Alkaline Stable Anion Exchange Membranes Based on Cross-Linked Poly(Arylene Ether Sulfone) Bearing Dual Quaternary Piperidines for Enhanced Anion Conductivity at Low Water Uptake

Alkaline stable anion exchange membranes based on the cross-linked poly(arylene ether sulfone) grafted with dual quaternary piperidine (XPAES-DP) units were synthesized. The chemical structure of the synthesized PAES-DP was validated using 1H-NMR and FT-IR spectroscopy. The physicochemical, thermal, and mechanical properties of XPAES-DP membranes were compared with those of two linear PAES based membranes grafted with single piperidine (PAES-P) unit and conventional trimethyl amine (PAES-TM). XPAES-DP membrane showed the ionic conductivity of 0.021 S cm−1 at 40 °C which was much higher than that of PAES-P and PAES-TM because of the possession of more quaternary ammonium groups in the cross-linked structure. This cross-linked structure of the XPAES-DP membrane resulted in a higher tensile strength of 18.11 MPa than that of PAES-P, 17.09 MPa. In addition, as the XPAES-DP membrane shows consistency in the ionic conductivity even after 96 h in 3 M KOH solution with a minor change, its chemical stability was assured for the application of anion exchange membrane fuel cell. The single-cell assembled with XPAES-DP membrane displayed a power density of 109 mWcm−2 at 80 °C under 100% relative humidity.

Performance and Durability of Anion Exchange Membrane Water Electrolyzers using Down-selected Polymer Electrolytes

Over the last decade, several stable anion exchange polymer electrolytes have been developed for electrochemical devices. Herein, we investigate how the chemical structure and physical properties of polymer electrolytes affect...