scholarly journals Leachability and Decay Resistance of Wood Polyesterified with Sorbitol and Citric Acid

Forests ◽  
2020 ◽  
Vol 11 (6) ◽  
pp. 650 ◽  
Author(s):  
Greeley Beck
Keyword(s):  
Cell Wall ◽  
Citric Acid ◽  
Moisture Content ◽  
Brown Rot ◽  
Decay Resistance ◽  
White Rot ◽  
Modification System ◽  
Sorption Behaviour ◽  
Wood Modification ◽  
Water Saturated

Research Highlights: Polyesterification of wood with sorbitol and citric acid (SCA) increases decay resistance against brown-rot and white-rot fungi without reducing cell wall moisture content but the SCA polymer is susceptible to hydrolysis. Background and Objectives: SCA polyesterification is a low-cost, bio-based chemical wood modification system with potential for commercialisation. Materials and Methods: This study investigates moisture-related properties and decay resistance in SCA-modified wood. Scots pine sapwood was polyesterified at 140 °C with various SCA solution concentrations ranging from 14–56% w/w. Dimensional stability was assessed and leachates were analysed with high-performance liquid chromatography (HPLC). Chemical changes were characterized with attenuated total reflection Fourier-transform infrared spectroscopy (ATR-FTIR) and spectra were quantitatively compared with peak ratios. Low-field nuclear magnetic resonance (LFNMR) relaxometry was used to assess water saturated samples and decay resistance was determined with a modified EN113 test. Results: Anti-swelling efficiency (ASE) ranged from 23–43% and decreased at higher weight percentage gains (WPG). Reduced ASE at higher WPG resulted from increased water saturated volumes for higher treatment levels. HPLC analysis of leachates showed detectable citric acid levels even after an EN84 leaching procedure. ATR-FTIR analysis indicated increased ester content in the SCA-modified samples and decreased hydroxyl content compared to controls. Cell wall water assessed by non-freezing moisture content determined with LFNMR was found to increase because of the modification. SCA-modified samples resisted brown-rot and white-rot decay, with a potential decay threshold of 50% WPG. Sterile reference samples incubated without fungi revealed substantial mass loss due to leaching of the samples in a high humidity environment. The susceptibility of the SCA polymer to hydrolysis was confirmed by analysing the sorption behaviour of the pure polymer in a dynamic vapour sorption apparatus. Conclusions: SCA wood modification is an effective means for imparting decay resistance but, using the curing parameters in the current study, prolonged low-level leaching due to hydrolysis of the SCA polymer remains a problem.

Effect of Heat Treatment on Decay Resistance of Chinese Fir and Pine

2012 ◽  
Vol 468-471 ◽  
pp. 1118-1122
Author(s):  
Yan Jun Li ◽  
Lan Xing Du ◽  
Gou Ying Hu ◽  
Xing Xia Ma
Keyword(s):  
Heat Treatment ◽  
Moisture Content ◽  
Treatment Time ◽  
Brown Rot ◽  
Decay Resistance ◽  
Chinese Fir ◽  
Heat Treatment Time ◽  
White Rot ◽  
Heat Treated ◽  
Brown Rot Fungus

To enhance decay resistance, the effect of heat treatment and the variation of chemical composition on Chinese Fir and Pine were investigated in this study — heat treatment temperature was 170°C, 190°C and 210°C, respectively, heat treatment time was 2, 3 and 4hours, respectively. Both of them were subsequently exposed to white-rot fungus and brown-rot fungus. The results showed that:(1) With the increasing of the heat treatment, decay resistance of Chinese Fir and Pine were improved, anti-corrosion of Pine after being heat treated at 190°C which were exposed to write-rot fungus can reach I, anti-corrosion of Chinese Fir after being heat treated at 170°C treated which were exposed to brown-rot fungus could reach I yet, After being heat treated at 210°C for 3 hours , the Chinese fir samples had no measurable weight loss when exposed to the write-rot fungus.(2) There was no remarkable influence on both Chinese Fir and Pine by heat treatment time.(3) The moisture content of Chinese Fir and Pine were lower than the moisture content that the rot fungus need, macromolecule chains such as cellulose and hemicellulose broke down, their contents decreased, and the hemicellulose decomposed into acetic acid, they prevented the growth of rot fungus.

