scholarly journals Effect of annealing atmosphere on LiMn2O4 for thin film Li-ion batteries from aqueous chemical solution deposition

2016 ◽  
Vol 4 (47) ◽  
pp. 18457-18469 ◽  
Author(s):  
G. Maino ◽  
J. D'Haen ◽  
F. Mattelaer ◽  
C. Detavernier ◽  
A. Hardy ◽  
...  
Keyword(s):  
Thin Film ◽  
Thin Films ◽  
Chemical Solution Deposition ◽  
Annealing Atmosphere ◽  
Li Ion Batteries ◽  
Chemical Solution ◽  
Solution Deposition ◽  
Current Collectors ◽  
Li Ion

Aqueous CSD provides LMO thin films at low T in a N2 ambient, eliminating issues with stacking and sensitive current collectors.

Preparation of (La,Sr)MnO3 Thin Film by Chemical Solution Deposition

2013 ◽  
Vol 566 ◽  
pp. 187-190
Author(s):  
Keiichi Sasajima ◽  
Hiroshi Uchida
Keyword(s):  
Thin Film ◽  
Thin Films ◽  
Electrical Resistivity ◽  
Silicon Substrate ◽  
Chemical Solution Deposition ◽  
Buffer Layers ◽  
Chemical Solution ◽  
Solution Deposition ◽  
Ferroelectric Capacitor ◽  
Lower Electrical Resistivity

Thin films of (La,Sr)MnO3 (LSMO) were fabricated by industrial-versatile chemical solution deposition (CSD) technique. Well [100]-oriented LSMO films were fabricated at 650-750 °C by use of buffer layers of LaNiO3 buffer layer on a silicon substrate. The product of lower electrical resistivity is promising as an electrode of fatigue-free ferroelectric capacitor.

Influence of Mn dopants on the structure and multiferroic properties of a Bi0.90Ho0.10FeO3 thin film

RSC Advances ◽  
2015 ◽  
Vol 5 (54) ◽  
pp. 43594-43600 ◽  
Author(s):  
Wei Ye ◽  
Guoqiang Tan ◽  
Xia Yan ◽  
Huijun Ren ◽  
Ao Xia
Keyword(s):  
Thin Film ◽  
Thin Films ◽  
Chemical Solution Deposition ◽  
Chemical Solution ◽  
Solution Deposition ◽  
Multiferroic Properties

Mn substituted Bi0.90Ho0.10FeO3 (BHFO) thin films having the compositions Bi0.90Ho0.10Fe1−xMnxO3 (BHFMO) (x = 0, 0.01, 0.03, 0.05) were synthesized via chemical solution deposition.

Epitaxial growth of PbZr0.5Ti0.5O3 thin films on SrRuO3/SrTiO3 substrates using chemical solution deposition: Microstructural and ferroelectric properties

2001 ◽  
Vol 16 (6) ◽  
pp. 1739-1744 ◽  
Author(s):  
J. H. Kim ◽  
Youngman Kim ◽  
A. T. Chien ◽  
F. F. Lange
Keyword(s):  
Thin Film ◽  
Thin Films ◽  
Chemical Solution Deposition ◽  
Ferroelectric Properties ◽  
Chemical Solution ◽  
Solution Deposition ◽  
Pzt Thin Films ◽  
Chemical Solution Deposition Method ◽  
Pzt Thin Film ◽  
Film Substrate

Epitaxial PbZr0.5Ti0.5O3 (PZT) thin films were grown on top of a SrRuO3 epitaxial electrode layer on a (100) SrTiO3 substrate by the chemical solution deposition method at various temperatures. The microstructure of the PZT thin films was investigated by x-ray diffraction and transmission electron microscopy, and the ferroelectric properties were measured using the Ag/PZT/SRO capacitor structure. In the PZT thin film annealed at low temperature (450 °C/1h), both the perovskite PZT phase at the film/substrate interface and the fluorite PZT phase in the upper region of the film were obtained. It exhibited nonferroelectric properties. The PZT thin film annealed at temperature as low as 525 °C had only a perovskite tetragonal phase and the epitaxial orientational relationship of (001)[010]PZT∥(001)[010]SRO∥(001)[010]STOwith the substrate, and shows a ferroelectric property. The remnant (Pr) and saturation polarization (Ps) density of the sample annealed at 600 °C/1h were measured to be Pr ˜ 51.4 μC/cm2 and Ps ˜ 62.1 μC/cm2 at 5 V, respectively. The net switched polarization dropped only to 98% of its initial value after 7 × 108 fatigue cycles.

The Effect of Bi-excess Surface Layers on BiFeO3 Thin Films Prepared by Chemical Solution Deposition

2007 ◽  
Vol 1034 ◽  
Author(s):  
Yoshitaka Nakamura ◽  
Seiji Nakashima ◽  
Dan Ricinschi ◽  
Masanori Okuyama
Keyword(s):  
Thin Film ◽  
Thin Films ◽  
Chemical Solution Deposition ◽  
Remanent Polarization ◽  
Bottom Surface ◽  
Chemical Solution ◽  
Surface Layers ◽  
Solution Deposition ◽  
Excess Surface ◽  
Imperfect Crystal

AbstractWe have investigated the effect of Bi-excess surface layers of stoichiometric BiFeO3 thin films prepared by chemical solution deposition. A stoichiometric BiFeO3 thin film with both the Bi-excess top and bottom surface layers shows improved crystallinity with the remanent polarization of 65 μC/cm2 at 80 K, which is larger than BiFeO3 film prepared by the same process using stoichiometric solution. These results are attributed to the reduction of the imperfect crystal at the interface between BiFeO3 film and electrode. Stoichiometric BiFeO3 thin film with Bi-excess top and bottom surface layers also reserves the magnetic property of stoichiometric film. Stoichiometric BiFeO3 thin films with Bi-excess surface layers are an effective way to obtain good multiferroic properties.

Ca3Co4O9/polycrystalline Al2O3: an effective template for c-axis oriented layered cobaltate thin films by chemical solution deposition

RSC Advances ◽  
2015 ◽  
Vol 5 (23) ◽  
pp. 17746-17750 ◽  
Author(s):  
Renhuai Wei ◽  
Xianwu Tang ◽  
Jie Yang ◽  
Jianming Dai ◽  
Changhao Liang ◽  
...  
Keyword(s):  
Thin Film ◽  
Thin Films ◽  
Chemical Solution Deposition ◽  
Chemical Solution ◽  
Solution Deposition

Ca3Co4O9/polycrystalline Al2O3 thin film is an effective template for growth of c-axis oriented layered cobaltate thin films.

Sign in / Sign up

Export Citation Format

Share Document