Curves of Elasto-Plastic Deformation of Thin Coatings Obtained in Depth-Sensing Indentation Experiments

1997 ◽  
Vol 505 ◽  
Author(s):  
S. N. Dub
Keyword(s):  
Thin Films ◽  
Plastic Deformation ◽  
Room Temperature ◽  
Brittle Materials ◽  
Depth Sensing ◽  
Thin Coatings ◽  
Deformation Curves ◽  
Indentation Tests

ABSTRACTA method to obtain curves of elasto-plastic deformation of materials in depth-sensing indentation tests is proposed. Elasto-plastic deformation curves of thin films and brittle materials have been received at room temperature using this method.

Time-Dependent Deformation in Room-Temperature Indentation Experiments using a Nanoindenter

1991 ◽  
Vol 239 ◽  
Author(s):  
Shefford P. Baker ◽  
Troy W. Barbee ◽  
William D. Nix
Keyword(s):  
Thin Films ◽  
Plastic Deformation ◽  
Strain Rate ◽  
Room Temperature ◽  
Rate Dependence ◽  
Time Dependent ◽  
Depth Sensing

ABSTRACTTime-dependent deformation in room-temperature indentation is a well known phenomenon which is frequently overlooked in depth-sensing indentation experiments. In this study, the time-dependent displacements which occur during depth-sensing indentation experiments using a Nanoindenter were investigated. Time-dependent displacements were found to result both from plastic deformation of the sample and experimental drift. A simple correction for experimental drift was applied in experiments on sputtered copper thin films and reasonable strain rate sensitivities were obtained. The sources of experimental drift were identified and measured. It appears to be possible to measure the rate-dependence of plastic deformation in a variety of materials using this instrument.

scholarly journals Continuous Strain Bursts in Crystalline and Amorphous Metals During Plastic Deformation by Nanoindentation

2005 ◽  
Vol 20 (11) ◽  
pp. 3072-3081 ◽  
Author(s):  
H. Li ◽  
A.H.W. Ngan ◽  
M.G. Wang
Keyword(s):  
Plastic Deformation ◽  
Metallic Glass ◽  
Room Temperature ◽  
Burst Size ◽  
Limited Range ◽  
Amorphous Selenium ◽  
Continuous Series ◽  
Depth Sensing ◽  
Strain Burst ◽  
Self Organized

Using depth-sensing indentation with sub-nanometer displacement resolution, the plastic deformation of a range of materials, including a metallic glass, amorphous selenium, Ni3Al, pure Nb, Al, Cu, and Zn metals, and an Al-Mg alloy, has been investigated at room temperature. In amorphous selenium, even the sub-nanometer displacement resolution of the nanoindentation technique cannot reveal any strain burst during deformation at room temperature. In all other metals studied, what may appear to be smooth load-displacement curves at macroscopic scale during indentation deformation in fact turn out to consist of a continuous series of random bursts of the nanometer scale. The occurrence probability of the bursts is found to decrease at increasing burst size. In all of the crystalline metals and alloys studied, the size distribution of the strain bursts seems to follow an exponential law with a characteristic length scale. The absence of the self-organized critical behavior is likely a result of the small size of the strained volume in the nanoindentation situation, which gives rise to a constraint of a characteristic strain. In the metallic glass sample, due to the limited range of the burst sizes encountered, whether the deformation bursts follow an exponential or a power-law behavior corresponding to self-organized criticality is inconclusive. From a theoretical viewpoint based on the Shannon entropy, the exponential distribution is the most likely distribution at a given mean burst size, and this is thought to be the reason for its occurrence in different materials.

Studies on Water in the Hydration Chamber of a Modified Electron Microscope

1970 ◽  
Vol 28 ◽  
pp. 544-545
Author(s):  
R. C. Moretz ◽  
G. G. Hausner ◽  
D. F. Parsons
Keyword(s):  
Thin Film ◽  
Thin Films ◽  
Electron Microscope ◽  
Steady State ◽  
Room Temperature ◽  
Small Mass ◽  
Equilibrium Pressure ◽  
Biological Objects ◽  
Mechanical Pump ◽  
Differential Pumping

Use of the electron microscope to examine wet objects is possible due to the small mass thickness of the equilibrium pressure of water vapor at room temperature. Previous attempts to examine hydrated biological objects and water itself used a chamber consisting of two small apertures sealed by two thin films. Extensive work in our laboratory showed that such films have an 80% failure rate when wet. Using the principle of differential pumping of the microscope column, we can use open apertures in place of thin film windows.Fig. 1 shows the modified Siemens la specimen chamber with the connections to the water supply and the auxiliary pumping station. A mechanical pump is connected to the vapor supply via a 100μ aperture to maintain steady-state conditions.

