Glass-Ceramic Synthesis of Cr-substituted Strontium Hexaferrite Nanoparticles with Enhanced Coercivity

Magnetically hard ferrites attract considerable interest due to their ability to maintain a high coercivity of nanosized particles and therefore show promising applications as nanomagnets ranging from magnetic recording to biomedicine. Herein, we report an approach to prepare nonsintered single-domain nanoparticles of chromium-substituted hexaferrite via crystallization of glass in the system SrO–Fe2O3–Cr2O3–B2O3. We have observed a formation of plate-like hexaferrite nanoparticles with diameters changing from 20 to 190 nm depending on the annealing temperature. We demonstrated that chromium substitution led to a significant improvement of the coercivity, which varied from 334 to 732 kA m−1 for the smallest and the largest particles, respectively. The results provide a new strategy for producing high-coercivity ferrite nanomagnets.

Investigation of Structural and Luminescent Properties of Sol-Gel-Derived Cr‑Substituted Mg3Al1−xCrx Layered Double Hydroxides

In the present work, Cr-substituted Mg3Al1−xCrx layered double hydroxides (LDHs) were synthesised through the phase conversion of sol-gel-derived mixed-metal oxides in an aqueous medium. The chromium substitution level in the range of 1 to 25 mol% was investigated. It was demonstrated that all synthesised specimens were single-phase LDHs. The results of elemental analysis confirmed that the suggested synthetic sol-gel chemistry approach is suitable for the preparation of LDHs with a highly controllable chemical composition. The surface microstructure of sol-gel-derived Mg3Al1−xCrx LDHs does not depend on the chromium substitution level. The formation of plate-like agglomerated particles, which consist of hexagonally shaped nanocrystallites varying in size from approximately 200 to 300 nm, was observed. Optical properties of the synthesised Mg3Al1−xCrx LDHs were investigated by means of photoluminescence. All Cr-containing powders exhibited characteristic emission in the red region of the visible spectrum. The strongest emission was observed for the sample doped with 5 mol% Cr3+ ions. However, the emission intensity of samples doped with 1–10 mol% Cr3+ ions was relatively similar. A further increase in the Cr3+ ion concentration to 25 mol% resulted in severe concentration quenching.