Hydrogen bonding in the crystal structure of phurcalite, Ca2[(UO2)3O2(PO4)2]·7H2O: single-crystal X-ray study and TORQUE calculations

The crystal structure of phurcalite, Ca2[(UO2)3O2(PO4)2]·7H2O, orthorhombic, a = 17.3785 (9) Å, b = 15.9864 (8) Å, c = 13.5477 (10) Å, V = 3763.8 (4) Å3, space group Pbca, Z = 8 has been refined from single-crystal XRD data to R = 0.042 for 3182 unique [I > 3σ(I)] reflections and the hydrogen-bonding scheme has been refined by theoretical calculations based on the TORQUE method. The phurcalite structure is layered, with uranyl phosphate sheets of the phosphuranylite topology which are linked by extensive hydrogen bonds across the interlayer occupied by Ca2+ cations and H2O groups. In contrast to previous studies the approach here reveals five transformer H2O groups (compared to three expected by a previous study) and two non-transformer H2O groups. One of the transformer H2O groups is, nevertheless, not linked to any metal cation, which is a less frequent type of H2O bonding in solid state compounds and minerals. The structural formula of phurcalite has been therefore redefined as {Ca2(H2 [3]O)5(H2 [4]O)2}[(UO2)3O2(PO4)2], Z = 8.

Dissolution of poorly soluble uranyl phosphate phases in the Metaautunite Subgroup under uranyl peroxide cage cluster forming conditions

Uranyl phosphate minerals are widespread in uranium deposits and normally exhibit very low solubility in aqueous systems. Uranyl phosphates of the autunite group and metaautunite subgroup impact the mobility of uranium in the environment and have inspired groundwater remediation strategies that emphasize their low solubility. The importance of soluble uranium-bearing macro-anions, including nanoscale uranyl peroxide cage clusters, is largely unexplored relative to solubilization of normally low-solubility uranium minerals. Eight synthetic analogs of metaautunite subgroup minerals have been prepared and placed in various alkaline aqueous solutions containing hydrogen peroxide and tetraethylammonium hydroxide. Each uranyl phosphate studied has a topologically identical anionic sheet of uranyl square bipyramids and phosphate tetrahedra combined with various cations (Li+, Na+, K +, Rb+, Cs+, Mg2+, Ca2+, Ba2+) and water in the interlayer. Uranyl peroxides formed under many of the experimental conditions examined, including solid studtite [(UO2)(O2)(H2O)2](H2O)2 and soluble uranyl peroxide cage clusters containing as many as 28 uranyl ions. Uranyl phosphate solids in contact with solutions in which uranyl peroxide cage clusters formed dissolved extensively or completely. The greatest dissolution of uranyl phosphates occurred in systems that contained cations with larger hydrated radii, Li+ and Na+. The details of the uranium speciation in solution depended on the pH and counter cations provided from the interlayers of the uranyl phosphate solids.