500°C to 580°C. Annealed at 550°C, the BiFeO3 thin films with the lower loss are obtained. At 1MHz, the dielectric loss is 0.12.

PREPARATION AND FERROELECTRIC PROPERTY OF (100)-ORIENTED Ca0.4Sr0.6Bi4Ti4O15 THIN FILM ON Pt/Ti/SiO2/Si SUBSTRATE

2010 ◽  
Vol 17 (05n06) ◽  
pp. 445-449 ◽  
Author(s):  
SUHUA FAN ◽  
QUANDE CHE ◽  
FENGQING ZHANG
Keyword(s):  
Thin Film ◽  
Thin Films ◽  
Ferroelectric Property ◽  
Remanent Polarization ◽  
Sol Gel ◽  
Xrd Analysis ◽  
Sem Analysis ◽  
Si Substrate ◽  
Degree Of Orientation ◽  
Equiaxed Grains

The (100)-oriented Ca0.4Sr0.6Bi4Ti4O15(C0.4S0.6BTi ) thin film was successfully prepared by a sol-gel method on Pt/Ti/SiO2/Si substrate. The orientation and formation of thin films under different annealing schedules were studied using XRD and SEM. XRD analysis indicated that (100)-oriented C0.4S0.6BTi thin film with degree of orientation of I(200)/I(119) = 1.60 was prepared by preannealing the film at 400°C for 3 min followed by rapid thermal annealing at 800°C for 5 min. SEM analysis further indicated that the (100)-oriented C0.4S0.6BTi thin film with a thickness of about 800 nm was mainly composed of equiaxed grains. The remanent polarization and coercive field of the film were 16.1 μC/cm2 and 85 kV/cm, respectively.

scholarly journals Preparation of Glass Plate-Supported Nanostructure ZnO Thin Film Deposited by Sol-Gel Spin-Coating Technique and Its Photocatalytic Degradation to Monoazo Textile Dye

2008 ◽  
Vol 2008 ◽  
pp. 1-5 ◽  
Author(s):  
Mohammad Hossein Habibi ◽  
Mohammad Khaledi Sardashti
Keyword(s):  
Thin Film ◽  
Thin Films ◽  
Photocatalytic Degradation ◽  
Spin Coating ◽  
Sol Gel ◽  
Glass Plate ◽  
Zno Thin Films ◽  
Visible Range ◽  
Textile Dye ◽  
Axis Orientation

Glass plate-supported nanostructure ZnO thin films were deposited by sol-gel spin coating. Films were preheated at275∘Cfor 10 minutes and annealed at 350, 450, and550∘Cfor 80 minutes. The ZnO thin films were transparent ca 80–90% in visible range and revealed that absorption edges at about 370 nm. Thec-axis orientation improves and the grain size increases which was indicated by an increase in intensity of the (002) peak at34.4∘in XRD corresponding to the hexagonal ZnO crystal. The photocatalytic degradation of X6G an anionic monoazo dye, in aqueous solutions, was investigated and the effects of some operational parameters such as the number of layer and reusability of ZnO nanostructure thin film were examined. The results showed that the five-layer coated glass surfaces have a very high photocatalytic performance.

The Ferroelectric and Electrical Properties of CaBi4Ti4O15 Thin Films Prepared by Sol-Gel Technology

2011 ◽  
Vol 239-242 ◽  
pp. 891-894 ◽  
Author(s):  
Tsung Fu Chien ◽  
Jen Hwan Tsai ◽  
Kai Huang Chen ◽  
Chien Min Cheng ◽  
Chia Lin Wu
Keyword(s):  
Thin Film ◽  
Thin Films ◽  
Sol Gel ◽  
Morphological Characterization ◽  
Experimental Result ◽  
X Ray Diffraction ◽  
Solution Deposition ◽  
Capacitance Voltage ◽  
Preferential Crystal Orientation

In this study, thin films of CaBi4Ti4O15with preferential crystal orientation were prepared by the chemical solution deposition (CSD) technique on a SiO2/Si substrate. The films consisted of a crystalline phase of bismuth-layer-structured dielectric. The as-deposited CaBi4Ti4O15thin films were crystallized in a conventional furnace annealing (RTA) under the temperature of 700 to 800°C for 1min. Structural and morphological characterization of the CBT thin films were investigated by X-ray diffraction (XRD) and field-emission scanning electron microscope (FE-SEM). The impedance analyzer HP4294A and HP4156C semiconductor parameters analyzer were used to measurement capacitance voltage (C-V) characteristics and leakage current density of electric field (J-E) characteristics by metal-ferroelectric-insulator- semiconductor (MFIS) structure. By the experimental result the CBT thin film in electrical field 20V, annealing temperature in 750°C the CBT thin film leaks the electric current is 1.88x10-7A/cm2and the memory window is 1.2V. In addition, we found the strongest (119) peak of as-deposited thin films as the annealed temperature of 750°C

