scholarly journals Effects of Curing Conditions on the MECHANICAL and Microstructural Properties of Ultra-High-Performance Concrete (UHPC) Incorporating Iron Tailing Powder

Materials ◽  
2021 ◽  
Vol 14 (1) ◽  
pp. 215
Author(s):  
Dong Lu ◽  
Jing Zhong ◽  
Baobao Yan ◽  
Jing Gong ◽  
Ziye He ◽  
...  
Keyword(s):  
High Performance ◽  
Mechanical Performance ◽  
High Performance Concrete ◽  
Microstructural Properties ◽  
Ultra High Performance Concrete ◽  
Steam Curing ◽  
Curing Conditions ◽  
Curing Method ◽  
Mechanical And Microstructural Properties ◽  
Curing Regime

It has been reported that iron tailing powder (ITP) has the potential to partially replace cement to prepare ultra-high-performance concrete (UHPC). However, the reactivity of ITP particles in concrete largely depends on the curing method. This study investigates the effects of curing conditions on the mechanical and microstructural properties of UHPC containing ITP. To achieve this objective, three research tasks are conducted, including (1) preparing seven concrete formulations by introducing ITP; (2) characterizing their mechanical performance under different curing regimes; and (3) analyzing their microstructure by XRD patterns, FTIR analysis, and SEM observation. The experimental results show that there is an optimum ITP dosage (15%) for their application. The concrete with 15% ITP under standard curing obtains 94.3 MPa at 7 days, their early-age strength could be even further increased by ~30% (warm-water curing) and ~35% (steamed curing). The steam curing regime stimulates the activity of ITP and refines the microstructure. This study demonstrates the potential of replacing Portland cement with ITP in UHPC production.

scholarly journals Effect of Graphene Oxide Nanosheets on Physical Properties of Ultra-High-Performance Concrete with High Volume Supplementary Cementitious Materials

Materials ◽  
2020 ◽  
Vol 13 (8) ◽  
pp. 1929 ◽  
Author(s):  
Yu-You Wu ◽  
Jing Zhang ◽  
Changjiang Liu ◽  
Zhoulian Zheng ◽  
Paul Lambert
Keyword(s):  
Graphene Oxide ◽  
Physical Properties ◽  
High Performance ◽  
High Performance Concrete ◽  
High Volume ◽  
Cementitious Materials ◽  
Supplementary Cementitious Materials ◽  
Ultra High Performance Concrete ◽  
Steam Curing ◽  
Slump Flow

Nanomaterials have been increasingly employed for improving the mechanical properties and durability of ultra-high-performance concrete (UHPC) with high volume supplementary cementitious materials (SCMs). Recently, graphene oxide (GO) nanosheets have appeared as one of the most promising nanomaterials for enhancing the properties of cementitious composites. To date, a majority of studies have concentrated on cement pastes and mortars with fewer investigations on normal concrete, ultra-high strength concrete, and ultra-high-performance cement-based composites with a high volume of cement content. The studies of UHPC with high volume SCMs have not yet been widely investigated. This paper presents an experimental investigation into the mini slump flow and physical properties of such a UHPC containing GO nanosheets at additions from 0.00 to 0.05% by weight of cement and a water–cement ratio of 0.16. The study demonstrates that the mini slump flow gradually decreases with increasing GO nanosheet content. The results also confirm that the optimal content of GO nanosheets under standard curing and under steam curing is 0.02% and 0.04%, respectively, and the corresponding compressive and flexural strengths are significantly improved, establishing a fundamental step toward developing a cost-effective and environmentally friendly UHPC for more sustainable infrastructure.

SUSTAINABLE ULTRA-HIGH-PERFORMANCE GLASS CONCRETE FOR INFRASTRUCTURES

2017 ◽  
Vol 4 (1) ◽  
Author(s):  
Arezki Tagnit-Hamou ◽  
Nancy A. Soliman
Keyword(s):  
High Performance ◽  
Glass Powder ◽  
Mechanical Performance ◽  
High Performance Concrete ◽  
Low Cost ◽  
Research Work ◽  
High Strength ◽  
Quartz Powder ◽  
Ultra High Performance Concrete ◽  
Powder Particles

This paper presents research work on the development of a green type of ultra-high-performance concrete using ground glass powders with different degrees of fineness (UHPGC). This article presents the development of an innovative, low-cost, and sustainable UHPGC through the use of glass powder to replace cement, and quartz powder particles. An UHPGC with a compressive strength (fc) of up to 220 MPa was prepared and its fresh, and mechanical properties were investigated. The test results indicate that the fresh UHPGC properties were improved when the cement and quartz powder were replaced with non-absorptive glass powder particles. The strength improvement can be attributed to the glass powder’s pozzolanicity and to its mechanical performance (very high strength and elastic modulus of glass). A case study of using this UHPGC is presented through the design and construction of a footbridge. Erection of footbridge at University of Sherbrooke Campus using UHPGC is also presented as a full-scale application.

