Electrochemical Investigation of the Effect of Process Parameters on the Corrosion Behavior of Aluminum-Cladded Pressure Vessel Steel Using a Friction Stir Diffusion Cladding Process

Surface cladding and coatings are commonly used to protect structures against corrosion in corrosive environments. In this paper, electrochemical properties of friction stir diffusion cladded ASTM A516-70 with corrosion-resistant aluminum alloy grade 5052 are studied. The effect of process parameters, tool rotational and traverse speeds on the corrosion behavior of produced cladded steels was comparatively assessed. Electrochemical analyses revealed that the cladded steel sample provided good corrosion protection performance in comparison with the un-cladded steel substrate following an immersion test of up to 21 days in 3.5% NaCl medium. Increasing the tool traverse speed was found to negatively affect the corrosion resistance. Optimum parameters for the selected cladding system were found to be a 500 rpm tool rotational speed, and a 50 mm/min tool traverse speed for protection against general corrosion. Meanwhile, higher traverse speed demonstrated stable passivation behavior and, therefore, lower propensity for pitting localized corrosion. Post characterization of the exposed area indicated that tool shoulder marks were favorable spots for the accumulation of corrosion products.

Ultrasonic Propagation in Highly Attenuating Insulation Materials

Experiments have been performed to demonstrate that ultrasound in the 100–400 kHz frequency range can be used to propagate signals through various types of industrial insulation. This is despite the fact that they are highly attenuating to ultrasonic signals due to scattering and viscoelastic effects. The experiments used a combination of piezocomposite transducers and pulse compression processing. This combination allowed signal-to-noise levels to be enhanced so that signals reflected from the surface of an insulated and cladded steel pipe could be obtained.

Fatigue Tests and Metallographic of Explosively Cladded Steel-Titanium Bimetal/ Badania Zmęczeniowe I Metalograficzne Bimetalu Stal-Tytan Zgrzewanego Wybuchowo

The paper contains a description of fatigue life tests of titan-steel bimetal. The study involved specimens made of bimetal which was a combination of S355J2 steel and SB G1 265 titanium, which was imposed in the material by explosive cladding method. The research shows that the fatigue life of specimens made of native material, derived from cladded plate is less than the life of specimens of titanium-steel bimetal

Fatigue Life Tests of Explosively Cladded Steel-Titanium Bimetal

The paper contains a description of fatigue life tests of titan-steel bimetal. The study involved specimens made of bimetal which was a combination of S355J2 steel and SB G1 265 titanium, which was imposed in the material by explosive cladding method. The research shows that the fatigue life of specimens made of native material, derived from cladded plate is less than the life of specimens of titanium-steel bimetal.