Mechanical properties of steel fiber reinforced concrete material in construction of road bridge deck

2021 ◽  
Vol 16 (4) ◽  
pp. 169-176
Author(s):  
Xiaohu Luo
Keyword(s):  
Mechanical Properties ◽  
Compressive Strength ◽  
Reinforced Concrete ◽  
Flexural Strength ◽  
Steel Fiber ◽  
Fiber Content ◽  
Fiber Reinforced Concrete ◽  
Fiber Reinforced ◽  
Steel Fiber Reinforced Concrete ◽  
Bridge Construction

In order to improve the application effect of steel fiber reinforced concrete (SFRC) in road bridge construction, the mechanical properties of SFRC with different fiber content were analyzed. The SFRC specimens with 0%, 0.5%, 1%, 1.5% and 2% fiber content were designed, and the mechanical properties were tested. The results showed that the compressive strength first increased and then decreased with the increase of fiber content, and the maximum compressive strength of SFRC1.5 reached 40.86 MPa, increasing by 7.19%; the increase amplitude of tensile strength of SFRC1.5 was 73.04%, which was the most obvious; the flexural strength of SFRC increased with the increase of fiber content, and the flexural strength of SFRC2 was 9.78 MPa, increasing by 94.43%. It is concluded from the experimental results of a case study that SFRC1.5 presents the optimal overall mechanical properties and is more suitable for road bridge construction.

scholarly journals Optimization of the Fine to Coarse Aggregate Ratio for the Workability and Mechanical Properties of High Strength Steel Fiber Reinforced Concretes

Materials ◽  
2020 ◽  
Vol 13 (22) ◽  
pp. 5202
Author(s):  
Mohammad Iqbal Khan ◽  
Wasim Abbass ◽  
Mohammad Alrubaidi ◽  
Fahad K. Alqahtani
Keyword(s):  
Mechanical Properties ◽  
Reinforced Concrete ◽  
Flexural Strength ◽  
Coarse Aggregate ◽  
Steel Fiber ◽  
High Strength ◽  
Fiber Reinforced Concrete ◽  
Fiber Reinforced ◽  
Steel Fiber Reinforced Concrete ◽  
Fresh State

High-strength concrete is used to provide quality control for concrete structures, yet it has the drawback of brittleness. The inclusion of fibers improves the ductility of concrete but negatively affects the fresh properties of fiber-reinforced concrete. The effects of different fine to coarse aggregate ratios on the fresh and hardened properties of steel fiber reinforced concrete were investigated in this study. Mixtures were prepared with various fine to coarse aggregate (FA/CA) ratios incorporating 1% steel fiber content (by volume) at constant water to cement ratio. The workability, unit weight, and temperature of the concrete in the fresh state, and the mechanical properties of steel-fiber-reinforced concrete (SFRC) were investigated. The inclusion of fiber in concrete influenced the mobility of concrete in the fresh state by acting as a barrier to the movement of coarse aggregate. It was observed that the concrete with an FA/CA ratio above 0.8 showed better flowability in the fresh state, whilst an above 0.9 FA/CA ratio requires excessive superplasticizer to maintain the flowability of the mixtures. The compressive and flexural strength of SFRC increased with an increase in the FA/CA ratio by around 10% and 28%, respectively. Experimental values of compressive strength and flexural strength showed good agreement, however, modulus of elasticity demonstrated slightly higher values. The experimentally obtained measurements of the mechanical properties of SFRC conformed reasonably well with the available existing prediction equations, and further enabled establishing predictive isoresponse interactive equations within the scope of the investigation domain.

Mechanical Properties of Hybrid Nylon-Steel- and Steel-Fibre-Reinforced High Strength Concrete at Low Fibre Volume Fraction

2010 ◽  
Vol 168-170 ◽  
pp. 1704-1707 ◽  
Author(s):  
Ming Kun Yew ◽  
Othman Ismail
Keyword(s):  
Mechanical Properties ◽  
Compressive Strength ◽  
Reinforced Concrete ◽  
High Strength Concrete ◽  
Steel Fiber ◽  
Volume Fraction ◽  
High Strength ◽  
Fiber Reinforced Concrete ◽  
Fiber Reinforced ◽  
Steel Fiber Reinforced Concrete

The mechanical properties of hybrid nylon-steel-fiber-reinforced concrete were investigated in comparison to that of the steel-fiber-reinforced concrete, at the same volume fraction (0.5%). The combining of fibers, often called hybridization is investigated in this paper for a very high strength concrete of an average compressive strength of 105 MPa. Test results showed that fibers when used in a hybrid nylon-steel fibers reinforced concrete form could result in superior composite performance compared to steel-fiber-reinforced concrete. The basic property of the hybridized material that was evaluated and analyzed extensively was the modulus of rupture (MOR) and splitting tensile while the compressive strength was only slightly decreased compared to single steel fiber reinforced concrete. There is a synergy effect in the hybrid fibers system.

scholarly journals Prediction of Fiber Reinforced Concrete Strength Properties by Micromechanics Method

2019 ◽  
Vol 5 (1) ◽  
pp. 200 ◽  
Author(s):  
Shriganesh Shantikumar Kadam ◽  
V. V. Karjinni ◽  
C. S. Jarali
Keyword(s):  
Compressive Strength ◽  
Reinforced Concrete ◽  
Flexural Strength ◽  
Steel Fiber ◽  
Testing Machine ◽  
Strength Properties ◽  
Strength Test ◽  
Fiber Reinforced Concrete ◽  
Fiber Reinforced ◽  
Steel Fiber Reinforced Concrete

