scholarly journals Mechanical Properties and Microstructure of W-6Ni-4Co Alloy by a Two-Step Sintering Process

Metals ◽  
2019 ◽  
Vol 9 (6) ◽  
pp. 680 ◽  
Author(s):  
Hongfeng Dong ◽  
Peiyou Li ◽  
Taotao Ai ◽  
Wenhu Li
Keyword(s):  
Mechanical Properties ◽  
Mechanical Alloying ◽  
Solid Phase ◽  
Particle Sizes ◽  
Sintering Process ◽  
Dwelling Time ◽  
Milled Powders

The mechanical properties and microstructure of W-6Ni-4Co alloy through solid phase sintering and two-step sintering process were investigated. The results demonstrated that the particle sizes of W-6Ni-4Co alloy milled powders increased firstly and decreased later during a mechanical alloying process. The shape of alloy milled powders affected that of grains in alloy by solid phase sintering. The shape of W-rich particles in the alloys changed from stripes to network, to polygonal and to subsphaeroidal finally during two-step sintering process. The mechanical properties could be attributed to the densification and microstructure of alloys, and increased during two-step sintering with short dwelling time.

Mechanical Properties Improvement of Porous Titanium-Bioglass Nanocomposites by Mechanical Alloying

2013 ◽  
Vol 829 ◽  
pp. 319-323
Author(s):  
Saeed Riahi ◽  
Mohammad Rajabi ◽  
Sayed Mahmood Rabiee
Keyword(s):  
Mechanical Properties ◽  
Mechanical Alloying ◽  
Biomedical Application ◽  
Diffraction Method ◽  
Porous Titanium ◽  
Sintering Process ◽  
Compression Tests ◽  
X Ray Diffraction ◽  
Mechanically Alloyed ◽  
Space Holder

In this study, porous titanium-10 wt.% bioglass nanocomposites were fabricated by the combination of mechanical alloying and a space holder sintering process. The mixed powders were mechanically alloyed for 15 h. The blended Ti-Bioglass was mixed with 30 wt.% carbamide as a space holder. The mixtures were uniaxially pressed and finally, the green compacts sintered at 1150°C for 5 hours. The porous structures are characterized by X-ray diffraction method (XRD) and scanning electron microscopy (SEM). The mechanical properties were examined using micro hardness and compression tests. The investigation revealed that after 15 h of milling, the Bioglass dissolved in Ti lattice. Also, results show that nanostructured Ti-10 wt.% Bioglass with 31.5 nm crystallite size possess greater hardness compared to respective microcrystalline titanium and desirable compressive strength for using in biomedical application.

Mechanical properties of FeAlSi powders prepared by mechanical alloying from different initial feedstock materials

2019 ◽  
Vol 107 (2) ◽  
pp. 207 ◽  
Author(s):  
Jaroslav Čech ◽  
Petr Haušild ◽  
Miroslav Karlík ◽  
Veronika Kadlecová ◽  
Jiří Čapek ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Mechanical Alloying ◽  
Young’S Modulus ◽  
Milling Time ◽  
Young's Modulus ◽  
Element Model ◽  
X Ray Diffraction ◽  
X Ray ◽  
Powder Particles ◽  
Complete Homogenization

FeAl20Si20 (wt.%) powders prepared by mechanical alloying from different initial feedstock materials (Fe, Al, Si, FeAl27) were investigated in this study. Scanning electron microscopy, X-ray diffraction and nanoindentation techniques were used to analyze microstructure, phase composition and mechanical properties (hardness and Young’s modulus). Finite element model was developed to account for the decrease in measured values of mechanical properties of powder particles with increasing penetration depth caused by surrounding soft resin used for embedding powder particles. Progressive homogenization of the powders’ microstructure and an increase of hardness and Young’s modulus with milling time were observed and the time for complete homogenization was estimated.

