scholarly journals Strong Interactions between Austenite and the Matrix of Medium-Mn Steel during Intercritical Annealing

Materials ◽  
2020 ◽  
Vol 13 (15) ◽  
pp. 3366 ◽  
Author(s):  
Tianpeng Zhou ◽  
Cunyu Wang ◽  
Chang Wang ◽  
Wenquan Cao ◽  
Zejun Chen
Keyword(s):  
Grain Size ◽  
Annealing Temperature ◽  
Ferrite Matrix ◽  
Strong Interactions ◽  
Recrystallization Process ◽  
Austenite Grain Size ◽  
Recrystallization Kinetics ◽  
Average Grain Size ◽  
The Matrix ◽  
Austenite Grains

The effects of heat treatment on the microstructure evolution was studied in regards to austenite nucleation and grain growth. It was found that the austenite nucleation and matrix recrystallization kinetics of samples annealed at 675 °C for different times were revealed, implying a strong interaction between the ferrite matrix and austenite. The recrystallization of the matrix during annealing provided favorable conditions for austenite nucleation and growth, and the formation of austenite during this process reduced the matrix recrystallization kinetics, thus delaying the recrystallization process of the matrix around the austenite grains. The statistical results for the austenite grain size under different annealing temperatures indicated that the average grain size of the austenite slightly increases with increasing of the annealing temperature, but the austenite with the largest grain size grows faster at the same temperature. This difference is attributed to the strict Kurdjumov Sachs (KS) orientation relationship (OR) between the austenite grains and the matrix, because the growth of austenite with a strict KS OR with the matrix is often inhibited during annealing. In contrast, the austenite maintains a non-strict KS OR with the matrix and can grow preferentially with increasing annealing temperature and time.

scholarly journals Kinetics of Austenite Grain Growth during a Continuous Heating of a Niobium Microalloyed Steel

2004 ◽  
Vol 467-470 ◽  
pp. 929-934 ◽  
Author(s):  
David San Martín ◽  
Francisca García Caballero ◽  
Carlos Capdevila ◽  
C. Carcía de Andrés
Keyword(s):  
Grain Size ◽  
Grain Boundaries ◽  
Heating Rate ◽  
Grain Growth ◽  
Continuous Heating ◽  
Second Phase ◽  
Austenite Grain Size ◽  
Austenite Grain ◽  
Average Grain Size ◽  
The Matrix

Grain growth is a thermally activated process in which the average grain size increases as temperature and time increases. The driving force for grain growth results from the decrease in the free energy associated with the reduction in total grain boundary energy. There are several known factors that influence the migration of grain boundaries such as second phase particles precipitated in the matrix and the solute elements segregated at grain boundaries. The austenite grain boundaries are revealed using the thermal etching method. Carbon extraction replicas were prepared to determine the composition and size of precipitates present in the matrix. In this work, the evolution of the average prior austenite grain size (PAGS) of a low carbon steel microalloyed with niobium is studied as a function of temperature and heating rate. Austenite grains show a two-stage growth. It has been found that as heating rate increases, the grain coarsening temperature (TGC) increases and the grain size at that temperature decreases. TGC temperature lies around 40-60°C below the temperature for complete dissolution of carbonitrides (TDISS).

scholarly journals Effect of Vanadium Reinforcement on the Microstructure and Mechanical Properties of Magnesium Matrix Composites

Crystals ◽  
2021 ◽  
Vol 11 (7) ◽  
pp. 806
Author(s):  
Liqing Sun ◽  
Shuai Sun ◽  
Haiping Zhou ◽  
Hongbin Zhang ◽  
Gang Wang ◽  
...  
Keyword(s):  
Grain Size ◽  
Grain Refinement ◽  
Milling Process ◽  
Mg Alloy ◽  
Matrix Composites ◽  
Magnesium Matrix Composites ◽  
Pinning Effect ◽  
Average Grain Size ◽  
The Matrix ◽  
Hot Press Sintering

