Effect of Plasmonic Nanostructures on the Optical Properties of CH3NH3PbI Perovskite Films

This paper investigated the optical properties of both silver island films (SIF) and CH3NH3PbI3 perovskite films obtained on the surface of SIF. It was found that the surface morphology of SIF has a substantial effect on the optical density of perovskite films. Furthermore, a significant redshift in the absorption spectrum of the island films was observed when perovskite is deposited on them. The intensity and lifetime of the luminescence of perovskite films on the surface of the island films depend on the wavelength of the exciting light. The results indicate that SIFs not only can be potentially used to increase the intensity of light emitting diodes based on perovskites, but also prolong the lifetime of charge carriers in perovskites, and thus lead to potentially improve the photovoltaic properties of perovskite solar cells.

TO THE PROBLEM OF STABILITY OF NANOSCALE ISLAND FILMS AND EXTENDED FILMS WITH NANOSIZED THICKNESS

Геометрическая нестабильность наноразмерных островковых пленок интерпретируется как проявление явления смачивания в твердом состоянии, а нестабильность сплошных пленок, наноразмерных по толщине, - как следствие десмачивания в твердом состоянии. С использованием молекулярно-динамического эксперимента исследованы закономерности и механизмы растекания твердых наночастиц Pb по различным граням Си при температуре, на 10 К ниже температуры плавления наночастиц выбранного размера (10 нм). Полученные в молекулярнодинамических экспериментах результаты сравниваются с экспериментальными данными, относящимися к микрочастицам Pb размером 5 -10 мкм. Установлено, что в одной и той же системе «островок-подложка» могут одновременно наблюдаться оба явления: смачивания в твердом состоянии и десмачивания в твердом состоянии. The geometric instability of nanoscale island films is interpreted as a manifestation of the solid state wetting phenomenon, and instability of continuous extended films with nanosized thickness as a consequence of the solid state dewetting. Using molecular dynamics experiment, regularities and mechanisms are investigated of spreading of Pb solid nanoparticles on different Cu faces at a temperature 10 K below the melting temperature of nanoparticles of the chosen size (10 nm). The results obtained in molecular dynamics experiments are compared with experimental data for Pb microparticles of 5 -10 pm in size. It has been also established that in the same «island -substrate» system both solid state wetting and solid state dewetting phenomena can simultaneously take place.