Fabrication and Mechanical Properties of ultra fine WC-6wt.%Co by Spark Plasma Sintering Process

2011 ◽  
Vol 49 (01) ◽  
pp. 40-45 ◽  
Author(s):  
Hyun-Kuk Park ◽  
Seung-Min Lee ◽  
Hee-Jun Youn ◽  
Ki-Sang Bang ◽  
Ik-Hyun Oh
Keyword(s):  
Mechanical Properties ◽  
Spark Plasma Sintering ◽  
Sintering Process ◽  
Plasma Sintering ◽  
Spark Plasma

Effects of particle sizes, wood to cement ratio and chemical additives on the properties of sesendok (Endospermum Diadenum) cement-bonded particleboard

2010 ◽  
Vol 7 (2) ◽  
pp. 57
Author(s):  
Jamaludin Kasim ◽  
Shaikh Abdul Karim Yamani ◽  
Ahmad Firdaus Mat Hedzir ◽  
Ahmad Syafiq Badrul Hisham ◽  
Mohd Arif Fikri Mohamad Adnan
Keyword(s):  
Mechanical Properties ◽  
Experimental Investigation ◽  
Cement Content ◽  
Particle Sizes ◽  
Thickness Swelling ◽  
Chemical Additives ◽  
Board Density ◽  
Cement Ratio ◽  
Aluminium Silicate ◽  
Cement Board

An experimental investigation was performed to evaluate the properties of cement-bonded particleboard made from Sesendok wood. The target board density was set at a standard 1200 kg m". The effect offarticle size, wood to cement ratio and the addition ofsodium silicate and aluminium silicate on the wood cement board properties has been evaluated. A change ofparticle size from 1.0 mm to 2.0 mm has a significant effect on the mechanical properties, however the physical properties deteriorate. Increasing the wood to cement ratio from 1:2.25 to 1:3 decreases the modulus ofrupture (MOR) by 11% and the addition ofsodium silicate improves valuesfurther by about 28% compared to the addition ofaluminum silicate. The modulus ofelasticity (MOE) in general increases with increasing cement content, but is not significantly affected by the addition ofsodium silicate or aluminium silicate, although the addition of their mixture (sodium silicate andaluminium silicate) consistentlyyields greater MOE values. Water absorption and thickness swelling is significantly affected by the inclusion ofadditives and better values are attained using higher wood to cement ratios.

Effects of Vickers Cracks on the Mechanical Properties of Solid-phase-sintered Silicon Carbide Ceramics

2012 ◽  
Vol 27 (9) ◽  
pp. 965-969
Author(s):  
Xiao YANG ◽  
Xue-Jian LIU ◽  
Zheng-Ren HUANG ◽  
Gui-Ling LIU ◽  
Xiu-Min YAO
Keyword(s):  
Mechanical Properties ◽  
Silicon Carbide ◽  
Solid Phase ◽  
Carbide Ceramics ◽  
Silicon Carbide Ceramics ◽  
Sintered Silicon

scholarly journals Experimental Analysis of the Mechanical Properties and Resistivity of Tectonic Coal Samples with Different Particle Sizes

Energies ◽  
2021 ◽  
Vol 14 (8) ◽  
pp. 2303
Author(s):  
Congyu Zhong ◽  
Liwen Cao ◽  
Jishi Geng ◽  
Zhihao Jiang ◽  
Shuai Zhang
Keyword(s):  
Mechanical Properties ◽  
Particle Size ◽  
Compressive Strength ◽  
Elastic Modulus ◽  
Uniaxial Compressive Strength ◽  
Coalbed Methane ◽  
Coal Sample ◽  
Fine Particles ◽  
Particle Sizes ◽  
Tectonic Coal

Because of its weak cementation and abundant pores and cracks, it is difficult to obtain suitable samples of tectonic coal to test its mechanical properties. Therefore, the research and development of coalbed methane drilling and mining technology are restricted. In this study, tectonic coal samples are remodeled with different particle sizes to test the mechanical parameters and loading resistivity. The research results show that the particle size and gradation of tectonic coal significantly impact its uniaxial compressive strength and elastic modulus and affect changes in resistivity. As the converted particle size increases, the uniaxial compressive strength and elastic modulus decrease first and then tend to remain unchanged. The strength of the single-particle gradation coal sample decreases from 0.867 to 0.433 MPa and the elastic modulus decreases from 59.28 to 41.63 MPa with increasing particle size. The change in resistivity of the coal sample increases with increasing particle size, and the degree of resistivity variation decreases during the coal sample failure stage. In composite-particle gradation, the proportion of fine particles in the tectonic coal sample increases from 33% to 80%. Its strength and elastic modulus increase from 0.996 to 1.31 MPa and 83.96 to 125.4 MPa, respectively, and the resistivity change degree decreases. The proportion of medium particles or coarse particles increases, and the sample strength, elastic modulus, and resistivity changes all decrease.