In this work, vanadium particles (VP) were utilized as a novel reinforcement of AZ31 magnesium (Mg) alloy. The nanocrystalline (NC) AZ31–VP composites were prepared via mechanical milling (MM) and vacuum hot-press sintering. During the milling process, the presence of VP contributed to the cold welding and fracture mechanism, resulting in the acceleration of the milling process. Additionally, increasing the VP content accelerated the grain refinement of the matrix during the milling process. After milling for 90 h, the average grain size of AZ31-X wt % Vp (X = 5, 7.5, 10) was refined to only about 23 nm, 19 nm and 16 nm, respectively. In the meantime, VP was refined to sub-micron scale and distributed uniformly in the matrix, exhibiting excellent interfacial bonding with the matrix. After the sintering process, the average grain size of AZ31-X wt % VP (X = 5, 7.5, 10) composites still remained at the NC scale, which was mainly caused by the pinning effect of VP. Besides that, the porosity of the sintered composites was no more than 7.8%, indicating a good densification effect. As a result, there was little difference between the theoretical and real density. Compared to as-cast AZ31 Mg alloy, the microhardness of sintered AZ31-X wt % VP (X = 5, 7.5, 10) composites increased by 65%, 87% and 96%, respectively, owing to the strengthening mechanisms of grain refinement strengthening, Orowan strengthening and load-bearing effects.

Austenite Grain Evolution Mechanism of High Carbon Rail Based on Thermal Technology

2020 ◽  
Vol 837 ◽  
pp. 74-80
Author(s):  
Jun Yuan ◽  
Zhen Yu Han ◽  
Yong Deng ◽  
Da Wei Yang
Keyword(s):  
Grain Size ◽  
Tensile Strength ◽  
Rail Steel ◽  
Heating Temperature ◽  
Great Influence ◽  
Stable Operation ◽  
High Carbon ◽  
Austenite Grain Size ◽  
Austenite Grain ◽  
Austenite Grains

In view of the special requirements of rails to ensure the safe and stable operation of Railways in China, the formation characteristics of austenite grains in high carbon rail are revealed through industrial exploration, the process of industrial rail heating and rolling is simulated, innovative experimental research methods such as different heating and heat treatment are carried out on the actual rails in the laboratory. Transfer characteristics of austenite grain size, microstructures and key properties of high carbon rail during the process are also revealed. The results show that the austenite grain size of industrial produced U75V rail is about 9.0 grade. When the holding temperature is increased from 800 C to 1300 C, the austenite grain size of high carbon rail steel decreases, the austenite grain are gradually coarsened, and the tensile strength increases slightly. The tensile strength is affected by the heating temperature. With the increase of heating temperature, the elongation and impact toughness of high carbon rail decrease. The heating temperature of high carbon rail combined with austenite grain size shows that the heating temperature has a great influence on austenite grain size, and has the most obvious influence on the toughness of high carbon rail.

scholarly journals The Influence of Annealing Temperature on the Structure and Magnetic Properties of Nanocrystalline BiFeO3 Prepared by Sol–Gel Method

2021 ◽  
Author(s):  
T. Pikula ◽  
T. Szumiata ◽  
K. Siedliska ◽  
V. I. Mitsiuk ◽  
R. Panek ◽  
...  
Keyword(s):  
Grain Size ◽  
Magnetic Properties ◽  
Annealing Temperature ◽  
Sol Gel ◽  
Weak Ferromagnetism ◽  
X Ray Diffraction ◽  
Gel Method ◽  
Sol Gel Method ◽  
Average Grain Size ◽  
Spin Cycloid

AbstractIn this work, BiFeO3 powders were synthesized by a sol–gel method. The influence of annealing temperature on the structure and magnetic properties of the samples has been discussed. X-ray diffraction studies showed that the purest phase was formed in the temperature range of 400 °C to 550 °C and the samples annealed at a temperature below 550 °C were of nanocrystalline character. Mössbauer spectroscopy and magnetization measurements were used as complementary methods to investigate the magnetic state of the samples. In particular, the appearance of weak ferromagnetic properties, significant growth of magnetization, and spin-glass-like behavior were observed along with the drop of average grain size. Mössbauer spectra were fitted by the model assuming cycloidal modulation of spins arrangement and properties of the spin cycloid were determined and analyzed. Most importantly, it was proved that the spin cycloid does not disappear even in the case of the samples with a particle size well below the cycloid modulation period λ = 62 nm. Furthermore, the cycloid becomes more anharmonic as the grain size decreases. The possible origination of weak ferromagnetism of the nanocrystalline samples has also been discussed.

