scholarly journals A Study on Cement-free Geopolymer Concrete incorporated with industrial waste Cured at Open Environment for different molarities of sodium hydroxide

2021 ◽  
Keyword(s):  
Compressive Strength ◽  
Sodium Hydroxide ◽  
Ultrasonic Pulse Velocity ◽  
Strength Properties ◽  
Ultrasonic Pulse ◽  
Pulse Velocity ◽  
Cement Industry ◽  
Geopolymer Concrete ◽  
Regression Equations ◽  
Waste Products

<p>Nowadays, the increase in population and industrial growth that generates lot of waste products which creates disposal problems and severe environmental hazards. The cement industry is one of the important sectors which liberates greenhouse gas such as carbon dioxide. The consumption of waste products which eradicate the disposal issues and also it diminishes the emission of greenhouse gases to the environment. This is an important reason for the introduction of cement-free Geopolymer Concrete. This paper was invented to understand the suitability of Geopolymer Concrete cured at ambient temperature in the construction industry and the effect of molarity on strength properties. Totally, five types of Geopolymer Concrete mixes were prepared by altering the molarities of sodium hydroxide like 4M, 6M, 8M, 10M and 12M. The compressive strengths (1, 3, 7, 14 and 28 days), splitting tensile strengths (7, 14 and 28 days) and flexural strengths at 28 days were studied for aforesaid molarities. Generally, the rise in molarity increases the compressive strength. The ultimate strength was achieved up to 57.53MPa at 28 days for 8M Geopolymer Concrete. For the validation of compressive strength predicted by Destructive test (DT), the Non-Destructive tests (NDT) (Rebound Hammer and Ultrasonic pulse velocity) were carried out at resembled age of curing. Regression analysis is also done between compressive strength established by DT and NDT results. The arrived linear regression equations were well correlated with the experimental results and the co-efficient (R2) values varied from 0.8970-0.9967.</p>

scholarly journals Empirical Investigation on Compressive Strength of Geopolymer and Conventional Concretes by Nondestructive Method

2021 ◽  
Vol 2021 ◽  
pp. 1-10
Author(s):  
B. Ravali ◽  
K. Bala Gopi Krishna ◽  
D. Ravi Kanth ◽  
K. J. Brahma Chari ◽  
S. Venkatesa Prabhu ◽  
...  
Keyword(s):  
Compressive Strength ◽  
Fly Ash ◽  
Ultrasonic Pulse Velocity ◽  
Ultrasonic Pulse ◽  
Pulse Velocity ◽  
Nondestructive Method ◽  
Geopolymer Concrete ◽  
River Sand ◽  
Rebound Hammer ◽  
Compressive Strength Of Concrete

Need of construction is increasing due to increase in population growth rate. The geopolymer concrete is eco-friendly than ordinary concrete. Current experimental investigation was conducted on ordinary and geopolymer concrete using nondestructive testing (NDT) tests like ultrasonic pulse velocity (UPV) test and rebound hammer (RH) test. Cube specimens of dimensions 150 mm × 150 mm × 150 mm are used to conduct these tests at 7, 14, and 28 days. Proportions considered for concrete are cement-fly ash-river sand (100-0-100% and 60-40-100%), cement-fly ash-robo sand (100-0-100% and 60-40-100%) whereas geopolymer concrete fly ash-metakaolin is taken in proportions of 100-0%, 60-40%, and 50-50%. Alkaline activators (sodium hydroxide and sodium silicate with molarity 12M) were used in preparing geopolymer concrete. The major objective of the current study is to obtain relation between compressive strength of concrete and UPV values.

