The influence of oxidized technical carbon N121 on the properties of butyl-based rubbers

2019 ◽  
pp. 123-128
Author(s):  
M. N. Nagornaya ◽  
A. V. Myshliavtsev ◽  
S. Ya. Khodakova
Keyword(s):  
Hydrogen Peroxide ◽  
Carbon Black ◽  
Gas Permeability ◽  
Mechanical Tests ◽  
Butyl Rubber ◽  
Rubber Mixture ◽  
Active Forms Of Oxygen ◽  
Technical Carbon ◽  
Furnace Black ◽  
The Subject

The subject of the study were samples of channel technical carbon K354, furnace technical carbon N121 and experimental – based on TUN121, oxidized with active forms of oxygen. Samples of carbon black were studied in the composition of a rubber mixture based on BK 1675N butyl rubber. The purpose of this study was to determine the possibility of using oxidized technical carbon N121 in fillers of rubber based on butyl rubber, instead of carbon black K354. The physicochemical properties of the samples of technical carbon under study, the results of physical and mechanical tests, and the gas permeability tests of rubber mixtures filled with the samples under study are presented. A conclusion is made about the possibility of replacing channel technical carbon K354 with furnace black carbon N121 oxidized with 30% hydrogen peroxide.

A Fourier Transform Infrared Method of Studying Elastomers Filled with Carbon Black

1977 ◽  
Vol 31 (3) ◽  
pp. 220-224 ◽  
Author(s):  
W. W. Hart ◽  
P. C. Painter ◽  
J. L. Koenig ◽  
M. M. Coleman
Keyword(s):  
Fourier Transform ◽  
Carbon Black ◽  
Fourier Transform Infrared ◽  
General Purpose ◽  
Attenuated Total Reflection ◽  
Furnace Black ◽  
Infrared Spectrometer ◽  
Infrared Method ◽  
Principal Method ◽  
Transmission And Reflection

Infrared spectra have been obtained of carbon black filled polybutadiene using a Fourier transform infrared spectrometer. Transmission and reflection techniques were employed. Polybutadiene was compounded with three fillers: Silene, general purpose furnace black, and Austin black. Subtle changes were observed in the vibrations of polybutadiene upon the addition of fillers. Transmission sampling through dilution with KBr gave better spectra than attenuated total reflection techniques in ease of data acquisition, and was therefore chosen as the principal method for further studies.

Improving the Effectiveness of Using Porous Furnace Black by Bulk Electric Heating

2008 ◽  
Vol 35 (1) ◽  
pp. 39-40
Author(s):  
S. Ya. Khodakova ◽  
V. N. Anikeev ◽  
Yu. N. Nikitin
Keyword(s):  
Electric Heating ◽  
Furnace Black

Immobilization of Elastomers at the Carbon Black Particle Surface

1970 ◽  
Vol 43 (5) ◽  
pp. 973-980 ◽  
Author(s):  
A. K. Sircar ◽  
A. Voet
Keyword(s):  
Carbon Black ◽  
Particle Surface ◽  
Carbon Black Particle ◽  
High Energy ◽  
Molecular Weights ◽  
Boiling Points ◽  
Furnace Black ◽  
Bound Rubber ◽  
Black Surface ◽  
Black Particle

Abstract Determinations have been made of the amount of elastomer unextractable from unvulcanized masticated mixes with carbon black by a given solvent at boil, expressed as immobilized elastomer. Saturated and unsaturated elastomers varying in molecular weights from 2000 to 325,000, were used, while solvents of greatly differing boiling points and solvent power were employed. It could be shown that the bonding between elastomers and carbon black is not a simple adsorption, but involves a higher energy interaction, defined as chemisorption. At successively higher temperatures elastomer is increasingly removed from the carbon black surface. The temperature Tm, obtained by extrapolation of the linear relationship between amounts immobilized and temperature of extraction, represents the temperature theoretically required to eliminate all bonds between carbon black and elastomer and is therefore indicative of the bond strength. Data suggest the existence of a bonding energy spectrum. Upon graphitization, blacks show a considerable decline in high energy bonding ability for elastomers. Saturated elastomers show less bonding than unsaturated elastomers with the same furnace black. “Bound rubber” represents the sum total of physically adsorbed, mechanically entangled, and chemisorbed elastomer. The actual values are greatly dependent upon the procedure used. “Immobilized rubber”, indicating chemisorbed elastomer, is easily determined, is not influenced by the method, and is more significant as an indicator of reinforcement.