Thermal Stability of Ultrafine-Grained Pure Titanium Processed by High-Pressure Torsion

2021 ◽  
Vol 1016 ◽  
pp. 338-344
Author(s):  
Wan Ji Chen ◽  
Jie Xu ◽  
De Tong Liu ◽  
De Bin Shan ◽  
Bin Guo ◽  
...  
Keyword(s):  
Activation Energy ◽  
Thermal Stability ◽  
Grain Size ◽  
High Pressure ◽  
Annealing Temperature ◽  
High Pressure Torsion ◽  
Stored Energy ◽  
Ultrafine Grained ◽  
Average Grain Size ◽  
Thermal Stability Of

High-pressure torsion (HPT) was conducted under 6.0 GPa on commercial purity titanium up to 10 turns. An ultrafine-grained (UFG) pure Ti with an average grain size of ~96 nm was obtained. The thermal properties of these samples were studied by using differential scanning calorimeter (DSC) which allowed the quantitative determination of the evolution of stored energy, the recrystallization temperatures, the activation energy involved in the recrystallization of the material and the evolution of the recrystallized fraction with temperature. The results show that the stored energy increases, beyond which the stored energy seems to level off to a saturated value with increase of HPT up to 5 turns. An average activation energy of about 101 kJ/mol for the recrystallization of 5 turns samples was determined. Also, the thermal stability of the grains of the 5 turns samples with subsequent heat treatments were investigated by microstructural analysis and Vickers microhardness measurements. It is shown that the average grain size remains below 246 nm when the annealing temperature is below 500 °C, and the size of the grains increases significantly for samples at the annealing temperature of 600 °C.

Effect of Austenitizing Temperature on the Quenching Microstructure and Properties of 51CrV4

2019 ◽  
Vol 944 ◽  
pp. 357-363
Author(s):  
Xiao Dong Zhang ◽  
Dian Xiu Xia ◽  
Shou Ren Wang
Keyword(s):  
Grain Size ◽  
Austenitizing Temperature ◽  
Austenite Grain Size ◽  
Microstructure And Properties ◽  
Austenite Grain ◽  
Test Steel ◽  
Austenite Grains ◽  
Martensite Structure

The effect of austenitizing temperature on the quenching microstructure and properties of 51CrV4 steel was studied. The results show that with the increase of austenitizing temperature, the austenite grains grow gradually. After quenching, the hardness increased first and then decreased, and the strength increased first and then decreased after tempering at 460°C. When the austenitizing temperature was 880°C, the austenite grains were fine and uniform, about 16μm, the martensite structure was dense, the strength and hardness reached maximum. When the austenitizing temperature was 910°C, the decarburization phenomenon was obvious, and the strength, hardness and plasticity of the test steel decreased obviously. When the austenitizing temperature exceeded 910°C, the austenite grains grow sharply and some grains were abnormally coarse. The austenite grain size reached 20μm and the microstructure was coarser at austenitizing temperature of 950°C. Therefore, in order to ensure uniform grain size and no decarburization under the premise of complete austenitization, the best austenitizing temperature of 51CrV4 steel for good properties is 880°C.

scholarly journals Exploring the Difference in Bainite Transformation with Varying the Prior Austenite Grain Size in Low Carbon Steel

Metals ◽  
2018 ◽  
Vol 8 (12) ◽  
pp. 988 ◽  
Author(s):  
Liangyun Lan ◽  
Zhiyuan Chang ◽  
Penghui Fan
Keyword(s):  
Grain Size ◽  
Prior Austenite ◽  
Low Carbon Steel ◽  
Low Carbon ◽  
Bainite Transformation ◽  
Austenite Grain Size ◽  
Austenite Grain ◽  
Austenite Grains ◽  
Prior Austenite Grain Size ◽  
Prior Austenite Grain

The simulation welding thermal cycle technique was employed to generate different sizes of prior austenite grains. Dilatometry tests, in situ laser scanning confocal microscopy, and transmission electron microscopy were used to investigate the role of prior austenite grain size on bainite transformation in low carbon steel. The bainite start transformation (Bs) temperature was reduced by fine austenite grains (lowered by about 30 °C under the experimental conditions). Through careful microstructural observation, it can be found that, besides the Hall–Petch strengthening effect, the carbon segregation at the fine austenite grain boundaries is probably another factor that decreases the Bs temperature as a result of the increase in interfacial energy of nucleation. At the early stage of the transformation, the bainite laths nucleate near to the grain boundaries and grow in a “side-by-side” mode in fine austenite grains, whereas in coarse austenite grains, the sympathetic nucleation at the broad side of the pre-existing laths causes the distribution of bainitic ferrite packets to be interlocked.

