This chapter explains how decarburization can occur during carburizing processes and how to limit the severity of its effects. It describes the reactions and conditions that result in a loss of carbon atoms and how they vary with changes in the physical metallurgy of the affected material and the processing environment. It examines the characteristic features of decarburized microstructures and assesses their influence on hardness, residual stresses, and fatigue and fracture behaviors. It also discusses corrective measures and practical considerations regarding their use.

Core Properties and Case Depth

The design of case-hardened components is an iterative process, requiring the consideration of multiple interrelated factors. This chapter walks readers through the steps involved in selecting an appropriate material and assessing the influence of alloy composition and cooling rate on core properties including hardenability, microstructure, tensile and yield strength, ductility, toughness, and fatigue resistance. It likewise explains how carbon affects case hardenability, surface hardness, and case toughness and how case depth influences residual stresses and bending and contact fatigue. It also discusses the effect of quenching methods and addresses the issue of distortion.

Carbides

This chapter discusses the formation of free carbides and their effect on case-carburized components. It explains how alloying elements influence the composition and structure of carbide phases produced at cooling rates typical of carburizing process. It describes the morphology and distribution of the various types of carbides formed and explains how they affect mechanical properties such as hardness, residual stresses, fatigue and fracture behaviors, and wear resistance. It also provides guidance for determining what processing conditions to avoid and when and why parts should be rejected.

Retained Austenite

This chapter addresses the issue of retained austenite in quenched carburized steels. It explains why retained austenite can be expected at the surface of case-hardened components, how to estimate the amount that will be present, and how to effectively stabilize or otherwise control it. It presents detailed images and data plots showing how retained austenite appears and how it influences hardness, tensile properties, residual stresses, fatigue and fracture behaviors, and wear resistance.

Influential Microstructural Features

This chapter is a study of the microstructure of case-hardened steels. It explains what can be learned by examining grain size, microcracking, nonmetallic inclusions, and the effects of microsegregation. It identifies information-rich features, describing their ideal characteristics, the likely cause of variations observed, and their effect on mechanical properties and behaviors. The discussions throughout the chapter are aided by the use of images, diagrams, data plots, and tables.

Introduction and Perspectives

This chapter provides a brief but practical overview of the case carburizing process. It discusses the benefits and challenges of the process and compares and contrasts it with other hardening methods. It explains how design allowables and safety factors compensate for unknowns and familiarizes readers with the steps involved in determining case depth and verifying that case carbon requirements have been met.

Internal Oxidation

Gas carburizing is known to promote internal oxidation in steel which can adversely affect certain properties. This chapter discusses the root of the problem and its effect on component lifetime and performance. It explains that gas-carburizing atmospheres contain water vapor and carbon dioxide, providing oxygen that reacts with alloying elements, particularly manganese, chromium, and silicon. It examines the composition and distribution of oxides produced in different steels and assesses the resulting composition gradients. It describes how these changes influence the development of high-temperature transformation products as well as microstructure, hardenability, and carbon content and properties such as fatigue and fracture behaviors, hardness, and wear resistance. It also explains how to manage internal oxidation through material design, process control, and other measures.

Postcarburizing Thermal Treatments

This chapter familiarizes readers with tempering and refrigeration treatments and their effect on case-carburized parts. It explains how tempering makes such parts easier to machine, more structurally and dimensionally stable, and more durable in certain applications. It identifies key process parameters and provides test data showing how they affect hardness, yield strength, bending and contact fatigue, and fracture toughness. It also addresses potential problems stemming from process-related factors such as the presence of hydrogen and the effects of aging and grinding. In regard to refrigeration, the chapter explains that it is not uncommon for subzero treatments to be included in the production of carburized parts whether as a standard procedure or optional step. Subzero cooling promotes the transformation of retained austenite to martensite, thereby increasing surface hardness and reducing the propensity of quenched carburized steels to burn and crack during surface grinding. The chapter includes numerous data plots and tables showing how the various treatments influence hardness, wear resistance, tensile properties, and fatigue and fracture behaviors.

Postcarburizing Mechanical Treatments

Mechanical treatments such as grinding and shot peening are often employed in the production of case-carburized parts. Grinding, besides restoring precision, removes carbide films, internal oxidation, and high-temperature transformation products. Shot peening strengthens component surfaces and induces a stress state that increases fatigue resistance. This chapter describes both processes as well as roller burnishing. It explains how these treatments are applied and how they influence the microstructure, properties, and behaviors of case-hardened components. It also addresses process challenges, particularly in regard to grinding.