scholarly journals DECAY RESISTANCE, DIMENSIONAL STABILITY AND MECHANICAL STRENGTH OF POPLAR WOOD MODIFIED WITH PLANT-DERIVED COMPOUNDS

Wood Research ◽  
2021 ◽  
Vol 66 (4) ◽  
pp. 556-568
Author(s):  
JIAPENG WANG ◽  
ZHENJU BI ◽  
ZHANGJING CHEN ◽  
LI YAN ◽  
YAFANG LEI
Keyword(s):  
Mechanical Properties ◽  
Citric Acid ◽  
Dimensional Stability ◽  
Color Change ◽  
White Rot Fungi ◽  
Brown Rot ◽  
Decay Resistance ◽  
White Rot ◽  
Modulus Of Rupture ◽  
Weight Percentage

The cinnamaldehyde, salicylic acid, stearolic acid and citric acid were plant-derived organic compounds that can be activated to fungi, that could degrade the wood in long term. The compounds with concentrations of 3%, 5% and 7% assisted by different dispersants were impregnated into poplar (Populus nigra L.) specimens by the vacuum-pressure method. After that, weight percentage gain (WPG), decay resistance against white-rot fungi (Trametes versicolor) and brown-rot fungi (Gloeophyllum trabeum), color change, dimensional stability and mechanical properties including modulus of elasticity (MOE) and modulus of rupture (MOR) were measured. The results indicated that cinnamaldehyde impregnated poplar showed antifungi activity against both G. trabeumand T. versicolor, and citric acid impregnated poplar showed antifungi activity against G. trabeum. The color of poplar specimens before and after impregnated cinnamaldehyde and citric acid had a little change, dimensional stability had been improved and mechanical properties especially for MOR increased significantly.

scholarly journals Cell Wall Bulking by Maleic Anhydride for Wood Durability Improvement

Forests ◽  
2020 ◽  
Vol 11 (4) ◽  
pp. 367 ◽  
Author(s):  
Mingming He ◽  
Dandan Xu ◽  
Changgui Li ◽  
Yuzhen Ma ◽  
Xiaohan Dai ◽  
...  
Keyword(s):  
Cell Wall ◽  
Maleic Anhydride ◽  
Wood Cell Wall ◽  
Brown Rot ◽  
Decay Resistance ◽  
White Rot ◽  
White Rot Fungus ◽  
Hydroxyl Group ◽  
Hydroxyl Groups ◽  
Decay Fungi

Wood is susceptible to swelling deformation and decay fungi due to moisture adsorption that originates from the dynamic nanopores of the cell wall and the abundant hydroxyl groups in wood components. This study employed as a modifier maleic anhydride (MAn), with the help of acetone as solvent, to diffuse into the wood cell wall, bulk nanopores, and further chemically bond to the hydroxyl groups of wood components, reducing the numbers of free hydroxyl groups and weakening the diffusion of water molecules into the wood cell wall. The derived MAn-bulked wood, compared to the control wood, presented a reduction in water absorptivity (RWA) of ~23% as well as an anti-swelling efficiency (ASE) of ~39% after immersion in water for 228 h, and showed an improvement in decay resistance of 81.42% against white-rot fungus and 69.79% against brown-rot fungus, respectively. The method of combined cell wall bulking and hydroxyl group bonding could effectively improve the dimensional stability and decay resistance with lower doses of modifier, providing a new strategy for wood durability improvement.

