Effect of Holding Time of Decarbonization Annealing on Recrystallization in Fe-3.2%Si-0.047Nb% Low-Temperature Oriented Silicon Steel

In this study, the effects of decarburization annealing time on the primary recrystallization microstructure, the texture and the magnetic properties of the final product of 0.047% Nb low-temperature grain-oriented silicon steel were investigated by means of OM, EBSD and XRD. The results show that when the decarburization annealing condition is 850 °C for 5 min, the uniform fine primary recrystallization microstructure can be obtained, and the content of favorable texture {111} < 112 > is the highest while that of unfavorable texture {110} < 112 > is the lowest, which is mostly distributed near the central layer. At the same time, there are the most high-energy grain boundaries with high mobility in the primary recrystallization microstructure of the sample annealed at 850 °C for 5 min, and the ∑9 boundary has the highest percentage of grain boundaries. The samples with different decarburization annealing time were annealed at high temperature. It was found that perfect secondary recrystallization occurred after high-temperature annealing when the decarburization annealing condition was 850 °C for 5 min. The texture component was characterized by a single Goss texture, and the size of the Goss grain reached 4.6mm. Under such annealing conditions, the sample obtained shows the optimal soft magnetic properties of B800 = 1.89T and P1.7/50 = 1.33 w/kg.

Cooperative effects of surface and interface treatments in a hematite (α-Fe2O3) photo-anode on its photo-electrochemical performance

To enhance the efficiency of the oxygen evolution reaction of hematite (α-Fe2O3), we engineered both the surface of the hematite nanorods and the FTO/hematite interface simultaneously with an optimal annealing condition.

Quenching and Partitioning of Multiphase Aluminum-Added Steels

The quenching and partitioning response following intercritical annealing was investigated for three lean TRIP-type high-Al steel compositions. Depending on the intercritical austenite fraction following annealing, the steels assumed either a ferrite/martensite/retained austenite microstructure or a multiphase structure with ferritic, bainitic and martensitic constituents along with retained austenite. The amount of retained austenite was found to correlate with the initial quench temperature and, depending on the intercritical annealing condition prior to initial quenching, with the uniform and ultimate elongations measured in tensile testing.