High-Resolution Characterization of Intergranular Attack and Stress Corrosion Cracking of Alloy 600 in High-Temperature Primary Water

CORROSION ◽  
2000 ◽  
Vol 56 (6) ◽  
pp. 572-587 ◽  
Author(s):  
L. E. Thomas ◽  
S. M. Bruemmer
Keyword(s):  
High Temperature ◽  
High Resolution ◽  
Stress Corrosion ◽  
Stress Corrosion Cracking ◽  
Corrosion Cracking ◽  
Alloy 600 ◽  
Intergranular Attack ◽  
Primary Water

Relationship Between Acid Intergranular Corrosion and Caustic Stress Corrosion Cracking of Alloy 600

CORROSION ◽  
1977 ◽  
Vol 33 (1) ◽  
pp. 20-26 ◽  
Author(s):  
G. J. THEUS
Keyword(s):  
Heat Treatment ◽  
Stress Corrosion ◽  
Stress Corrosion Cracking ◽  
Corrosion Cracking ◽  
Alloy 600 ◽  
Intergranular Attack ◽  
Electrochemical Tests ◽  
Stress Relieving ◽  
Service Conditions ◽  
The Relationship

Abstract Modified Streicher and 288 C (550 F) electrochemical caustic stress corrosion tests were performed on Alloy 600 to determine the relationship between acid intergranular attack susceptibility and caustic stress corrosion cracking (SCC) susceptibility. Mill annealed and solution annealed materials with and without a subsequent 621 C (1150 F) heat treatment (simulated stress relief) were evaluated. Susceptibility to attack in the Streicher test was greatest for material that had received a 621 C (1150 F) heat treatment, whereas this heat treatment caused the same material to be least susceptible to cracking in the electrochemical tests. The conclusions drawn from these results are: (1) stress relieving Alloy 600 does improve its resistance to caustic SCC, and (2) resistance of Alloy 600 to acid intergranular attack does not imply resistance of Alloy 600 to caustic SCC. Therefore, the results demonstrate the need for selecting corrosion qualification tests which are relevant to service conditions.