Growth behavior of wood-destroying fungi in chemically modified wood: wood degradation and translocation of nitrogen compounds

Holzforschung ◽  
2021 ◽  
Vol 0 (0) ◽  
Author(s):  
Lukas Emmerich ◽  
Maja Bleckmann ◽  
Sarah Strohbusch ◽  
Christian Brischke ◽  
Susanne Bollmus ◽  
...  
Keyword(s):  
Protective Action ◽  
Treated Wood ◽  
Untreated Wood ◽  
Brown Rot ◽  
Decay Resistance ◽  
White Rot ◽  
Decay Fungi ◽  
Chemically Modified ◽  
Decay Tests ◽  
Modified Wood

Abstract Chemical wood modification has been used to modify wood and improve its decay resistance. However, the mode of protective action is still not fully understood. Occasionally, outdoor products made from chemically modified timber (CMT) show internal decay while their outer shell remains intact. Hence, it was hypothesized that wood decay fungi may grow through CMT without losing their capability to degrade non-modified wood. This study aimed at developing a laboratory test set-up to investigate (1) whether decay fungi grow through CMT and (2) retain their ability to degrade non-modified wood. Acetylated and 1,3-dimethylol-4,5-dihydroxyethyleneurea (DMDHEU) treated wood were used in decay tests with modified ‘mantle specimens’ and untreated ‘core dowels’. It became evident that white rot (Trametes versicolor), brown rot (Coniophora puteana) and soft rot fungi can grow through CMT without losing their ability to degrade untreated wood. Consequently, full volume impregnation of wood with the modifying agent is required to achieve complete protection of wooden products. In decay tests with DMDHEU treated specimens, significant amounts of apparently non-fixated DMDHEU were translocated from modified mantle specimens to untreated wood cores. A diffusion-driven transport of nitrogen and DMDHEU seemed to be responsible for mass translocation during decay testing.

scholarly journals Comparison of the Decay Behavior of Two White-Rot Fungi in Relation to Wood Type and Exposure Conditions

2020 ◽  
Vol 8 (12) ◽  
pp. 1931
Author(s):  
Ehsan Bari ◽  
Geoffrey Daniel ◽  
Nural Yilgor ◽  
Jong Sik Kim ◽  
Mohammad Ali Tajick-Ghanbary ◽  
...  
Keyword(s):  
Cell Wall ◽  
Moisture Content ◽  
Wood Species ◽  
White Rot Fungi ◽  
White Rot ◽  
High Mass ◽  
Type I ◽  
Oak Wood ◽  
Mass Losses ◽  
Decay Behavior

Fungal wood decay strategies are influenced by several factors, such as wood species, moisture content, and temperature. This study aims to evaluate wood degradation characteristics of spruce, beech, and oak after exposure to the white-rot fungi Pleurotusostreatus and Trametesversicolor. Both fungi caused high mass losses in beech wood, while spruce and oak wood were more resistant to decay. The moisture content values of the decayed wood correlated with the mass losses for all three wood species and incubation periods. Combined microscopic and chemical studies indicated that the two fungi differed in their decay behavior. While T. versicolor produced a decay pattern (cell wall erosion) typical of white-rot fungi in all wood species, P. ostreatus caused cell wall erosion in spruce and beech and soft-rot type I (cavity formation) decay in oak wood. These observations suggest that P. ostreatus may have the capacity to produce a wider range of enzymes/radicals triggered by the chemical composition of wood cell walls and/or local compositional variability within the cell wall.

Thermal Stability and Decay Resistance Properties of Tropical Wood Polymer Nanocomposites (WPNC)

2013 ◽  
Vol 667 ◽  
pp. 482-489 ◽  
Author(s):  
Md. Saiful Islam ◽  
Sinin Hamdan ◽  
Mohamad Rusop ◽  
Md. Rezaur Rahman
Keyword(s):  
Thermal Stability ◽  
Polymer Nanocomposites ◽  
Phenol Formaldehyde ◽  
Brown Rot ◽  
Decay Resistance ◽  
White Rot ◽  
Postia Placenta ◽  
Tropical Wood ◽  
Wood Polymer ◽  
The Fourier Transform

