Effect of epoxidized natural rubber on the processing behavior, tensile properties, morphology, and thermal properties of linear-low-density polyethylene/soya powder blends

2010 ◽  
Vol 16 (4) ◽  
pp. 238-245 ◽  
Author(s):  
S.T. Sam ◽  
H. Ismail ◽  
Z. Ahmad
Keyword(s):  
Thermal Properties ◽  
Natural Rubber ◽  
Tensile Properties ◽  
Epoxidized Natural Rubber ◽  
Low Density Polyethylene ◽  
Low Density ◽  
Linear Low Density Polyethylene ◽  
Powder Blends

Degradation of epoxidized natural rubber compatibilized linear low density polyethylene/ soya powder blends: the effect of natural weathering

2013 ◽  
Vol 33 (7) ◽  
pp. 579-588 ◽  
Author(s):  
S.T. Sam ◽  
H. Ismail ◽  
H.P.S. Abdul Khalil
Keyword(s):  
Natural Rubber ◽  
Exposure Period ◽  
Natural Weathering ◽  
Epoxidized Natural Rubber ◽  
Low Density Polyethylene ◽  
Low Density ◽  
Linear Low Density Polyethylene ◽  
Scanning Calorimetry ◽  
Powder Blends ◽  
Compatibilized Blends

Abstract In the present study, linear low density polyethylene (LLDPE)/soya powder blends were compatibilized with epoxidized natural rubber (ENR 50) and exposed to natural weathering. The exposure period for the blends was 1 year. It was found that the degradability of the compatibilized blends was higher than that of uncompatibilized blends. Fourier transform infrared (FTIR) spectra, the tensile test, scanning electron microscopy (SEM), and differential scanning calorimetry (DSC) were applied to analyze the degradability of the blends. IR spectra showed that the carbonyl index (CI) of the blends increased as a function of exposure period and soya powder content. The compatibilized blends gave higher carbonyl indices. The retention tensile strength and elongation at break (Eb) of the compatibilized blends after weathering was generally lower than for the uncompatibilized blends. The increase of crystallinity also indicated a reduction of the amorphous portion after degradation. The higher crystallinity in compatibilized blends further confirms the higher degradability of ENR 50 compatibilized blends. The weight loss and molecular weight change indicated that the incorporation of ENR 50 into LLDPE/soya powder blends can enhance the degradability of the blends upon outdoor exposure.

Thermal Properties of Linear-Low Density Polyethylene (LLDPE)/Soya Spent Powder Blends with the Addition of Epoxidised Natural Rubber

2013 ◽  
Vol 795 ◽  
pp. 433-437 ◽  
Author(s):  
S.T. Sam ◽  
N.Z. Noriman ◽  
S. Ragunathan ◽  
O.H. Lin ◽  
H. Ismail
Keyword(s):  
Thermal Properties ◽  
Natural Rubber ◽  
Mixing Time ◽  
Low Density Polyethylene ◽  
Low Density ◽  
Linear Low Density Polyethylene ◽  
Scanning Calorimetry ◽  
Powder Composites ◽  
Powder Content ◽  
Internal Mixer

Soya spent powder as an inexpensive and renewable source has been used as a filler for linear-low density polyethylene (LLDPE) in this study. Linear-low density polyethylene (LLDPE)/soya spent powder composites were prepared by using Haake internal mixer. The mixing time was 10 minutes at 150°C with rotor speed 50 rpm. Epoxidised natural rubber (ENR 50) has been used as a compatibilizer in the present study. The thermal properties of the LLDPE/soya spent powder composites with and without ENR were studied with a differential scanning calorimetry (DSC). The crystallinity of the LLDPE/soya spent powder composites decreased with increasing soya spent powder content. However, the addition of ENR 50 as a compatibilizer increased the crystallinity of the LLDPE/soya spent powder composites.

Tensile Properties LLDPE/Soya Spent Powder Blends: Oven Aging

2013 ◽  
Vol 795 ◽  
pp. 429-432
Author(s):  
S.T. Sam ◽  
N.Z. Noriman ◽  
S. Ragunathan ◽  
H. Ismail
Keyword(s):  
Tensile Strength ◽  
Tensile Properties ◽  
Aging Time ◽  
Thermal Aging ◽  
Low Density Polyethylene ◽  
Low Density ◽  
Linear Low Density Polyethylene ◽  
Elongation At Break ◽  
Powder Blends ◽  
Internal Mixer

Linear low-density polyethylene (LLDPE)/soya spent powder blends with different blends ratio were prepared by using internal mixer. Soya spent powder was varied from 5 to 40 wt. The thermal degradability was assessed by subjecting the dumbbell sample to oven aging. Thermal aging was carried out for 5 weeks. The degradability was measured by the periodic change in tensile properties of the blend samples. The tensile strength and elongation at break of the blends reduced as increasing the aging time. The effect of degradation was obvious in higher soya spent powder blends.

Effect of Epoxide Group in Thermoplastic Elastomer on the Properties of Polyamide6 and Low-Density Polyethylene Blends

2014 ◽  
Vol 979 ◽  
pp. 143-146 ◽  
Author(s):  
Surakit Tuampoemsab ◽  
Saad Riyajan ◽  
Thritima Sritapunya ◽  
Pornsri Pakeyangkoon
Keyword(s):  
Impact Strength ◽  
Natural Rubber ◽  
Shear Viscosity ◽  
Thermoplastic Elastomer ◽  
Phase Morphology ◽  
Epoxidized Natural Rubber ◽  
Low Density Polyethylene ◽  
Dispersed Phase ◽  
Low Density ◽  
Epoxide Group

Studies on the effect of percentages of epoxide group in thermoplastic elastomer as a compatibilizer on properties of polyamide6 (PA6) and low-density polyethylene (LDPE) blends was successfully carried out in this study. Thermoplastic epoxidized natural rubber (TPENR), made from epoxidized natural rubber (ENR) and LDPE, prepared from 3 types of ENR, i.e., ENR-20, ENR-50 and ENR-70, with the ratio of 90/10 of LDPE/ENR by weight. TPENR was applied as a compatibilizer into the blend of PA6/LDPE/TPENR at the ratio by weight of 80/20/1 by using a twin screw extruder at 235°C. All test specimens were characterized for phase morphology, impact strength and rheological behaviour. Results exhibited that phase morphology of PA6/LDPE blend was incompatible. The addition of TPENR improved the compatibility of PA6/LDPE blends. With inclusion of TPENR-20 as a compatibilizer, the uniformity and the maximum reduction of dispersed phase sized were observed. Moreover, it was revealed that the rheological properties such as shear viscosity increased when compared with PA6/LDPE incompatible blend. In addition, it was found that the highest shear viscosity and also the highest impact strength were obtained for the blend of PA6/LDPE compatibilized by TPENR-20. This result was further supported by SEM images, which showed that the smallest dispersed phase size occurred when a TPENR-20 was used as a compatibilizer. So, it was clearly demonstrated in this study that the suitable type of TPENR, i.e., TPENR-20, has an effect on improving phase morphology and properties of PA6/LDPE blends.