Magnetron Sputtering of Nanolaminated Cr2AlB2

A ternary Cr2AlB2 phase was deposited as a film using magnetron sputtering. Its anisotropic structure displays both structural and chemical similarities with the nanolaminated MAX phases (Mn+1AXn (n = 1–3) where M usually is an early transition metal, A is typically an element in group 13–14 and X is C or N), and can be described as CrB slabs separated by layers of Al. Combinatorial sputtering was used to optimise the sputtering process parameters for films with the Cr2AlB2 composition. The influences of substrate, temperature and composition were studied using X-ray diffraction, X-ray photoelectron spectroscopy and electron microscopy. Films deposited at room temperature were X-ray amorphous but crystalline films could be deposited on MgO substrates at 680 °C using a composite Al-B, Cr and Al targets. X-ray diffraction analyses showed that the phase composition and texture of the films was strongly dependent on the chemical composition. Films with several phases or with a single Cr2AlB2 phase could be deposited, but an additional Al target was required to compensate for a loss of Al at the high deposition temperatures used in this study. The microstructure evolution during film growth was strongly dependent on composition, with a change in texture in Al-rich films from a preferred [010] orientation to a [100]/[001] orientation. A model based on Al desorption from the surface of the growing grains is proposed to explain the texture variations.

On the Effects of Diluted and Mixed Ionic Liquids as Liquid Substrates for the Sputter Synthesis of Nanoparticles

The synthesis of nanoparticles by combinatorial sputtering in ionic liquids is a versatile approach for discovering new materials. Whereas the influence on nanoparticle formation of different pure ionic liquids has been addressed, the influence of (I) dilution of ionic liquid with solvents and (II) different mixtures of ionic liquids is less known. Therefore, mixtures of the ionic liquid [Bmim][(Tf)2N] with the organic solvent anisole and other ionic liquids ([Bmim][(Pf)2N], [BmPyr][(Tf)2N]) were used as liquid substrates for the sputter synthesis of nanoparticles, in order to investigate the influence of these mixtures on the size of the nanoparticles. First, mixtures of anisole with a suspension of sputtered Ag nanoparticles in [Bmim][(Tf)2N] were prepared in different volumetric steps to investigate if the stabilization of the NPs by the ionic liquid could be reduced by the solvent. However, a continuous reduction in nanoparticle size and amount with increasing anisole volume was observed. Second, Ag, Au and Cu were sputtered on ionic liquid mixtures. Ag nanoparticles in [Bmim][(Tf)2N]/[Bmim][(Pf)2N] mixtures showed a decrease in size with the increasing volumetric fraction of [Bmim][(Tf)2N], whereas all nanoparticles obtained from [Bmim][(Tf)2N]/[BmPyr][(Tf)2N] mixtures showed increasing size and broadening of the size distribution. Maximum sizes of sputtered Ag and Au NPs were reached in mixtures of [Bmim][(Tf)2N] with 20 vol.% and 40 vol.% [BmPyr][(Tf)2N]. The results indicate that ionic liquid mixtures with different portions of cations and anions have the capability of influencing the ionic liquid stabilization characteristics with respect to, e.g., nanoparticle size and size distribution.

Accelerated discovery and mechanical property characterization of bioresorbable amorphous alloys in the Mg–Zn–Ca and the Fe–Mg–Zn systems using high-throughput methods

High throughput discovery of amorphous bioresorbable alloys. Top: combinatorial sputtering setup. Bottom: composition of libraries deposited on silicon (Si) wafers for (a) magnesium (Mg)–zinc (Zn)–calcium (Ca) and the (b) iron (Fe)–Mg–Zn systems.

Exploring a wider range of Mg–Ca–Zn metallic glass as biocompatible alloys using combinatorial sputtering

Using combinatorial thin film processing and characterization techniques, we demonstrate a new capability of exploring a wider composition range of Mg–Ca–Zn metallic glass for biocompatible applications.