The effects of nanoclay on the thermal stability and decay resistance properties of tropical wood polymer nanocomposites (WPNCs) were investigated in this work. WPNC were prepared from several selected tropical wood species by impregnating the selected woods with a combination of nanoclay and phenol formaldehyde (PF) prepolymer mixture. The formation of WPNC was confirmed by the fourier transform infrared spectroscopy (FTIR) analysis. Thermal property of manufactured WPNC in terms of thermogravimetric analysis (TGA) was evaluated, and an improvement in thermal stability was found for fabricated WPNC. The wood was then exposed to two types of fungi; white-rot (polyporous versicolor) and brown-rot (postia placenta), for 12 weeks. Decay was assessed through percentage (%) of weight loss. A significant improvement was found in the treated woods compared to the untreated ones. In addition, the fabricated WPNC showed lower moisture content compared with raw one.

scholarly journals Resistance of thermally modified and pressurized hot water extracted Scots pine sapwood against decay by the brown-rot fungus Rhodonia placenta

2019 ◽  
Vol 78 (1) ◽  
pp. 161-171 ◽  
Author(s):  
Michael Altgen ◽  
Suvi Kyyrö ◽  
Olli Paajanen ◽  
Lauri Rautkari
Keyword(s):  
Cell Wall ◽  
Mass Loss ◽  
Scots Pine ◽  
Elevated Temperatures ◽  
Brown Rot ◽  
Decay Resistance ◽  
Hot Water ◽  
Decay Fungi ◽  
Effective Reduction ◽  
Cell Wall Porosity

AbstractThe thermal degradation of wood is affected by a number of process parameters, which may also cause variations in the resistance against decay fungi. This study compares changes in the chemical composition, water-related properties and decay resistance of Scots pine sapwood that was either thermally modified (TM) in dry state at elevated temperatures (≥ 185 °C) or treated in pressurized hot water at mild temperatures (≤ 170 °C). The thermal decomposition of easily degradable hemicelluloses reduced the mass loss caused by Rhodonia placenta, and it was suggested that the cumulative mass loss is a better indicator of an actual decay inhibition. Pressurized hot water extraction (HWE) did not improve the decay resistance to the same extent as TM, which was assigned to differences in the wood-water interactions. Cross-linking reactions during TM caused a swelling restraint and an effective reduction in moisture content. This decreased the water-swollen cell wall porosity, which presumably hindered the transport of degradation agents through the cell wall and/or reduced the accessibility of wood constituents for degradation agents. This effect was absent in hot water-extracted wood and strong decay occurred even when most hemicelluloses were already removed during HWE.

Efficacy of Pinosylvins against White-Rot and Brown-Rot Fungi

Holzforschung ◽  
1999 ◽  
Vol 53 (5) ◽  
pp. 491-497 ◽  
Author(s):  
Catherine C. Celimene ◽  
Jessie A. Micales ◽  
Leslie Ferge ◽  
Raymond A. Young
Keyword(s):  
Picea Glauca ◽  
Pinus Banksiana ◽  
White Rot Fungi ◽  
Brown Rot ◽  
Monomethyl Ether ◽  
Decay Resistance ◽  
White Rot ◽  
Red Maple ◽  
Brown Rot Fungi ◽  
Agar Media

Summary Three stilbenes, pinosylvin (PS), pinosylvin monomethyl ether (PSM) and pinosylvin dimethyl ether (PSD), were extracted from white spruce (Picea glauca), jack pine (Pinus banksiana), and red pine (Pinus resinosa) pine cones, and their structures were confirmed by spectroscopic and chromatographic (HPLC, GC/MS, NMR and FTIR) analysis. PS, PSM, PSD or a 1:1:1 mixture of these stilbenes at concentrations of 0.1 % and 1.0 % were examined for their fungal inhibitory activity by two bioassay methods. Growth of white-rot fungi (Trametes versicolor and Phanerochaete chrysosporium), and brown-rot fungi (Neolentinus lepideus, Gloeophyllum trabeum and Postia placenta) on agar media in the presence of each of the stilbenes or a 1:1:1 mixture inhibited growth of white-rot fungi, but slightly stimulated growth of brown-rot fungi. Soil-block assays, conditions more representative of those found in nature, did not correlate with those from the screening on agar media. PS, PSM, PSD or a 1:1:1 mixture of the three compounds at concentrations of 0.1 % and 1.0 % did not impart any significant decay resistance to white-rot fungi inoculated on a hardwood (Red maple). However under the same conditions, decay resistance was observed against brown-rot fungi on a softwood (Southern yellow pine). It appears that stilbenes at least partially contribute to wood decay resistance against brown-rot fungi.

