Strength, Hardness, and Ductility Evidence of Solid Solution Strengthening and Limited Hydrogen Embrittlement in the Alloy System Palladium-Copper (Cu wt. % 5–25)

Strength, hardness, and ductility characteristics were determined for a series of palladium-copper alloys that compositionally vary from 5 to 25 weight percent copper. Alloy specimens subjected to vacuum annealing showed clear evidence of solid solution strengthening. These specimens showed, as a function of increasing copper content, increased yield strength, ultimate strength, and Vickers microhardness, while their ductility was little affected by compositional differences. Annealed alloy specimens subsequently subjected to exposure to hydrogen at 323 K and PH2 = 1 atm showed evidence of hydrogen embrittlement up to a composition of ~15 wt. % Cu. The magnitude of the hydrogen embrittlement decreased with increasing copper content in the alloy.

Theoretical insight into the electrocatalytic reduction of CO2 with different metal ratios and reaction mechanisms on palladium–copper alloys

Environmental impacts of continued CO2 production have led to an increased need for new methods of CO2 removal and energy development.