High Temperature Mechanical Properties and Wear Performance of B4C/Al7075 Metal Matrix Composites

In this study, high volume fraction B4C reinforced Al matrix composites were fabricated with a liquid pressing process. Microstructural analysis by scanning electron microscope and a transmission electron microscopy shows a uniform distribution of the B4C reinforcement in the matrix, without any defects such as pore and unwanted reaction products. The compressive strength and wear properties of the Al7075 matrix and the composite were compared at room temperature, 100, 200, and 300 °C, respectively. The B4C reinforced composite showed a very high ultimate compression strength (UCS) over 1.4 GPa at room temperature. The UCS gradually decreased as the temperature was increased, and the UCS of the composite at 300 °C was about one third of the UCS of the composite at room temperature. The fractography of the compressive test specimen revealed that the fracture mechanism of the composites was the brittle fracture mode at room temperature during the compression test. However, at the elevated temperature, AMCs had a mixed mode of a brittle and ductile fracture mechanism under the compressive load. The composite produced by a liquid pressing process also showed superior wear resistance compared with the Al matrix. The result of the wear test indicates that the wear loss of the Al matrix at 300 °C was two times higher than that of the AMCs, which is attributed to the formation of a mechanically mixed layer (MML) in the composites at the high temperature.

Microstructural Evolution and Strengthening Mechanism of SiC/Al Composites Fabricated by a Liquid-Pressing Process and Heat Treatment

Aluminum alloy (Al7075) composites reinforced with a high volume fraction of silicon carbide (SiC) were produced by a liquid-pressing process. The characterization of their microstructure showed that SiC particles corresponding to a volume fraction greater than 60% were uniformly distributed in the composite, and Mg2Si precipitates were present at the interface between the matrix and the reinforcement. A superior compressive strength (1130 MPa) was obtained by an effective load transfer to the hard ceramic particles. After solution heat treatment and artificial aging, the Mg2Si precipitates decomposed from rod-shaped large particles to smaller spherical particles, which led to an increase of the compressive strength by more than 200 MPa. The strengthening mechanism is discussed on the basis of the observed microstructural evolution.