scholarly journals Effect of KyAl4(Si8-y) O20(OH)4 Calcined Based-Clay on the Microstructure and Mechanical Performances of High-Performance Concrete

Crystals ◽  
2021 ◽  
Vol 11 (10) ◽  
pp. 1152
Author(s):  
David O. Nduka ◽  
Babatunde J. Olawuyi ◽  
Olabosipo I. Fagbenle ◽  
Belén G. Fonteboa
Keyword(s):  
High Performance ◽  
High Performance Concrete ◽  
Cementitious Materials ◽  
Attenuated Total Reflection ◽  
Maximum Temperature ◽  
Microstructural Properties ◽  
Calcined Clay ◽  
X Ray ◽  
Cement Replacement ◽  
Mechanical And Microstructural Properties

The work described in this paper has been performed to determine the potential use of meta-illite (KyAl4(Si8-y) O20(OH)4) calcined clay (MCC) as a supplementary cementitious material (SCM) in a binary Portland cement (PC) for high-performance concrete (HPC) production. To obtain the properties of the cementitious materials, the chemical composition, mineral phases, morphology, calcination efficiency and physical properties were quantitatively analysed using the advanced techniques of X-ray fluorescence (XRF), scanning electron microscopy/energy dispersive X-ray (SEM/EDX), X-ray diffraction (XRD), Fourier transform infrared/attenuated total reflection (FTIR/ATR), thermogravimetric analysis (TGA), laser particle sizing and Brunauer–Emmett–Teller (BET) nitrogen absorption method. The MCC’s effect on the workability and mechanical properties (compressive, splitting tensile and flexural strengths) and microstructure (morphology and crystalline phases) of hardened MCC-based HPCs were determined. The XRF result shows that the oxide composition of MCC confirmed the pozzolanic material requirements with recorded high useful oxides content. At the same time, the SEM image presents particles of broad, solid masses with a wider surface area of irregular shape. The XRD results show that the MCC was majorly an illite-based clay mineral calcined at a maximum temperature of 650 °C, as revealed by the TGA. The MCC addition increases the slump flow of HPCs at 5–15% cement replacement. The MCC incorporation at 10% cement replacement best improved the porosity of HPCs at a later age resulting in increased mechanical and microstructural properties of tested samples. Therefore, it is recommended that MCC addition within 10% cement replacement be adopted for low W/B Class I HPC at no deleterious results on mechanical and microstructural properties of the concrete.

scholarly journals Mechanical Performance and Microstructure of Ultra-High-Performance Concrete Modified by Calcium Sulfoaluminate Cement

2021 ◽  
Vol 2021 ◽  
pp. 1-9
Author(s):  
Meimei Song ◽  
Chuanlin Wang ◽  
Ying Cui ◽  
Qiu Li ◽  
Zhiyang Gao
Keyword(s):  
Compressive Strength ◽  
High Performance ◽  
Mechanical Performance ◽  
High Performance Concrete ◽  
Autogenous Shrinkage ◽  
Ultra High Performance Concrete ◽  
Maximum Heat ◽  
Degree Of Hydration ◽  
Calcium Sulfoaluminate ◽  
Shrinkage Property

High autogenous shrinkage property is one of the disadvantages of ultra-high-performance concrete (UHPC), which may induce early age cracking and threaten the safety of concrete structure. In the present study, different dosages of calcium sulfoaluminate (CSA) cement were added in UHPC as an effective expansive binder. Hydration mechanism, autogenous shrinkage property, and compressive strength of UHPC were carried out to investigate the effect of CSA addition on the mechanical properties of UHPC. Scanning electron microscopy was also employed to characterize the intrinsic microstructural reasons relating to the changes in macroproperties. Based on the XRD diagram, increasing formation of ettringite and Ca(OH)2 can be found with increasing CSA content up to 15%. In the heat flow results of UHPC with 10% CSA addition, the maximum heat release increases to 2.6 mW/g, which is 8.3% higher than the reference UHPC, suggesting a higher degree of hydration with CSA addition. The results in autogenous shrinkage show that CSA expansion agent plays a significantly beneficial role in improving the autogenous shrinkage of UHPC. The corresponding autogenous shrinkage of UHPC is −59.66 μ ε , −131.11 μ ε , and −182.31 μ ε , respectively, at 7 d with 5%, 10%, and 15% addition, which is 108%, 117%, and 123% reduction compared to the reference specimen without CSA. In terms of compressive strength, UHPC with 5%, 10%, 15%, and 20% CSA addition has 10.5%, 17.4%, 30.2%, and 22.1% higher compressive strength than that for the reference UHPC at 28 d. Microstructural study shows that there is an extremely dense microstructure in both the bulk matrix and interfacial transition zone of UHPC with 10% CSA addition, which can be attributed to the higher autogenous shrinkage property and can therefore result in higher mechanical performance.