Decay resistance of softwoods and hardwoods thermally modified by the Thermovouto type thermo-vacuum process to brown rot and white rot fungi

Holzforschung ◽  
2016 ◽  
Vol 70 (9) ◽  
pp. 877-884 ◽  
Author(s):  
Jie Gao ◽  
Jong Sik Kim ◽  
Nasko Terziev ◽  
Geoffrey Daniel
Keyword(s):  
White Rot Fungi ◽  
Brown Rot ◽  
Decay Resistance ◽  
Fungal Species ◽  
White Rot ◽  
Agar Block ◽  
Pycnoporus Sanguineus ◽  
Postia Placenta ◽  
Soil Block ◽  
Class 1

Abstract Softwoods (SW, spruce and fir) and hardwoods (HW, ash and beech) were thermally modified by the thermo-vacuum (Termovuoto) process for 3–4 h in the temperature range 160–220°C (TMW160–220°C) and their fungal durability were examined in soil-block tests with two brown rot (BR, Postia placenta, Gloeophyllum trabeum) and two white rot (WR, Pycnoporus sanguineus, Phlebia radiata) fungi. SW-TMW160–220°C were exposed to P. placenta and P. sanguineus and HW-TMW190–220°C to all fungal species. Considerable improvement (durability class 1–3) in decay resistance was only achieved for SW- and HW-TMW220°C. Thermal modification (TM) below 200°C influenced decay resistance negatively in case of some fungal species applied for both SW and HW. Judged by the durability class, decay resistance was higher in HW- than in SW-TMW at high TM temperature. Behavior of TM differed significantly between ash (ring-porous HW) and beech (diffuse-porous HW). A comparison between results of soil- and agar-block tests on Termovouoto wood demonstrated that the influence of testing method in terms of assignment to durability classes is not significant.

scholarly journals Mode of action of brown rot decay resistance in modified wood: a review

Holzforschung ◽  
2014 ◽  
Vol 68 (2) ◽  
pp. 239-246 ◽  
Author(s):  
Rebecka Ringman ◽  
Annica Pilgård ◽  
Christian Brischke ◽  
Klaus Richter
Keyword(s):  
Cell Wall ◽  
Mode Of Action ◽  
Wood Decay ◽  
Brown Rot ◽  
Decay Resistance ◽  
Hydroxyl Groups ◽  
Decay Fungi ◽  
Brown Rot Decay ◽  
Thermally Modified Wood ◽  
Modified Wood

Abstract Chemically or physically modified wood materials have enhanced resistance to wood decay fungi. In contrast to treatments with traditional wood preservatives, where the resistance is caused mainly by the toxicity of the chemicals added, little is known about the mode of action of nontoxic wood modification methods. This study reviews established theories related to resistance in acetylated, furfurylated, dimethylol dihydroxyethyleneurea-treated, and thermally modified wood. The main conclusion is that only one theory provides a consistent explanation for the initial inhibition of brown rot degradation in modified wood, that is, moisture exclusion via the reduction of cell wall voids. Other proposed mechanisms, such as enzyme nonrecognition, micropore blocking, and reducing the number of free hydroxyl groups, may reduce the degradation rate when cell wall water uptake is no longer impeded.

Sign in / Sign up

Export Citation Format

Share Document