scholarly journals Microstructure Evolution of Ag/TiO2 Thin Film

2021 ◽  
Vol 7 (1) ◽  
pp. 14
Author(s):  
Dewi Suriyani Che Halin ◽  
Kamrosni Abdul Razak ◽  
Mohd Arif Anuar Mohd Salleh ◽  
Mohd Izrul Izwan Ramli ◽  
Mohd Mustafa Al Bakri Abdullah ◽  
...  
Keyword(s):  
Thin Film ◽  
Thin Films ◽  
Growth Rate ◽  
Synchrotron Radiation ◽  
Tio2 Thin Film ◽  
Sol Gel ◽  
Tio2 Thin Films ◽  
Contact Mode ◽  
X Ray ◽  
Radiation Imaging

Ag/TiO2 thin films were prepared using the sol-gel spin coating method. The microstructural growth behaviors of the prepared Ag/TiO2 thin films were elucidated using real-time synchrotron radiation imaging, its structure was determined using grazing incidence X-ray diffraction (GIXRD), its morphology was imaged using the field emission scanning electron microscopy (FESEM), and its surface topography was examined using the atomic force microscope (AFM) in contact mode. The cubical shape was detected and identified as Ag, while the anatase, TiO2 thin film resembled a porous ring-like structure. It was found that each ring that coalesced and formed channels occurred at a low annealing temperature of 280 °C. The energy dispersive X-ray (EDX) result revealed a small amount of Ag presence in the Ag/TiO2 thin films. From the in-situ synchrotron radiation imaging, it was observed that as the annealing time increased, the growth of Ag/TiO2 also increased in terms of area and the number of junctions. The growth rate of Ag/TiO2 at 600 s was 47.26 µm2/s, and after 1200 s it decreased to 11.50 µm2/s and 11.55 µm2/s at 1800 s. Prolonged annealing will further decrease the growth rate to 5.94 µm2/s, 4.12 µm2/s and 4.86 µm2/s at 2400 s, 3000 s and 3600 s, respectively.

Synthesis and Characterizations of Strontium Substituted Hydroxyapatite Thin Films

2010 ◽  
Vol 93-94 ◽  
pp. 231-234
Author(s):  
B. Hongthong ◽  
Satreerat K. Hodak ◽  
Sukkaneste Tungasmita
Keyword(s):  
Thin Film ◽  
Thin Films ◽  
Chemical Composition ◽  
Spin Coating ◽  
Phase Structure ◽  
Sol Gel ◽  
Cross Linking ◽  
X Ray Diffraction ◽  
X Ray ◽  
Sol Gel Process

Strontium substituted hydroxyapatite(SrHAp) were fabricated both in the form of powder as reference and thin film by using inorganic precursor reaction. The sol-gel process has been used for the deposition of SrHAp layer on stainless steal 316L substrate by spin coating technique, after that the films were annealed in air at various temperatures. The chemical composition of SrHAp is represented (SrxCa1-x)5(PO4)3OH, where x is equal to 0, 0.5 and 1.0. Investigations of the phase structure of SrHAp were carried out by using X-ray diffraction technique (XRD). The results showed that strontium is incorporated into hydroxyapatite where its substitution for calcium increases in the lattice parameters, and Sr3(PO4)2 can be detected at 900°C. The SEM micrographs showed that SrHAp films exhibited porous structure before develop to a cross-linking structure.

Synthesis and Film Investigation of Titania

2013 ◽  
Vol 832 ◽  
pp. 128-131
Author(s):  
Sharipah Nadzirah ◽  
Uda Hashim
Keyword(s):  
Thin Film ◽  
Electron Microscopy ◽  
Thin Films ◽  
Scanning Electron Microscopy ◽  
Titanium Dioxide ◽  
Sol Gel ◽  
Titanium Butoxide ◽  
Before And After ◽  
Scanning Electron ◽  
Spin Coater

Titania or titanium dioxide (TiO2) thin film has been synthesized via sol-gel method with monoethanolamine (MEA) as a catalyst. The mixing of titanium butoxide as a precursor, ethanol as a solvent and MEA were stirred using magnetic stirrer under ambient temperature [. The TiO2solution prepared then was deposited on SiO2substrates using spin-coater and the coated films were annealed at 600°C. Finally, both before and after annealed TiO2thin films were characterized using Field Emission Scanning Electron Microscopy (FESEM). The obtained results show the different TiO2particles formation before and after annealed.