Study on the surface quality of 60vol% SiCp/Al2024 composites with large-grained

In this paper, the finite element cutting simulation model with irregular distribution of multiple particles is established, the stress and strain distribution of SiC particles in the process of machining, as well as the material removal mechanism are analyzed. The effects of cutting velocity and feed per tooth on the surface quality of the material are also analyzed. The effect of feed per tooth on subsurface damage is revealed. The results show that in the micro-milling of SiCp/Al2024 composites, the particle removal form is mainly crushing and extraction. The surface defects of the workpiece mainly include pits, scratches, cracks, and extrusion damage. When the cutting velocity increases, the surface defects gradually change to crack, which can improve the surface quality of the workpiece. Increasing the feed per tooth will increase the surface defects of the workpiece and lead to poor surface quality. When the feed per tooth increased from 0.428 µm to 0.714 µm, the subsurface damage thickness increased from 35.2 µm to 47.3 µm.

Investigation on the Effect of Dynamic Fracture Toughness to Zirconia Ceramic Grinding Performance with Different Grain Sizes

To reveal the material removal mechanism of zirconia ceramics, an improved prediction models of the critical grinding force and maximum subsurface damage depth models are developed based on the dynamic fracture toughness. The effects of three different grain sizes on the material removal mechanism during brittle- ductile transition process of zirconia ceramics is analyzed through grinding experiments. And the influence of grain size on grinding force, workpiece surface roughness, surface fragmentation rate and subsurface damage depth in grinding are discussed. The results of the experiment results indicated that the value of dynamic fracture toughness tends to decrease with an increase in equivalent grinding thickness, and the ductile removal range of zirconia ceramics expands for the reason that the critical grinding force considering dynamic fracture toughness is higher than the static grinding force considering static fracture toughness, and the maximum subsurface damage depth is closer to actual maximum subsurface damage depth. Besides the smaller the grain size of zirconia ceramics, the higher the surface quality of grinding.

Lubricating effect of graphene during ultra-precision mechanical polishing by atomic scale simulation

As a new two-dimensional material with unique friction and wear properties, graphene often serves as a solid lubricant. In order to better understand the lubrication effect of graphene in the process of three-body polishing of single crystal silicon with diamond abrasive, a molecular dynamics model of this process was established in this study. Further, the changes of coordination number, friction coefficient, temperature, potential energy, stress, and surface/subsurface damage in the process of three-body polishing were analyzed in detail. The results showed that graphene lubrication could enhance the heat dissipation and reduce the number of defect atoms, friction coefficient, potential energy, stress, and chips. Therefore, less subsurface damage and material resistance were observed in the workpiece with graphene lubrication during machining. In general, graphene can be used as a high-quality solid lubricant in the three-body polishing of single crystal silicon using diamond abrasive because of its excellent lubricating effect.