scholarly journals Biocomposites Produced from Hardwood Particles by Equal Channel Angular Pressing: Effects of Pre-Treatment

2020 ◽  
Vol 4 (4) ◽  
pp. 181
Author(s):  
Yu Bai ◽  
Xiaoqing Zhang ◽  
Kenong Xia
Keyword(s):  
Mechanical Properties ◽  
Equal Channel Angular Pressing ◽  
Agricultural Waste ◽  
Flexural Modulus ◽  
Cross Linking ◽  
Binding Agent ◽  
Angular Pressing ◽  
Particle Processing ◽  
Wood Particles ◽  
Pre Treatment

The benefit of using a combination of alkali pre-treatment and ball milling in processing hardwood particles into biocomposites via equal channel angular pressing (ECAP) was demonstrated. The penetration of bonding additives (polyethyleneimine and tannic acid) into hardwood structures was enhanced by the pre-treatment, resulting in plasticization and cross-linking derived from the additives during the particle processing. A significant improvement in the biocomposites’ mechanical properties was obtained, reaching flexural strength of 28–29 MPa and flexural modulus of 3650 MPa, comparable to those displayed by commercial wood fiberboard using thermosetting resins as the binding agent. This adds to the promise of developing biocomposites from industrial or agricultural waste through the simple and efficient ECAP technology in conjunction with common pre-treatment methodologies for wood particles.

scholarly journals Effects of equal channel angular pressing and heat treatments on the microstructures and mechanical properties of selective laser melted and cast AlSi10Mg alloys

2021 ◽  
Vol 21 (3) ◽  
Author(s):  
Przemysław Snopiński ◽  
Mariusz Król ◽  
Marek Pagáč ◽  
Jana Petrů ◽  
Jiří Hajnyš ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Low Temperature ◽  
Equal Channel Angular Pressing ◽  
Heat Treatments ◽  
Electron Backscattered Diffraction ◽  
Angular Pressing ◽  
Low Temperature Annealing ◽  
Transmission Electron ◽  
Before And After ◽  
The Impact

AbstractThis study investigated the impact of the equal channel angular pressing (ECAP) combined with heat treatments on the microstructure and mechanical properties of AlSi10Mg alloys fabricated via selective laser melting (SLM) and gravity casting. Special attention was directed towards determining the effect of post-fabrication heat treatments on the microstructural evolution of AlSi10Mg alloy fabricated using two different routes. Three initial alloy conditions were considered prior to ECAP deformation: (1) as-cast in solution treated (T4) condition, (2) SLM in T4 condition, (3) SLM subjected to low-temperature annealing. Light microscopy, transmission electron microscopy, X-ray diffraction line broadening analysis, and electron backscattered diffraction analysis were used to characterize the microstructures before and after ECAP. The results indicated that SLM followed by low-temperature annealing led to superior mechanical properties, relative to the two other conditions. Microscopic analyses revealed that the partial-cellular structure contributed to strong work hardening. This behavior enhanced the material’s strength because of the enhanced accumulation of geometrically necessary dislocations during ECAP deformation.

Microstructures and Mechanical Properties of AZ61 Mg Alloy Processed by Equal Channel Angular Pressing

2012 ◽  
Vol 468-471 ◽  
pp. 2124-2127 ◽  
Author(s):  
Shao Feng Zeng ◽  
Kai Huai Yang ◽  
Wen Zhe Chen
Keyword(s):  
Mechanical Properties ◽  
Grain Size ◽  
Equal Channel Angular Pressing ◽  
Uniform Elongation ◽  
Considerable Decrease ◽  
Angular Pressing ◽  
Az61 Magnesium Alloy ◽  
Average Grain Size ◽  
Microstructures And Mechanical Properties ◽  
Bimodal Grain Size

Equal channel angular pressing (ECAP) was applied to a commercial AZ61 magnesium alloy for up to 8 passes at temperatures as low as 473K. Microstructures and mechanical properties of as-received and ECAP deformed samples were investigated. The microstructure was initially not uniform with a “bimodal” grain size distribution but became increasingly homogeneous with further ECAP passes and the average grain size was considerably reduced from over 26 μm to below 5 μm. The ultimate tensile strength (UTS) decreases clearly after one pass, but increases significantly up to two passes, and then continuously slowly decreases up to six passes, and again increases slightly up to eight passes. In contrast, the uniform elongation increased significantly up to 3 passes, followed by considerable decrease up to 8 passes. These observations may be attributed to combined effects of grain refinement and texture development.