PEM Single Cells under Differential Conditions: Full Factorial Parameterization of the ORR and HOR Kinetics and Loss Analysis

The anode and cathode kinetics are parameterized based on differential cell measurements. Systematic parameter variations are evaluated to disentangle the dependencies of the electrochemical impedance spectroscopy (EIS) signatures in H2/H2 mode. We introduce a new CO recovery protocol for both electrodes that enables to accurately characterize the hydrogen oxidation reaction (HOR) kinetics. Then, we demonstrate that a compact Tafel kinetics law captures the oxygen reduction reaction (ORR) kinetics for a full factorial grid of conditions, covering a wide range of relative humidities (rH), temperatures, oxygen partial pressures and current densities. This yields the characteristic activation energy and effective reaction order, and we reconcile models that make different assumptions regarding the rH dependency. Moreover, we analyze O2 transport contributions by steady-state and transient limiting current techniques and heliox measurements. Although the rising uncertainty of loss corrections at high current densities makes it impossible to unambiguously identify an intrinsic potential-dependent change of the Tafel slope, our data support that such effect needs not be considered for steady-state cathodic half-cell potentials above 0.8 V.

Ultra-Low Pt Loading in PtCo Catalysts for the Hydrogen Oxidation Reaction: What Role Do Co Nanoparticles Play?

The effect of the nature of the catalyst on the performance and mechanism of the hydrogen oxidation reaction (HOR) is discussed for the first time in this work. HOR is an anodic reaction that takes place in anionic exchange membrane fuel cells (AEMFCs) and hydrogen pumps (HPs). Among the investigated catalysts, Pt exhibited the best performance in the HOR. However, the cost and the availability limit the usage. Co is incorporated as a co-catalyst due to its oxophylic nature. Five different PtCo catalysts with different Pt loading values were synthesized in order to decrease Pt loading. The catalytic activities and the reaction mechanism were studied via electrochemical techniques, and it was found that both features are a function of Pt loading; low-Pt-loading catalysts (Pt loading < 2.7%) led to a high half-wave potential in the hydrogen oxidation reaction, which is related to higher activation energy and an intermediate Tafel slope value, related to a mixed HOR mechanism. However, catalysts with moderate Pt loading (Pt loading > 3.1%) exhibited lower E1/2 than the other catalysts and exhibited a mechanism similar to that of commercial Pt catalysts. Our results demonstrate that Co plays an active role in the HOR, facilitating Hads desorption, which is the rate-determining step (RDS) in the mechanism of the HOR.

Subnanometer high-entropy alloy nanowires enable remarkable hydrogen oxidation catalysis

High-entropy alloys (HEAs) with unique physicochemical properties have attracted tremendous attention in many fields, yet the precise control on dimension and morphology at atomic level remains formidable challenges. Herein, we synthesize unique PtRuNiCoFeMo HEA subnanometer nanowires (SNWs) for alkaline hydrogen oxidation reaction (HOR). The mass and specific activities of HEA SNWs/C reach 6.75 A mgPt+Ru−1 and 8.96 mA cm−2, respectively, which are 2.8/2.6, 4.1/2.4, and 19.8/18.7 times higher than those of HEA NPs/C, commercial PtRu/C and Pt/C, respectively. It can even display enhanced resistance to CO poisoning during HOR in the presence of 1000 ppm CO. Density functional theory calculations reveal that the strong interactions between different metal sites in HEA SNWs can greatly regulate the binding strength of proton and hydroxyl, and therefore enhances the HOR activity. This work not only provides a viable synthetic route for the fabrication of Pt-based HEA subnano/nano materials, but also promotes the fundamental researches on catalysis and beyond.