MICROSTRUCTURE EVALUATION OF Fe-BASED AMORPHOUS ALLOYS INVESTIGATED BY DOPPLER BROADENING POSITRON ANNIHILATION TECHNIQUE

2013 ◽  
Vol 27 (19) ◽  
pp. 1341014
Author(s):  
WEI LU ◽  
PING HUANG ◽  
YUXIN WANG ◽  
BIAO YAN
Keyword(s):  
Grain Size ◽  
Positron Annihilation ◽  
Amorphous Alloys ◽  
Annealing Temperature ◽  
Amorphous Matrix ◽  
Nanocrystalline Phase ◽  
Magnetic Alloy ◽  
Type I ◽  
Doppler Broadening ◽  
Average Grain Size

Microstructure of Fe -based amorphous and nanocrystalline soft magnetic alloy has been investigated by X-ray diffraction (XRD), transmission electronic microscopy (TEM) and Doppler broadening positron annihilation technique (PAT). Doppler broadening measurement reveals that amorphous alloys (Finemet, Type I) which can form a nanocrystalline phase have more defects (free volume) than alloys (Metglas, Type II) which cannot form this microstructure. XRD and TEM characterization indicates that the nanocrystallization of amorphous Finemet alloy occurs at 460°C, where nanocrystallites of α- Fe with an average grain size of a few nanometers are formed in an amorphous matrix. With increasing annealing temperature up to 500°C, the average grain size increases up to around 12 nm. During the annealing of Finemet alloy, it has been demonstrated that positron annihilates in quenched-in defect, crystalline nanophase and amorphous-nanocrystalline interfaces. The change of line shape parameter S with annealing temperature in Finemet alloy is mainly due to the structural relaxation, the pre-nucleation of Cu nucleus and the nanocrystallization of α- Fe ( Si ) phase during annealing. This study throws new insights into positron behavior in the nanocrystallization of metallic glasses, especially in the presence of single or multiple nanophases embedded in the amorphous matrix.

The Effects of Hot Deformation Parameters on the Size of Dynamically Recrystallised Austenite Grains of HSLA Steel

2019 ◽  
Author(s):  
Sebastian Gnapowski ◽  
Elżbieta Kalinowska- Ozgowicz ◽  
Mariusz Sniadkowski ◽  
Aleksandra Pietraszek
Keyword(s):  
Grain Size ◽  
Hot Deformation ◽  
Hsla Steel ◽  
Optical Microscope ◽  
Austenite Grain Size ◽  
Deformation Parameters ◽  
Austenite Grain ◽  
Austenite Grains ◽  
Ebsd Technique ◽  
Scanning Electron

This paper presents the results of investigations of the effects of hot deformation parameters in compression investigation on the austenite grain size in HSLA steel (0.16% C, 0.037% Nb, 0.004% Ti, 0.0098% N). The axisymmetric compression investigations were performed on cylindrical investigation specimens of d=1.2 using the Gleeble 3800 simulator. The strain rate=1s-1÷15.9s-1 and strain degree ε=1.2. Before deformation, the research specimens were austenitized at TA = 1100 ÷ 1250 °C. Metallographic observations of the primary austenite grains were conducted with an optical microscope, while the structure of dynamically recrystallized austenite, inherited by martensite, was examined by EBSD technique using a scanning electron microscope. Based on the analysis of investigation results, it was found that the size of dynamically recrystallized austenite grains in HSLA steel were clearly affected by hot compression parameters. In contrast, no significant impact of austenitising temperature on their size was found.

Effect of Annealing Time on the Microstructure and Texture of Interstitial Free Steel

2012 ◽  
Vol 535-537 ◽  
pp. 593-596
Author(s):  
Zhi Fen Wang ◽  
Rong Dong Han ◽  
Shun Bing Zhou ◽  
Zhong Hai Yao ◽  
Li Xin Wu
Keyword(s):  
Grain Size ◽  
Annealing Time ◽  
Electron Backscatter Diffraction ◽  
Recrystallization Process ◽  
Interstitial Free ◽  
X Ray Diffraction ◽  
Steel Sheets ◽  
Grain Boundary Character ◽  
Average Grain Size ◽  
Backscatter Diffraction

Effect of annealing time on the microstructure and texture of IF steel sheets was investigated. Average grain size, grain boundary character and recrystallization texture were measured by X-ray diffraction (XRD) and electron backscatter diffraction (EBSD) in order to clarify the effect of annealing time on microstructure of recrystallization process. The average grain size increased with increasing annealing time. With rising annealing time, the number of low angle boundary (0～15o) decreased due to the mergence of grain with sub-boundary. The //ND (-fiber) pole intensity had a highest value annealed at 60s. The annealing time played an important role in recrystallization process which affected the mechanical properties and microstructure of IF steels.