Facile Synthesis of Cobalt Ferrite (CoFe2O4) Nanoparticles in the Presence of Sodium Bis (2-ethyl-hexyl) Sulfosuccinate and Their Application in Dyes Removal from Single and Binary Aqueous Solutions

A research study was conducted to establish the effect of the presence of sodium bis-2-ethyl-hexyl-sulfosuccinate (DOSS) surfactant on the size, shape, and magnetic properties of cobalt ferrite nanoparticles, and also on their ability to remove anionic dyes from synthetic aqueous solutions. The effect of the molar ratio cobalt ferrite to surfactant (1:0.1; 1:0.25 and 1:0.5) on the physicochemical properties of the prepared cobalt ferrite particles was evaluated using different characterization techniques, such as FT-IR spectroscopy, X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), N2 adsorption-desorption analysis, and magnetic measurements. The results revealed that the surfactant has a significant impact on the textural and magnetic properties of CoFe2O4. The capacity of the synthesized CoFe2O4 samples to remove two anionic dyes, Congo Red (CR) and Methyl Orange (MO), by adsorption from aqueous solutions and the factors affecting the adsorption process, such as contact time, concentration of dyes in the initial solution, pH of the media, and the presence of a competing agent were investigated in batch experiments. Desorption experiments were performed to demonstrate the reusability of the adsorbents.

Effect of nature and degree of crosslinking agent of poly(hydroxy-butyl-methacrylate-co-2-ethyl-hexyl-acrylate) networks on the swelling properties in nematic liquid crystal 5CB

We experimentally measured the effect of nature and concentration of crosslinker on the photopolymerized time of the poly(hydroxy-butyl-methacrylate-co-2-ethyl-hexyl-acrylate)/5CB system. Initial mixtures are composed of monofunctional monomers hydroxy-butyl-methacrylate (HBMA) and 2-ethyl-hexyl-acrylate (2-EHA), and one of the three bifunctional monomers, poly-propylene-glycol-di-acrylate (PPGDA), tri-propylene-glycol-di-acrylate (TPGDA), or 1,6-hexane-diol-di-acrylate (HDDA), and 2-hydroxy-2-methylpropiophenone (Darocur 1173) as a photoinitiator. The copolymers were elaborated via UV irradiation of reactive formulation. The central composite face-centered design of experiments (DoE) has been used to determine the influence of temperature, crosslinking density and their interactions on swelling behavior of poly(HBMA-co-EHA/crosslinker) networks in liquid crystal 5CB. The experimental results and the predicted responses indicate a good correlation and therefore the validity of the used model.