scholarly journals Abnormal Shear Performance of Microscale Ball Grid Array Structure Cu/Sn–3.0Ag–0.5Cu/Cu Solder Joints with Increasing Current Density

Crystals ◽  
2022 ◽  
Vol 12 (1) ◽  
pp. 85
Author(s):  
Bo Wang ◽  
Wangyun Li ◽  
Kailin Pan
Keyword(s):  
Shear Strength ◽  
Critical Current Density ◽  
Joule Heating ◽  
Current Density ◽  
Solder Joints ◽  
Solder Matrix ◽  
Ball Grid Array ◽  
Current Stressing ◽  
Shear Performance ◽  
Array Structure

The shear performance and fracture behavior of microscale ball grid array structure Cu/Sn–3.0Ag–0.5Cu/Cu solder joints with increasing electric current density (from 1.0 × 103 to 6.0 × 103 A/cm2) at various test temperatures (25 °C, 55 °C, 85 °C, 115 °C, 145 °C, and 175 °C) were investigated systematically. Shear strength increases initially, then decreases with increasing current density at a test temperature of no more than 85 °C; the enhancement effect of current stressing on shear strength decreases and finally diminishes with increasing test temperatures. These changes are mainly due to the counteraction of the athermal effect of current stressing and Joule heating. After decoupling and quantifying the contribution of the athermal effect to the shear strength of solder joints, the results show that the influence of the athermal effect presents a transition from an enhancement state to a deterioration state with increasing current density, and the critical current density for the transition decreases with increasing test temperatures. Joule heating is always in a deterioration state on the shear strength of solder joints, which gradually becomes the dominant factor with increasing test temperatures and current density. In addition, the fracture location changes from the solder matrix to the interface between the solder matrix and the intermetallic compound (IMC) layer (the solder/IMC layer interface) with increasing current density, showing a ductile-to-brittle transition. The interfacial fracture is triggered by current crowding at the groove of the IMC layer and driven by mismatch strain at the solder/IMC layer interface, and the critical current density for the occurrence of interfacial fracture decreases with increasing test temperatures.

scholarly journals Comprehensive Properties of a Novel Quaternary Sn-Bi-Sb-Ag Solder: Wettability, Interfacial Structure and Mechanical Properties

Metals ◽  
2019 ◽  
Vol 9 (7) ◽  
pp. 791 ◽  
Author(s):  
Kaipeng Wang ◽  
Fengjiang Wang ◽  
Ying Huang ◽  
Kai Qi
Keyword(s):  
Tensile Strength ◽  
Shear Strength ◽  
Low Temperature ◽  
Strain Rate ◽  
Isothermal Aging ◽  
Solder Joints ◽  
Solder Matrix ◽  
Interfacial Structure ◽  
Solder Alloys ◽  
Cu Substrate

Sn-58Bi eutectic solder is the most recommended low temperature Pb-free solder but is also limited from the interfacial embrittlement of Bi segregation. Since the quaternary Sn-38Bi-1.5Sb-0.7Ag solder provides a similar melting point as Sn-58Bi eutectic, this paper systematically investigated the properties of this solder from wettability, bulk tensile properties, interfacial microstructure in solder joints with a Cu substrate, interfacial evolution in joints during isothermal aging and the shear strength on ball solder joints with effect of aging conditions. The results were also compared with Sn-58Bi solder. The wettability of solder alloys was evaluated with wetting balance testing, and the quaternary Sn-38Bi-1.5Sb-0.7Ag solder had a better wettability than Sn-58Bi solder on the wetting time. Tensile tests on bulk solder alloys indicated that the quaternary Sn-38Bi-1.5Sb-0.7Ag solder had a higher tensile strength and similar elongation compared with Sn-58Bi solder due to the finely distributed SnSb and Ag3Sn intermetallics in the solder matrix. The tensile strength of solder decreased with a decrease in the strain rate and with an increase in temperature, while the elongation of solder was independent of the temperature and strain rate. When soldering with a Cu substrate, a thin Cu6Sn5 intermetallic compound (IMC) is produced at the interface in the solder joint. Measurement on IMC thickness showed that the quaternary Sn-38Bi-1.5Sb-0.7Ag had a lower IMC growth rate during the following isothermal aging. Ball shear test on solder joints illustrated that the quaternary Sn-38Bi-1.5Sb-0.7Ag solder joints had higher shear strength than Sn-58Bi solder joints. Compared with the serious deterioration on shear strength of Sn-58Bi joints from isothermal aging, the quaternary Sn-38Bi-1.5Sb-0.7Ag solder joints presented a superior high temperature stability. Therefore, the quaternary Sn-38Bi-1.5Sb-0.7Ag solder provides better performances and the possibility to replace Sn-58Bi solder to realize low temperature soldering.

scholarly journals Shear Strength and Aging Characteristics of Sn-3.0Ag-0.5Cu/Cu Solder Joint Reinforced with ZrO2 Nanoparticles

Metals ◽  
2020 ◽  
Vol 10 (10) ◽  
pp. 1295
Author(s):  
Sri Harini Rajendran ◽  
Seung Jun Hwang ◽  
Jae Pil Jung
Keyword(s):  
Shear Strength ◽  
Solder Joint ◽  
Solder Joints ◽  
Solder Matrix ◽  
Fracture Analysis ◽  
Zro2 Nanoparticles ◽  
Solder Paste ◽  
Lap Shear ◽  
Matrix Fracture ◽  
The Matrix