Interactions Between Al and Cr Thin Films

1976 ◽  
Vol 34 ◽  
pp. 638-639
Author(s):  
R. M. Anderson ◽  
T. M. Reith ◽  
M. J. Sullivan ◽  
E. K. Brandis
Keyword(s):  
Thin Films ◽  
Room Temperature ◽  
Vacuum System ◽  
Processing Temperature ◽  
Diffusion Couples ◽  
Electronic Circuits ◽  
Intermetallic Formation ◽  
Si Substrates ◽  
Aluminum Silicon

Thin films of aluminum or aluminum-silicon can be used in conjunction with thin films of chromium in integrated electronic circuits. For some applications, these films exhibit undesirable reactions; in particular, intermetallic formation below 500 C must be inhibited or prevented. The Al films, being the principal current carriers in interconnective metal applications, are usually much thicker than the Cr; so one might expect Al-rich intermetallics to form when the processing temperature goes out of control. Unfortunately, the JCPDS and the literature do not contain enough data on the Al-rich phases CrAl7 and Cr2Al11, and the determination of these data was a secondary aim of this work.To define a matrix of Cr-Al diffusion couples, Cr-Al films were deposited with two sets of variables: Al or Al-Si, and broken vacuum or single pumpdown. All films were deposited on 2-1/4-inch thermally oxidized Si substrates. A 500-Å layer of Cr was deposited at 120 Å/min on substrates at room temperature, in a vacuum system that had been pumped to 2 x 10-6 Torr. Then, with or without vacuum break, a 1000-Å layer of Al or Al-Si was deposited at 35 Å/s, with the substrates still at room temperature.

Investigation of ultra-thin films of YBa2Cu3O7−δ grown on MgO

1990 ◽  
Vol 48 (4) ◽  
pp. 6-7
Author(s):  
S.K. Streiffer ◽  
C.B. Eom ◽  
J.C. Bravman ◽  
T.H. Geballet
Keyword(s):  
Thin Films ◽  
Room Temperature ◽  
Deposition Process ◽  
Nucleation And Growth ◽  
Multilayer Structures ◽  
Rf Power ◽  
Oxygen Loss ◽  
Transmission Electron ◽  
Single Target ◽  
Mtorr Argon

The study of very thin (<15 nm) YBa2Cu3O7−δ (YBCO) films is necessary both for investigating the nucleation and growth of films of this material and for achieving a better understanding of multilayer structures incorporating such thin YBCO regions. We have used transmission electron microscopy to examine ultra-thin films grown on MgO substrates by single-target, off-axis magnetron sputtering; details of the deposition process have been reported elsewhere. Briefly, polished MgO substrates were attached to a block placed at 90° to the sputtering target and heated to 650 °C. The sputtering was performed in 10 mtorr oxygen and 40 mtorr argon with an rf power of 125 watts. After deposition, the chamber was vented to 500 torr oxygen and allowed to cool to room temperature. Because of YBCO’s susceptibility to environmental degradation and oxygen loss, the technique of Xi, et al. was followed and a protective overlayer of amorphous YBCO was deposited on the just-grown films.

TEM sample preparation of wear-tested room-temperature pulsed-laser-deposited thin films of MoS2 by ultramicrotomy

1993 ◽  
Vol 51 ◽  
pp. 1118-1119
Author(s):  
Pamela F. Lloyd ◽  
Scott D. Walck
Keyword(s):  
Thin Films ◽  
Sample Preparation ◽  
Room Temperature ◽  
High Vacuum ◽  
Pulsed Laser ◽  
Ultra High Vacuum ◽  
Wear Testing ◽  
Preparation Technique ◽  
Cross Sectional ◽  
Aerospace Applications

Pulsed laser deposition (PLD) is a novel technique for the deposition of tribological thin films. MoS2 is the archetypical solid lubricant material for aerospace applications. It provides a low coefficient of friction from cryogenic temperatures to about 350°C and can be used in ultra high vacuum environments. The TEM is ideally suited for studying the microstructural and tribo-chemical changes that occur during wear. The normal cross sectional TEM sample preparation method does not work well because the material’s lubricity causes the sandwich to separate. Walck et al. deposited MoS2 through a mesh mask which gave suitable results for as-deposited films, but the discontinuous nature of the film is unsuitable for wear-testing. To investigate wear-tested, room temperature (RT) PLD MoS2 films, the sample preparation technique of Heuer and Howitt was adapted.Two 300 run thick films were deposited on single crystal NaCl substrates. One was wear-tested on a ball-on-disk tribometer using a 30 gm load at 150 rpm for one minute, and subsequently coated with a heavy layer of evaporated gold.

