scholarly journals Parametric Analysis of Electrodeposited Nano-composite Coatings for Abrasive Wear Resistance

10.5772/62153 ◽  
2016 ◽  
Author(s):  
Kavian O. Cooke
Keyword(s):  
Wear Resistance ◽  
Abrasive Wear ◽  
Parametric Analysis ◽  
Composite Coatings ◽  
Abrasive Wear Resistance ◽  
Nano Composite

scholarly journals Structure and Abrasive Wear of Composite HSS M2/WC Coating

2012 ◽  
Vol 2012 ◽  
pp. 1-9
Author(s):  
S. F. Gnyusov ◽  
V. G. Durakov ◽  
S. Yu. Tarasov
Keyword(s):  
Wear Resistance ◽  
Abrasive Wear ◽  
Size Distribution ◽  
Composite Coatings ◽  
Abrasive Wear Resistance ◽  
Metastable Austenite ◽  
Eutectic Carbides ◽  
Reinforcing Particles ◽  
Tungsten Monocarbide ◽  
Carbide Content

Features of phase-structure formation and abrasive wear resistance of composite coatings “WC-M2 steel” worn against tungsten monocarbide have been investigated. It was established that adding 20 wt.% WC to the deposited powder mixture leads to the increase in M6C carbide content. These carbides show a multimodal size distribution consisting of~5.9 μm eutectic carbides along the grain boundaries,~0.25 μm carbides dispersed inside the grains. Also a greater amount of metastable austenite (~88 vol.%) is found. The high abrasive wear resistance of these coatings is provided byγ→α′-martensitic transformation and multimodal size distribution of reinforcing particles.

Abrasive Wear Resistance of Plasma-Sprayed Glass-Composite Coatings

2001 ◽  
Vol 10 (4) ◽  
pp. 599-603 ◽  
Author(s):  
D.T. Gawne ◽  
Z. Qiu ◽  
Y. Bao ◽  
T. Zhang ◽  
K. Zhang
Keyword(s):  
Wear Resistance ◽  
Abrasive Wear ◽  
Composite Coatings ◽  
Abrasive Wear Resistance ◽  
Glass Composite ◽  
Plasma Sprayed

BÖHLER K100

Alloy Digest ◽  
2020 ◽  
Vol 69 (3) ◽  
Keyword(s):  
Wear Resistance ◽  
Physical Properties ◽  
Abrasive Wear ◽  
Tool Steel ◽  
Cold Work ◽  
Abrasive Wear Resistance ◽  
High Carbon ◽  
High Chromium ◽  
Cold Work Tool Steel

Abstract Böhler K100 is a high-carbon, high-chromium (12%), alloy cold-work tool steel that is suitable for medium run tooling in applications where a very good abrasive wear resistance is needed but where demands on chipping resistance are small. This datasheet provides information on composition, physical properties, hardness, and elasticity. It also includes information on forming and machining. Filing Code: TS-788. Producer or source: voestalpine Böhler Edelstahl GmbH & Co.

SANDVIK APM 2730

Alloy Digest ◽  
2019 ◽  
Vol 68 (4) ◽  
Keyword(s):  
Wear Resistance ◽  
Compressive Strength ◽  
Physical Properties ◽  
Abrasive Wear ◽  
Tool Steel ◽  
High Speed ◽  
Heat Treating ◽  
Abrasive Wear Resistance ◽  
Steel Company ◽  
High Compressive Strength

Abstract Sandvik APM 2730 is a powder metallurgical alloyed hot-isostatic-pressed high-speed tool steel with abrasive wear resistance and high-compressive strength. This datasheet provides information on composition, physical properties, and elasticity. It also includes information on heat treating and machining. Filing Code: TS-763. Producer or source: Sandvik Steel Company.

BÖHLER K107

Alloy Digest ◽  
2020 ◽  
Vol 69 (9) ◽  
Keyword(s):  
Wear Resistance ◽  
Physical Properties ◽  
Abrasive Wear ◽  
Cold Work ◽  
Heat Treating ◽  
Abrasive Wear Resistance ◽  
Tungsten Alloy ◽  
High Carbon ◽  
Cold Work Tool Steel ◽  
Very High

Abstract Böhler K107 is a high-carbon (2.1%), 12% chromium. 0.7 % tungsten, alloy cold-work tool steel that is used in applications where a very high abrasive wear resistance is needed, but where demands on chipping resistance are small. This datasheet provides information on composition, physical properties, hardness, and elasticity. It also includes information on forming and heat treating. Filing Code: TS-799. Producer or source: voestalpine Böhler Edelstahl GmbH&Co KG.