This study investigates the shear strength and aging characteristics of Sn-3.0Ag-0.5Cu (SAC 305)/Cu joints by the addition of ZrO2 nanoparticles (NPs) having two different particle size: 5–15 nm (ZrO2A) and 70–90 nm (ZrO2B). Nanocomposite pastes were fabricated by mechanically mixing ZrO2 NPs and the solder paste. ZrO2 NPs decreased the β-Sn grain size and Ag3Sn intermetallic compound (IMC) in the matrix and reduced the Cu6Sn5 IMC thickness at the interface of lap shear SAC 305/Cu joints. The effect is pronounced for ZrO2A NPs added solder joint. The solder joints were isothermally aged at 175 °C for 24, 48, 144 and 256 h. NPs decreased the diffusion coefficient from 1.74 × 10–16 m/s to 3.83 × 10–17 m/s and 4.99 × 10–17 m/s for ZrO2A and ZrO2B NPs added SAC 305/Cu joints respectively. The shear strength of the solder joints decreased with the aging time due to an increase in the thickness of interfacial IMC and coarsening of Ag3Sn in the solder. However, higher shear strength exhibited by SAC 305-ZrO2A/Cu joints was attributed to the fine Ag3Sn IMC’s dispersed in the solder matrix. Fracture analysis of SAC 305-ZrO2A/Cu joints displayed mixed solder/IMC mode upon 256 h of aging.

Effects of Current Stressing and Isothermal Aging on the Tensile Strength of Microscale Lead-Free Solder Joints with Different Joint Volumes

2013 ◽  
Vol 634-638 ◽  
pp. 2800-2803 ◽  
Author(s):  
Li Meng Yin ◽  
Yan Fei Geng ◽  
Zhang Liang Xu ◽  
Song Wei
Keyword(s):  
Tensile Strength ◽  
Current Density ◽  
Isothermal Aging ◽  
Solder Joints ◽  
High Current Density ◽  
Copper Wire ◽  
Lead Free ◽  
Lead Free Solder ◽  
Current Stressing ◽  
Free Solder

Adopting an accurate micro-tensile method based on dynamic mechanical analyzer (DMA) instrument, the tensile strength of three kinds of copper-wire/solder/copper-wire sandwich structured microscale lead-free solder joints that underwent current stressing with a direct current density of 1.0×104 A/cm2 and loading time of 48 hours were investigated, and compared with those solder joints isothermal aged at 100 0C for 48 hours and as-reflowed condition. These three kinds of microscale columnar solder joints have different volumes, i.e., a same diameter of 300 μm but different heights of 100 μm, 200 μm and 300 μm. Experimental results show that both current stressing and isothermal aging degrades the tensile strength of microscale solder joints, and the solder joint with smaller volume obtains higher tensile strength under same test condition. In addition, current stressing induces obvious electromigration (EM) issue under high current density of 1.0×104 A/cm2, resulting in the decreasing of tensile strength and different fracture position, mode and surface morphology of microscale solder joints. The degree of strength degradation increases with the increasing of joint height when keep joint diameter constant, this is mainly due to that electromigration leads to voids form and grow at the interface of cathode, and solder joints with larger volume may contains more soldering defects as well.

Electromigration Reliability With Respect to Cu Weight Contents of Sn–Ag–Cu Flip-Chip Solder Joints Under Comparatively Low Current Stressing

2008 ◽  
Vol 130 (4) ◽  
Author(s):  
Yi-Shao Lai ◽  
Ying-Ta Chiu
Keyword(s):  
Intermetallic Compound ◽  
Ambient Temperature ◽  
Current Density ◽  
Flip Chip ◽  
Solder Joints ◽  
Average Current Density ◽  
Current Stressing ◽  
Weight Content ◽  
Average Current ◽  
Better Than

This work presents electromigration reliability and patterns of Sn–3Ag–0.5Cu and Sn–3Ag–1.5Cu∕Sn–3Ag–0.5Cu composite flip-chip solder joints with Ti∕Ni(V)∕Cu under bump metallurgy (UBM), bonded on Au∕Ni∕Cu substrate pads. The solder joints were subjected to an average current density of 5kA∕cm2 under an ambient temperature of 150°C. Under the situation when electron charges flow from the UBM toward the substrate, Sn diffuses from the Cu–Ni–Sn intermetallic compound developed around the UBM toward the UBM and eventually causes the Ni(V) layer to deform. Electromigration reliability of Sn–3Ag–1.5Cu∕Sn–3Ag–0.5Cu composite flip-chip solder joints was found to be better than that of Sn–3Ag–0.5Cu solder joints. According to the morphological observations on cross-sectioned solder joints, a failure mechanism is proposed as follows. Since the deformation of the Ni(V) layer as a result of Sn diffusion toward the UBM is considered as the dominant failure, a greater Cu weight content in the solder joints would trap more Sn in the Sn–Cu interfacial reaction and would therefore retard the diffusion of Sn toward the UBM and hence enhance the electromigration reliability.

Thermomigration in Pb–Sn solder joints under joule heating during electric current stressing

2003 ◽  
Vol 82 (7) ◽  
pp. 1045-1047 ◽  
Author(s):  
Hua Ye ◽  
Cemal Basaran ◽  
Douglas Hopkins
Keyword(s):  
Electric Current ◽  
Joule Heating ◽  
Solder Joints ◽  
Current Stressing