High strength steel fiber reinforced concrete (HSSFRC) was prepared with the help of steel fiber. 0.5%, 1.0%, and 1.5% steel fiber by volume of concrete specimen was used in concrete for present investigation. Compressive strength test and flexural strength test were conducted on cubical and prismatic specimens respectively.The main objective of the research work is to validate the experimental out comes by a numerical technique such as micromechanics approach. A high strength steel fiber reinforced concrete whose compressive strength is greater than 60 N/mm2 was prepared and tested on concrete testing machine. Flexural strength test was conducted on universal testing machine to evaluate the bending properties of concrete. It was observed that with increase in the percentage of steel fiber volume the compressive strength and flexural strength also increases. However the workability of concrete declines and concrete is no longer in working condition. Micromechanics technique helps to predict the strength properties which save time required for casting and such technique was found to be beneficial.

scholarly journals Evaluation of Fiber Type and Water-Binder Ratio Influence on Concrete Properties

2019 ◽  
Vol 9 (1) ◽  
pp. 6444-6450
Keyword(s):  
Compressive Strength ◽  
Reinforced Concrete ◽  
Flexural Strength ◽  
Steel Fiber ◽  
Fiber Type ◽  
Linear Regression Analysis ◽  
Polypropylene Fiber ◽  
Fiber Reinforced Concrete ◽  
Fiber Reinforced ◽  
Steel Fiber Reinforced Concrete

This paper enumerates the experimental study on workability and strength properties of concrete containing different dosage of polypropylene fiber from 0.1% to 0.6% and 1.0% to 3.5% of steel fiber. Water - binder ratio, fiber type and fiber dosage influence on flow behaviour, compressive strength, flexural strength and brittleness ratio were analysed. Experimental results were substantiated by linear regression analysis considering 95% confidence level. Reference mixes with 0.34 and 0.36 water- binder were prepared for results comparison with polypropylene and steel fiber reinforced concretes. Test results showed comparatively higher workability reduction in polypropylene fiber reinforced concrete. Compressive strength test results of fiber reinforced concrete indicted an optimum fiber content of 0.30% of polypropylene fiber and 2.50% of steel fiber. Steel fiber reinforced concrete displayed continuous increase in flexural strength with 44.46% average increase. Brittleness ratio, which was the ratio of flexural strength and compressive strength showed maximum value of 0.24 for concrete with 3.5 % steel fiber and 0.36 w/B ratio. Linear regression analysis revealed good correlation of flow properties with w/B ratio irrespective of fiber type. Though the compressive strength had low correlation with fiber type and w/B ratio, steel fiber reinforced concrete indicated up to 0.987 coefficient of determination with flexural strength.

Penetration Resistance Research of Fiber Reinforced RPC

2014 ◽  
Vol 1055 ◽  
pp. 23-26
Author(s):  
Can Xu
Keyword(s):  
Reinforced Concrete ◽  
Coarse Aggregate ◽  
Steel Fiber ◽  
Penetration Resistance ◽  
Fiber Content ◽  
Fiber Reinforced Concrete ◽  
Fiber Reinforced ◽  
Quartz Powder ◽  
Steel Fiber Reinforced Concrete

In the original to remove steel and steel fiber reinforced concrete coarse aggregate in quartz powder and a small amount of activator, can boost steel fiber content, and its application in construction makes it more convenient, but how the penetration resistance works is not particularly clear. Through the penetration resistance experiment, found that when joined the SF and BF, RPC can still keep complete even after three times by penetration ,indicating the good performance of penetration resistance.

Study on Retrofitting and Strengthening of Reinforced Concrete Beams Using Fibrous Concrete

2021 ◽  
Vol 9 (8) ◽  
pp. 1676-1684
Author(s):  
Natalia Sharma
Keyword(s):  
Mechanical Properties ◽  
Reinforced Concrete ◽  
Steel Fiber ◽  
Concrete Beams ◽  
Fiber Reinforced Concrete ◽  
Steel Fibers ◽  
Reinforced Concrete Beams ◽  
Cement Matrix ◽  
Fiber Reinforced ◽  
Steel Fiber Reinforced Concrete

Abstract: Reinforced concrete structures are frequently in need of repair and strengthening as a result of numerous environmental causes, ageing, or material damage under intense stress conditions, as well as mistakes made during the construction process. RC structures are repaired using a variety of approaches nowadays. The usage of FRC is one of the retrofitting strategies. Steel fiber reinforced concrete (SFRC) was used in this investigation because it contains randomly dispersed short discrete steel fibers that operate as internal reinforcement to improve the cementitious composite's characteristics (concrete). The main rationale for integrating small discrete fibers into a cement matrix is to reduce the amount of cement used. The principal reason for incorporating short discrete fibers into a cement matrix is to reduce cracking in the elastic range, increase the tensile strength and deformation capacity and increase the toughness of the resultant composite. These properties of SFRC primarily depend upon length and volume of Steel fibers used in the concrete mixture. In India, the steel fiber reinforced concrete (SFRC) has seen limited applications in several structures due to the lack of awareness, design guidelines and construction specifications. Therefore, there is a need to develop information on the role of steel fibers in the concrete mixture. The experimental work reported in this study includes the mechanical properties of concrete at different volume fractions of steel fibers. These mechanical properties include compressive strength, split tensile strength and flexural strength and to study the effect of volume fraction and aspect ratio of steel fibers on these mechanical properties. However, main aim of the study was significance of reinforced concrete beams strengthened with fiber reinforced concrete layer and to investigate how these beams deflect under strain. The objective of the investigation was finding that applying FRC to strengthen beams enhanced structural performance in terms of ultimate load carrying capacity, fracture pattern deflection, and mode of failure or not.