A two-level macroscale continuum description with embedded discontinuities for nonlinear analysis of brick/block masonry

A great proportion of the existing architectural heritage, including historical and monumental constructions, is made of brick/block masonry. This material shows a strong anisotropic behaviour resulting from the specific arrangement of units and mortar joints, which renders the accurate simulation of the masonry response a complex task. In general, mesoscale modelling approaches provide realistic predictions due to the explicit representation of the masonry bond characteristics. However, these detailed models are very computationally demanding and mostly unsuitable for practical assessment of large structures. Macroscale models are more efficient, but they require complex calibration procedures to evaluate model material parameters. This paper presents an advanced continuum macroscale model based on a two-scale nonlinear description for masonry material which requires only simple calibration at structural scale. A continuum strain field is considered at the macroscale level, while a 3D distribution of embedded internal layers allows for the anisotropic mesoscale features at the local level. A damage-plasticity constitutive model is employed to mechanically characterise each internal layer using different material properties along the two main directions on the plane of the masonry panel and along its thickness. The accuracy of the proposed macroscale model is assessed considering the response of structural walls previously tested under in-plane and out-of-plane loading and modelled using the more refined mesoscale strategy. The results achieved confirm the significant potential and the ability of the proposed macroscale description for brick/block masonry to provide accurate and efficient response predictions under different monotonic and cyclic loading conditions.

Residual TRM-to-Concrete Bond after Freeze–Thaw Cycles

In the present work, the effect of various freeze–thaw cycles (namely, 0, 10, 30, 50, 60, and 70) on the residual bond characteristics of textile reinforced mortar (TRM)-to-concrete was experimentally examined. The TRM consisted of a carbon dry fiber textile embedded in a cement-based matrix. Two mortar types were used as the matrix: a normal-weight and a lightweight one sharing the same hydraulic powders but different aggregates (limestone and pumice sand, respectively). The single-lap/single-prism set up was applied after the specimens underwent hygro-thermal treatment (according to ASTM C 666-Procedure B). Failure was due to the sleeve fibers rupturing the load aligned yarns or textile slippage from the mortar for an exposure period ranging between 0 and 60 cycles and to TRM debonding from the substrate for 70 cycles. Increasing cycles resulted in the intensification of partial interlaminar debonding phenomena and the weakening of the textile-to-matrix bond, with lightweight mortar being more prone to these effects. In the absence of a commonly accepted standardized method for the assessment of the freeze–thaw resistance of cement-based composites, the criterion for the termination of the freeze–thaw sequence was the number of cycles inferring a shift in failure mode (from fiber rupture/fiber slippage to TRM debonding from the substrate).