Preparation of Neodymium Metal by Pyro-Metallurgical Process Using Fluoride Salt

The neodymium fluoride was reduced to metal by thermal reduction or pyro-metallurgical process using calcium as reducing agent. Thermal reduction was carried out in a sealed reactions chamber in inert atmosphere with a nickel crucible having dry calcium fluoride lining. The stoichiometric mixture of neodymium fluoride and calcium metal chips were used in the form of pallets for pyro-metallurgical reactions. Small iodine was also added to increase heat available during ignition and to yield a lower melting and more fluid slag. The contents were heated electrically at a predetermined rate until ignition took place. The reaction was self-supporting and neodymium metal was obtained with fairly good efficiency.

Electrolysis Process for Preparation of Solar Grade Silicon

Studied on electrorefining metallurgical grade silicon to prepare solar grade silicon(SOG-Si) with electrochemical method in molten KCl and NaF mixture salt. Molten KCl and NaF mixture salt as electrolyte, the metallurgical grade silicon as anode and little metal nickel crucible for collecting silicon powder as cathode, electrorefining experiments were performed at 800 and 2.0V for 14h under dry argon atmosphere. The results showed that the metallurgical grade silicon could be dissolved and deposited on the cathode through molten potassium chloride (KCl) and sodium fluoride (NaF) mixture salt electrolyte. The nickel crucible was full of deposit, which was pure silicon by XRD and EDS. Purity of refined silicon was close to 99.99%, most of impurities like B and P were reduced significantly. Impurity level of silicon was reduced to the desired range for SOG-Si by advancement of the materials for the cell components.