scholarly journals Comprehensive Analysis of the Microstructure and Mechanical Properties of Friction-Stir-Welded Low-Carbon High-Strength Steels with Tensile Strengths Ranging from 590 MPa to 1.5 GPa

2021 ◽  
Vol 11 (12) ◽  
pp. 5728
Author(s):  
HyeonJeong You ◽  
Minjung Kang ◽  
Sung Yi ◽  
Soongkeun Hyun ◽  
Cheolhee Kim
Keyword(s):  
Mechanical Properties ◽  
Tensile Test ◽  
Joint Strength ◽  
Solid Phase ◽  
Welding Process ◽  
High Strength Steels ◽  
High Strength ◽  
Low Carbon ◽  
Friction Stir ◽  
Welding Processes

High-strength steels are being increasingly employed in the automotive industry, requiring efficient welding processes. This study analyzed the materials and mechanical properties of high-strength automotive steels with strengths ranging from 590 MPa to 1500 MPa, subjected to friction stir welding (FSW), which is a solid-phase welding process. The high-strength steels were hardened by a high fraction of martensite, and the welds were composed of a recrystallized zone (RZ), a partially recrystallized zone (PRZ), a tempered zone (TZ), and an unaffected base metal (BM). The RZ exhibited a higher hardness than the BM and was fully martensitic when the BM strength was 980 MPa or higher. When the BM strength was 780 MPa or higher, the PRZ and TZ softened owing to tempered martensitic formation and were the fracture locations in the tensile test, whereas BM fracture occurred in the tensile test of the 590 MPa steel weld. The joint strength, determined by the hardness and width of the softened zone, increased and then saturated with an increase in the BM strength. From the results, we can conclude that the thermal history and size of the PRZ and TZ should be controlled to enhance the joint strength of automotive steels.

scholarly journals Controlling the Thermal Stability of Kyanite-Based Refractory Geopolymers

Materials ◽  
2021 ◽  
Vol 14 (11) ◽  
pp. 2903
Author(s):  
Juvenal Giogetti Nemaleu Deutou ◽  
Rodrigue Cyriaque Kaze ◽  
Elie Kamseu ◽  
Vincenzo M. Sglavo
Keyword(s):  
Mechanical Properties ◽  
Thermal Stability ◽  
High Strength ◽  
Treatment Temperature ◽  
Strength Development ◽  
Particle Sizes ◽  
Cold Setting ◽  
Thermal Stability Of ◽  
Geopolymer Composites ◽  
Refractory Composites

The present project investigated the thermal stability of cold-setting refractory composites under high-temperature cycles. The proposed route dealt with the feasibility of using fillers with different particle sizes and studying their influence on the thermo-mechanical properties of refractory geopolymer composites. The volumetric shrinkage was studied with respect to particle sizes of fillers (80, 200 and 500 µm), treatment temperature (1050–1250 °C) and amount of fillers (70–85 wt.%). The results, combined with thermal analysis, indicated the efficiency of refractory-based kyanite aggregates for enhancing thermo-mechanical properties. At low temperatures, larger amounts of kyanite aggregates promoted mechanical strength development. Flexural strengths of 45, 42 and 40 MPa were obtained for geopolymer samples, respectively, at 1200 °C, made with filler particles sieved at 80, 200 and 500 µm. In addition, a sintering temperature equal to 1200 °C appeared beneficial for the promotion of densification as well as bonding between kyanite aggregates and the matrix, contributing to the reinforcement of the refractory geopolymer composites without any sign of vitrification. From the obtained properties of thermal stability, good densification and high strength, kyanite aggregates are efficient and promising candidates for the production of environmentally friendly, castable refractory composites.

Sign in / Sign up

Export Citation Format

Share Document