On effect of surface hardening on impact and abrasive wear resistance of Hadfi eld steel

2020 ◽  
pp. 252-255
Author(s):  
V.I. Bolobov ◽  
V.S. Bochkov ◽  
E.V. Akhmerov ◽  
V.A. Plashchinsky ◽  
E.A. Krivokrisenko E.A.
Keyword(s):  
Plastic Deformation ◽  
Wear Resistance ◽  
Abrasive Wear ◽  
Work Hardening ◽  
Surface Hardening ◽  
Cold Work ◽  
Abrasive Wear Resistance ◽  
Hadfield Steel ◽  
Mining Equipment ◽  
Effect Of Surface

On the example of Hadfield steel, as the most common material of fast-wearing parts of mining equipment, the effect of surface hardening by plastic deformation on their impact and abrasive wear resistance is considered. Wear test is conducted on magnetic ironstone as typical representative of abrasive and hard rock. As result of wear of initial samples with hardness of ∼200 HB and samples pre-hardened with different intensities to the hardness of 300, 337 and 368 HB, it is found that during the initial testing period, the initial samples pass the “self-cold-work hardening” stage with increase in hardness to ∼250 HB, which remains virtually unchanged during further tests; the hardness of the pre-hardened samples does not change significantly throughout the tests. It is established that the rate of impact-abrasive wear of pre-hardened samples is significantly (up to 1.4 times) lower than the original ones that are not subjected to plastic deformation, and decreases with increasing degree of cold-work hardening. Preliminary surface hardening by plastic deformation can serve as effective way to increase the service life of fast-wearing working parts of mining equipment.

INCREASING THE WEAR RESISTANCE OF THE WORKING BODIES OF AGRICULTURAL MACHINES BY THE HDTV METHOD WITH ADDING POWDER OF THE EED METHOD

2020 ◽  
Vol 4 (141) ◽  
pp. 123-131
Author(s):  
IL’YA ROMANOV ◽  
Keyword(s):  
Wear Resistance ◽  
Abrasive Wear ◽  
High Frequency ◽  
Machine Building ◽  
Abrasive Wear Resistance ◽  
Research Purpose ◽  
Powder Materials ◽  
Agricultural Machinery ◽  
Resource Saving ◽  
Working Bodies

The development of energy and resource-saving methods and technologies for strengthening and restoring the working bodies of agricultural machinery will increase their abrasive wear resistance and durability by using materials from machine-building waste and reduce the cost by 10-30 percent without reducing operational characteristics. (Research purpose) The research purpose is in increasing the abrasive wear resistance and durability of cultivator legs by surfacing powder materials obtained by electroerosive dispersion from solid alloy waste by high-frequency currents. (Materials and methods) Authors obtained a powder for research on their own experimental installations of the CCP "Nano-Center" of electroerosive dispersion from waste of sintered hard alloys of the T15K6 brand. The microhardness of powders and coatings on microshifts was measured using the PMT-3 device, and the hardness of coatings with the KMT-1 microhardometer was measured using the Rockwell method according to GOST 9013-59. The microwave-40AV installation was used to assess the wear resistance of materials of working bodies of tillage machines. (Results and discussion) In the course of laboratory wear tests the relative wear resistance of samples hardened by high-frequency surfacing currents significantly exceeds the wear resistance of non-hardened samples made OF 65g steel, accepted as the reference standard. (Conclusions) Based on the results of experimental studies, the article proposes a new resource-saving technological process for strengthening the working bodies of agricultural machinery through the use of materials from machine-building waste, which allows increasing the abrasive wear resistance of working bodies by 1.5-2 times due to the use of tungsten-containing materials.

Effects of nano-Al2O3 and nano-ZrO2 on the microstructure, behavior and abrasive wear resistance of WC-8Co cemented carbide

Rare Metals ◽  
2011 ◽  
Vol 30 (5) ◽  
pp. 533-538 ◽  
Author(s):  
Tian’en Yang ◽  
Ji Xiong ◽  
Lan Sun ◽  
Zhixing Guo ◽  
Kangcai Qin
Keyword(s):  
Wear Resistance ◽  
Abrasive Wear ◽  
Abrasive Wear Resistance ◽  
Cemented Carbide