Hierarchical Nanocauliflower Chemical Assembly Composed of Copper Oxide and Single-Walled Carbon Nanotubes for Enhanced Photocatalytic Dye Degradation

We present the fabrication and proficient photocatalytic performance of a series of heterojunction nanocomposites with cauliflower-like architecture synthesized from copper(II) oxide (CuO) nanocrystals and carbon nanotubes with single walls (SWCNTs). These unique photocatalysts were constructed via simplistic recrystallization succeeded by calcination and were labeled as CuOSC-1, CuOSC-2, and CuOSC-3 (representing the components; CuO and SC for SWCNTs, and the calcination time in hours). The photocatalytic potency of the fabricated nanocomposites was investigated on the basis of their capability to decompose methylene blue (MB) dye under visible-light irradiation. Every as-synthesized nanocomposite was effective photocatalyst for the photodecomposition of an MB solution. Moreover, CuOSC-3 exhibited the best photocatalytic activity, with 96% degradation of the visible-light irradiated MB solution in 2 h. Pure CuO nanocrystals generated through the same route and pure SWCNTs were used as controls, where the photocatalytic actions of the nanocomposite samples were found to be remarkably better than that of either the pure CuO or the pure SWCNTs. The recycling proficiency of the photocatalysts was also explored; the results disclosed that the samples could be applied for five cycles without exhibiting a notable change in photocatalytic performance or morphology.

Enhanced Visible-Light Photocatalysis of Nanocomposites of Copper Oxide and Single-Walled Carbon Nanotubes for the Degradation of Methylene Blue

We report enhanced catalytic action of a series of copper(II)-oxide-single-walled carbon nanotube (CuO-SWCNT) composite photocatalysts (abbreviated as CuO-SWCNT-0.5, CuO-SWCNT-2, and CuO-SWCNT-5, where 0.5, 2, and 5 represent the calcination time in hours) synthesized via recrystallization followed by calcination. The photocatalytic performance of the fabricated nanocomposites was examined by evaluating the degradation of methylene blue (MB) under irradiation with visible light. All of the as-fabricated nanocomposites were effective photocatalysts for the photodegradation of a MB solution; however, the CuO-SWCNT-5 displayed the best photocatalytic ability among the investigated catalysts, achieving 97.33% degradation of MB in 2 h under visible-light irradiation. The photocatalytic action of the nanocomposites was remarkably higher than that of pristine CuO nanocrystals fabricated using the same route. The recyclability of the photocatalyst was also investigated; the CuO-SWCNT-5 catalyst could be reused for three cycles without substantial degradation of its catalytic performance or morphology.

Preparation and Characterization of CuO/ZnO/PVDF/PAN Nanofiber Composites by Bubble-electrospinning

Background: Nanocomposites loaded with metal oxides, such as CuO and ZnO, have excellent optical, electrical, mechanical and chemical properties, which result in their great potential applications in optoelectronic devices, sensors, photocatalysts and other fields. Especially, electrospun metal- oxide-loaded nanofibers have attracted much attention in many fields. However, the single-needle Electrospinning (ES) inhibits the industrial application of these electrospun nanofiber composites. Bubble-Electrospinning (BE) is an effective free surface ES for mass production of nanofiber membranes loaded with metal oxide. Few relevant patents to the topic have been reviewed and introduced. Methods: The BE was used to prepare mass production of Cu(Ac)2 /Zn(Ac)2/ PVDF/ PAN Composite Nanofiber Membranes (CNFMs). Then PVDF/PAN CNFMs containing CuO and ZnO nanocrystals were obtained by heat-treatment. Finally, CuO nanosheets and ZnO nanorods were successfully grown on the surface of PVDF/PAN CNFMs using hydrothermal method. In addition, the morphology and crystal structure of CNFMs were investigated by scanning electron microscopy (SEM) and X-Ray Powder Diffractometer (XRD). Results: The morphology and crystal structure of the samples were characterized by SEM and XRD. The results showed the heat treatment temperature of 150oC and the hydrothermal temperature of 150oC were the optimal process parameters for the fabrication of PVDF/PAN CNFMs loaded with CuO and ZnO nanocrystals, and a higher heat treatment temperature results in higher crystallinity of ZnO and CuO. Conclusion: CuO/ZnO/PVDF/PAN CNFMs were successfully prepared by a combination of BE, heattreatment and hydrothermal method. The ZnO/CuO beads obtained by heat treatment is the key point of growing ZnO/CuO nanocrystals, and the growth temperature has great effect on the morphology of ZnO/CuO nanocrystals.