PHYSICAL ADSORPTION STUDIES IN CARBON BLACK TECHNOLOGY

1955 ◽  
Vol 33 (2) ◽  
pp. 314-319 ◽  
Author(s):  
M. H. Polley ◽  
W. D. Schaeffer ◽  
W. R. Smith
Keyword(s):  
Carbon Black ◽  
Adsorption Isotherms ◽  
Unit Area ◽  
Physical Adsorption ◽  
Butyl Rubber ◽  
Chemisorbed Oxygen ◽  
Heat Treated ◽  
Furnace Black ◽  
Cyclic Heat ◽  
Black Surface

The adsorption isotherms of n-butane and butene-1 on typical furnace and channel carbon blacks were determined over a range of temperatures, 55°–250 °C. The adsorption of n-butane on carbon black surfaces is attributed to physical adsorption; however, the extent of surface covered per unit area of carbon black is considerably greater at a given temperature than for a silica. Butene-1 is also physically adsorbed on the furnace blacks. The presence of approximately 3% chemisorbed oxygen on the surface of the channel blacks induces an isomerization of butene-1 to cis-butene-2. When oxygen is first chemisorbed on a furnace black surface, then that surface also interacts with butene-1. Those blacks which participate in the isomerization of butene-1 respond or "interact" in a cyclic heat treated Butyl rubber – carbon black masterbatch.

Structural Characterization of Filled Vulcanizates Part 1. Determination of the Concentration of Chemical Crosslinks in Natural Rubber Vulcanizates Containing High Abrasion Furnace Black

1967 ◽  
Vol 40 (3) ◽  
pp. 866-882 ◽  
Author(s):  
M. Porter
Keyword(s):  
Carbon Black ◽  
Natural Rubber ◽  
Volume Fraction ◽  
Exponential Relationship ◽  
Furnace Black ◽  
Simple Linear Relationship ◽  
Chemical Crosslinks ◽  
Natural Rubber Vulcanizates

Abstract The degree to which HAF black restricts the swelling of natural rubber vulcanizates in n-decane has been determined using a vulcanizing system in which the stoichiometry of crosslinking is unaffected by the carbon black. The dependence of the degree of restriction, as measured by the ratio of the volume fractions of rubber in the filled and unfilled vulcanizates swollen to equilibrium, on the concentration of carbon black follows an exponential relationship previously proposed by Lorenz and Parks. This is found to be equivalent to a simple linear relationship between the apparent and actual crosslink concentrations: napparent/nactual=1+Kϕ, where K is a constant characteristic of the filler and φ is its volume fraction in the vulcanizate. The relation has been used to determine actual crosslink concentrations in filled natural rubber vulcanizates. HAF black is found to cause increases of up to 25 per cent in the yield of polymer to polymer crosslinks in conventional sulfur vulcanizing systems, accompanied by changes in rate of cure and of crosslink reversion. All these are small compared with the effect of the filler on many physical properties.

The Chemistry of Carbon Black in Rubber Reinforcement

1961 ◽  
Vol 34 (3) ◽  
pp. 709-728 ◽  
Author(s):  
C. W. Sweitzer ◽  
K. A. Burgess ◽  
F. Lyon
Keyword(s):  
Heat Treatment ◽  
Carbon Black ◽  
Lower Energy ◽  
Chemical Effect ◽  
Carbon Surface ◽  
Minor Role ◽  
Cure Rate ◽  
Chemisorbed Oxygen ◽  
Furnace Black ◽  
Different Types

Abstract 1. The removal of chemisorbed oxygen from channel black and furnace black, without alteration of the underlying carbon surface, results in only minor effects in reinforcement potential regardless of the curative system employed, whether polar or free radical. 2. When the underlying carbon surface is changed by heat treatment to a state of lower energy, a significant decrease in the reinforcing ability of the carbon black results. 3. Different types of oxygen functional groups added to the carbon surface produce similar effects upon rubber properties. 4. These effects are limited to retardation of cure rate in sulfur curing systems. Only small effects of any kind are produced in the natural rubber-peroxide system. 5. The net conclusion to be drawn is that combined oxygen on the carbon surface plays a relatively minor role in the chemical effect of carbon black upon reinforcement; the nature of the carbon surface itself is of primary importance.