Electron microscope studies of the plastic deformation of ternary alloys based on GaAs

1990 ◽  
Vol 48 (4) ◽  
pp. 1120-1120
Author(s):  
R. Haswell ◽  
U. Bangert ◽  
P. Charsley
Keyword(s):  
Plastic Deformation ◽  
Electron Microscope ◽  
Room Temperature ◽  
Stacking Faults ◽  
The Other ◽  
Ternary Alloys ◽  
Dislocation Mobility ◽  
Semiconducting Materials ◽  
Micro Indentation

A knowledge of the behaviour of dislocations in semiconducting materials is essential to the understanding of devices which use them . This work is concerned with dislocations in alloys related to the semiconductor GaAs . Previous work on GaAs has shown that microtwinning occurs on one of the <110> rosette arms after indentation in preference to the other . We have shown that the effect of replacing some of the Ga atoms by Al results in microtwinning in both of the rosette arms.In the work to be reported dislocations in specimens of different compositions of Gax Al(1-x) As and Gax In(1-x) As have been studied by using micro indentation on a (001) face at room temperature . A range of electron microscope techniques have been used to investigate the type of dislocations and stacking faults/microtwins in the rosette arms , which are parallel to the [110] and [10] , as a function of composition for both alloys . Under certain conditions microtwinning occurs in both directions . This will be discussed in terms of the dislocation mobility.

Interface motion during recrystallization of amorphous NiSi2

1990 ◽  
Vol 48 (4) ◽  
pp. 524-525
Author(s):  
J. L. Batstone ◽  
D.A. Smith
Keyword(s):  
Thin Films ◽  
Room Temperature ◽  
Amorphous Film ◽  
Nucleation And Growth ◽  
Recrystallization Process ◽  
Amorphous Films ◽  
Interface Motion ◽  
Si Substrates ◽  
Spherical Caps ◽  
Crystal Interfaces

Recrystallization of amorphous NiSi2 involves nucleation and growth processes which can be studied dynamically in the electron microscope. Previous studies have shown thatCoSi2 recrystallises by nucleating spherical caps which then grow with a constant radial velocity. Coalescence results in the formation of hyperbolic grain boundaries. Nucleation of the isostructural NiSi2 results in small, approximately round grains with very rough amorphous/crystal interfaces. In this paper we show that the morphology of the rccrystallizcd film is dramatically affected by variations in the stoichiometry of the amorphous film.Thin films of NiSi2 were prepared by c-bcam deposition of Ni and Si onto Si3N4, windows supported by Si substrates at room temperature. The base pressure prior to deposition was 6 × 107 torr. In order to investigate the effect of stoichiomctry on the recrystallization process, the Ni/Si ratio was varied in the range NiSi1.8-2.4. The composition of the amorphous films was determined by Rutherford Backscattering.

STEM and ELS Observation of Early Oxide Formation on the Surface of Cr Thin Films

1980 ◽  
Vol 38 ◽  
pp. 412-413
Author(s):  
Fumio Watari ◽  
J. M. Cowley
Keyword(s):  
Thin Films ◽  
Optical System ◽  
Room Temperature ◽  
Oxide Formation ◽  
Initial Nucleation ◽  
Diffraction Patterns ◽  
Relationship Of ◽  
Multiple Twinning ◽  
Moderately High Temperature

STEM coupled with the optical system was used for the investigation of the early oxidation on the surface of Cr. Cr thin films (30 – 1000Å) were prepared by evaporation onto the polished or air-cleaved NaCl substrates at room temperature and 45°C in a vacuum of 10−6 Torr with an evaporation speed 0.3Å/sec. Rather thick specimens (200 – 1000Å) with various preferred orientations were used for the investigation of the oxidation at moderately high temperature (600 − 1100°C). Selected area diffraction patterns in these specimens are usually very much complicated by the existence of the different kinds of oxides and their multiple twinning. The determination of the epitaxial orientation relationship of the oxides formed on the Cr surface was made possible by intensive use of the optical system and microdiffraction techniques. Prior to the formation of the known rhombohedral Cr2O3, a thin spinel oxide, probably analogous to γ -Al203 or γ -Fe203, was formed. Fig. 1a shows the distinct epitaxial growth of the spinel (001) as well as the rhombohedral (125) on the well-oriented Cr(001) surface. In the case of the Cr specimen with the (001) preferred orientation (Fig. 1b), the rings explainable by spinel structure appeared as well as the well defined epitaxial spots of the spinel (001). The microdif fraction from 20A areas (Fig. 2a) clearly shows the same pattern as Fig. Ia with the weaker oxide spots among the more intense Cr spots, indicating that the thickness of the oxide is much less than that of Cr. The rhombohedral Cr2O3 was nucleated preferably at the Cr(011) sites provided by the polycrystalline nature of the present specimens with the relation Cr2O3 (001)//Cr(011), and by further oxidation it grew into full coverage of the rest of the Cr surface with the orientation determined by the initial nucleation.

Sign in / Sign up

Export Citation Format

Share Document