In this study, a wood fiber/polylactic acid composite (WPC) filament was used as feedstock to print the WPC part by means of fused deposition modeling (FDM). The morphology and mechanical properties of WPC parts printed at different speeds (30, 50, and 70 mm/s) were determined. The results show that the density of the printed WPC part increased as the printing speed decreased, while its surface color became darker than that of parts printed at a high speed. The printing time decreased with an increasing printing speed; however, there was a small difference in the time saving percentage without regard to the dimensions of the printed WPC part at a given printing speed. Additionally, the tensile and flexural properties of the printed WPC part were not significantly influenced by the printing speed, whereas the compressive strength and modulus of the FDM-printed part significantly decreased by 34.3% and 14.6%, respectively, when the printing speed was increased from 30 to 70 mm/s. Furthermore, scanning electronic microscopy (SEM) illustrated that the FDM process at a high printing speed produced an uneven surface of the part with a narrower width of printed layers, and pull-outs of wood fibers were more often observed on the fracture surface of the tensile sample. These results show that FDM manufacturing at different printing speeds has a substantial effect on the surface color, surface roughness, density, and compressive properties of the FDM-printed WPC part.

scholarly journals Effect of Extrusion Temperature on the Physico-Mechanical Properties of Unidirectional Wood Fiber-Reinforced Polylactic Acid Composite (WFRPC) Components Using Fused Deposition Modeling

Polymers ◽  
2018 ◽  
Vol 10 (9) ◽  
pp. 976 ◽  
Author(s):  
Teng-Chun Yang
Keyword(s):  
Mechanical Properties ◽  
Polylactic Acid ◽  
Fused Deposition Modeling ◽  
Wood Fiber ◽  
Color Difference ◽  
Extrusion Temperature ◽  
Fiber Reinforced ◽  
Substantial Impact ◽  
Fused Deposition ◽  
Deposition Modeling

Wood fiber-reinforced polylactic acid (PLA) composites (WFRPCs) were used as a filament to manufacture the unidirectional WFRPC components by means of fused deposition modeling (FDM). The physico-mechanical properties of the WFRPC components printed at different extrusion temperatures (200, 210, 220, and 230 °C) were determined. The results revealed that most of the physical properties (moisture content, surface roughness, water absorption rate, and thickness swelling rate) of the printed WFRPC component were not significantly influenced by extrusion temperature, while its density and color difference increased as the extrusion temperature increased. Additionally, the tensile and flexural properties of the FDM-printed WFRPC component decreased when the extrusion temperature was more than 200 °C, whereas the compressive strength and internal bond strength increased by 15.1% and 24.3%, respectively, when the extrusion temperature was increased from 200 to 230 °C. Furthermore, scanning electronic microscopy (SEM) demonstrated that the fracture surface of the tensile component printed at a higher extrusion temperature exhibited a better compatibility at fiber/PLA interfaces and good adhesion between the extruded filament segments. These results indicate that the FDM printing process using different extrusion temperatures has a substantial impact on the surface color, density, and mechanical properties of the printed WFRPC component.

Assessing the effect of FDM processing parameters on mechanical properties of PLA parts using Taguchi method

2021 ◽  
pp. 089270572110530
Author(s):  
Nagarjuna Maguluri ◽  
Gamini Suresh ◽  
K Venkata Rao
Keyword(s):  
Mechanical Properties ◽  
Tensile Properties ◽  
Fused Deposition Modeling ◽  
Fracture Strain ◽  
Processing Parameters ◽  
Fused Deposition ◽  
Deposition Modeling ◽  
Nozzle Temperature ◽  
Experimental Runs ◽  
Printing Speed

Fused deposition modeling (FDM) is a fast-expanding additive manufacturing technique for fabricating various polymer components in engineering and medical applications. The mechanical properties of components printed with the FDM method are influenced by several process parameters. In the current work, the influence of nozzle temperature, infill density, and printing speed on the tensile properties of specimens printed using polylactic acid (PLA) filament was investigated. With an objective to achieve better tensile properties including elastic modulus, tensile strength, and fracture strain; Taguchi L8 array has been used for framing experimental runs, and eight experiments were conducted. The results demonstrate that the nozzle temperature significantly influences the tensile properties of the FDM printed PLA products followed by infill density. The optimum processing parameters were determined for the FDM printed PLA material at a nozzle temperature of 220°C, infill density of 100%, and printing speed of 20 mm/s.

Property Enhancement of Carbon Fiber-Reinforced Polylactic Acid Composites Prepared by Fused-Deposition Modeling

2020 ◽  
pp. 455-478
Author(s):  
Pravin R. Kubade ◽  
Hrushikesh B. Kulkarni ◽  
Vinayak C. Gavali
Keyword(s):  
Mechanical Properties ◽  
Additive Manufacturing ◽  
Carbon Fiber ◽  
Polylactic Acid ◽  
Fused Deposition Modeling ◽  
Three Dimensional ◽  
Fiber Reinforced ◽  
Fused Deposition ◽  
Deposition Modeling ◽  
Properties Of Composites

Additive Manufacturing or three-dimensional printing refers to a process of building lighter, stronger three-dimensional parts, manufactured layer by layer. Additive manufacturing uses a computer and CAD software which passes the program to the printer to build the desired shape. Metals, thermoplastic polymers, and ceramics are the preferred materials used for additive manufacturing. Fused deposition modeling is one additive manufacturing technique involving the use of thermoplastic polymer for creating desired shape. Carbon fibers can be added into polymer to strengthen the composite without adding additional weight. Present work deals with the manufacturing of Carbon fiber-reinforced Polylactic Acid composites prepared using fused deposition modeling. Mechanical and thermo-mechanical properties of composites are studied as per ASTM standards and using sophisticated instruments. It is observed that there is enhancement in thermo-mechanical properties of composites due to addition reinforcement which is discussed in detail.

Effect of Printing Parameters on the Mechanical Properties of Parts Fabricated with Open-Source 3D Printers in PLA by Fused Deposition Modeling

2020 ◽  
Vol 22 (4) ◽  
pp. 895-908
Author(s):  
M. Ouhsti ◽  
B. El Haddadi ◽  
S. Belhouideg
Keyword(s):  
Mechanical Properties ◽  
Polylactic Acid ◽  
Fused Deposition Modeling ◽  
Acrylonitrile Butadiene Styrene ◽  
Fused Deposition Modelling ◽  
Fused Deposition ◽  
3D Printers ◽  
Deposition Modeling ◽  
Printed Materials ◽  
Printing Parameters

Abstract3D polymer-based printers have become easily accessible to the public. Usually, the technology used by these 3D printers is Fused Deposition Modelling (FDM). The majority of these 3D printers mainly use acrylonitrile butadiene styrene (ABS) and polylactic acid (PLA) to fabricate 3D objects. In order for the printed parts to be useful for specific applications, the mechanical properties of the printed parts must be known. The aim of this study is to determine the tensile strength and elastic modulus of printed materials in polylactic acid (PLA) according to three important printing parameters such as deposition angle, extruder temperature and printing speed. The central composite design (CCD) was used to reduce the number of tensile test experiments. The obtained results show that the mechanical properties of printed parts depend on printing parameters. Empirical models relating response and process parameters are developed. The analysis of variance (ANOVA) was used to test the validity of models relating response and printing parameters. The optimal printing parameters are determined for the desired mechanical properties.

Sign in / Sign up

Export Citation Format

Share Document