Ultra-High-Performance Concrete Shear Keys in Concrete Bridge Superstructures

2020 ◽  
pp. 036119812096472
Author(s):  
Elsy Y. Flores ◽  
Jordan Varbel ◽  
William K. Toledo ◽  
Craig M. Newtson ◽  
Brad D. Weldon
Keyword(s):  
High Performance ◽  
Load Transfer ◽  
Mechanical Performance ◽  
High Performance Concrete ◽  
Surface Preparation ◽  
Ultra High Performance Concrete ◽  
Direct Tension ◽  
Girder Bridges ◽  
Grouting Material ◽  
Shear Keys

This research investigated the use of locally produced, non-proprietary ultra-high-performance concrete (UHPC) as a grouting material to repair deteriorated shear keys. Shear keys are used in adjacent girder superstructures to produce monolithic behavior and load transfer across the structure. Shear key degradation can jeopardize the integrity of the structure. Transportation agencies have reported that 75% of distress in adjacent girder bridges is because of cracking and de-bonding along shear keys. Previous research has shown that locally produced UHPC has excellent mechanical and durability properties. UHPC has also been shown to have good bonding characteristics that are desirable in a potential grouting material. Bond strength between UHPC grout and substrate concrete was evaluated using slant-shear and direct tension tests. Results showed that adequate bond was achieved at 7 days. Low strengths at 28 days were observed because of low strength of the substrate concrete. Shrinkage of UHPC grout was also investigated. Shrinkage at 28 days was less than 600 µstrain which is acceptable for repair practices. Full-scale testing was used to evaluate load-deflection behavior of channel girder assemblages with grouted shear keys. Results showed that UHPC grout and non-shrink grout had similar mechanical performance. Excellent bond was achieved with all grouts, even with minimal surface preparation. The similar performances of the non-shrink grout and the UHPC grout indicates that UHPC grout does not provide a mechanical benefit over the non-shrink grout.

scholarly journals Early-Age Strength of Ultra-High Performance Concrete in Various Curing Conditions

Materials ◽  
2015 ◽  
Vol 8 (8) ◽  
pp. 5537-5553 ◽  
Author(s):  
Jong-Sup Park ◽  
Young Kim ◽  
Jeong-Rae Cho ◽  
Se-Jin Jeon
Keyword(s):  
High Performance ◽  
High Performance Concrete ◽  
Early Age ◽  
Ultra High Performance Concrete ◽  
Curing Conditions

Numerical analyses on flexural performance of prefabricated UHPC link slab

2021 ◽  
Author(s):  
Bruno Briseghella ◽  
Wei Xu ◽  
Jun-Qing Xue ◽  
Jian-hui Lin ◽  
Camillo Nuti
Keyword(s):  
Crack Resistance ◽  
Bearing Capacity ◽  
High Performance ◽  
High Performance Concrete ◽  
Labor Cost ◽  
Ultimate Bearing Capacity ◽  
Ultra High Performance Concrete ◽  
Steam Curing ◽  
Expansion Joints

<p><br clear="none"/></p><p>The expansion joints in the multi-span simply supported bridge can be eliminated by using the link slab. The ultra-high performance concrete (UHPC) with high tensile strength and crack resistance is an effective material for the link slab. However, the cast-in-situ UHPC link slab need to be cured with steam curing. Therefore, the construction processes are complicated and the construction quality is difficult to guarantee. In this paper, the prefabricated UHPC link slab which can be assembled on site to simply the construction process, accelerate the construction speed and reduce the labor cost was proposed. Finite element models of the prefabricated and cast-in-situ UHPC link slabs under bending were built by using ABAQUS. The ultimate bearing capacity of the prefabricated link slab was nearly the same of the cast in situ and the crack resistance slightly lower. Finally, the influence of the bolt (used to connect the prefabricated link slab) number and the distance from the bolt to the edge of the link slab on the crack resistance and ultimate bearing capacity of the prefabricated link slab were obtained.</p>

Sign in / Sign up

Export Citation Format

Share Document