An Ultrasonic Pulse Velocity Test on Fly-Ash Based Geopolymer Concrete in Frequency Domains

2014 ◽  
Vol 700 ◽  
pp. 310-313 ◽  
Author(s):  
Jee Sang Kim ◽  
Tae Hong Kim
Keyword(s):  
Compressive Strength ◽  
Construction Material ◽  
High Strength ◽  
Ultrasonic Pulse Velocity ◽  
Peak Frequency ◽  
Ultrasonic Pulse ◽  
Pulse Velocity ◽  
P Wave ◽  
Geopolymer Concrete ◽  
Existing Structures

The Non-Destructive Test techniques on concrete, which can assess the properties of materials without damages, have been developed as the deteriorations of existing structures increase. Among them, the ultrasonic pulse velocity (USPV) method is widely used because it can investigate the states of one material for a long time and repeatedly. However, there have been few researches on the NDT application to geopolymer concrete which is environment friendly construction material without any cement. This paper investigates the variations of ultrasonic pulse velocity and peak frequency of geopolymer concrete under monotonically increasing loads to assess the material conditions with various compressive strength levels by measuring P-wave signals. The pulse velocities and peak frequencies were higher in high strength geopolymer concrete specimens. There are not explicit relations between strength levels and peak frequencies but the peak frequencies are strongly influenced by the applied stress levels. In addition, a predicting equation for compressive strength of geopolymer concrete is derived based on experimental data in similar form for normal concrete.

scholarly journals Performance of Fly Ash Geopolymer Concrete Incorporating Bamboo Ash at Elevated Temperature

Materials ◽  
2019 ◽  
Vol 12 (20) ◽  
pp. 3404 ◽  
Author(s):  
Ishak ◽  
Lee ◽  
Singh ◽  
Ariffin ◽  
Lim ◽  
...  
Keyword(s):  
Compressive Strength ◽  
Fly Ash ◽  
Control Sample ◽  
Ultrasonic Pulse Velocity ◽  
Ultrasonic Pulse ◽  
Pulse Velocity ◽  
Air Cooling ◽  
Geopolymer Concrete ◽  
Water Cooling ◽  
Control Samples

This paper presents the experimental results on the behavior of fly ash geopolymer concrete incorporating bamboo ash on the desired temperature (200 °C to 800 °C). Different amounts of bamboo ash were investigated and fly ash geopolymer concrete was considered as the control sample. The geopolymer was synthesized with sodium hydroxide and sodium silicate solutions. Ultrasonic pulse velocity, weight loss, and residual compressive strength were determined, and all samples were tested with two different cooling approaches i.e., an air-cooling (AC) and water-cooling (WC) regime. Results from these tests show that with the addition of 5% bamboo ash in fly ash, geopolymer exhibited a 5 MPa (53%) and 5.65 MPa (66%) improvement in residual strength, as well as 940 m/s (76%) and 727 m/s (53%) greater ultrasonic pulse velocity in AC and WC, respectively, at 800 °C when compared with control samples. Thus, bamboo ash can be one of the alternatives to geopolymer concrete when it faces exposure to high temperatures.

PENGKAJIAN KEKUATAN BETON STRUKTUR JEMBATAN PASCA KEBAKARAN

2013 ◽  
Vol 12 (3) ◽  
Author(s):  
Sudarmadi Sudarmadi
Keyword(s):  
Compressive Strength ◽  
Concrete Strength ◽  
Ultrasonic Pulse Velocity ◽  
Ultrasonic Pulse ◽  
Pulse Velocity ◽  
Test Results ◽  
Concrete Compressive Strength ◽  
Strength Assessment ◽  
Concrete Testing

In this paper a case study about concrete strength assessment of bridge structure experiencing fire is discussed. Assessment methods include activities of visual inspection, concrete testing by Hammer Test, Ultrasonic Pulse Velocity Test, and Core Test. Then, test results are compared with the requirement of RSNI T-12-2004. Test results show that surface concrete at the location of fire deteriorates so that its quality is decreased into the category of Very Poor with ultrasonic pulse velocity ranges between 1,14 – 1,74 km/s. From test results also it can be known that concrete compressive strength of inner part of bridge pier ranges about 267 – 274 kg/cm2 and concrete compressive strength of beam and plate experiencing fire directly is about 173 kg/cm2 and 159 kg/cm2. It can be concluded that surface concrete strength at the location of fire does not meet the requirement of RSNI T-12-2004. So, repair on surface concrete of pier, beam, and plate at the location of fire is required.

scholarly journals The Hydration, Mechanical, Autogenous Shrinkage, Durability, and Sustainability Properties of Cement–Limestone–Slag Ternary Composites

2021 ◽  
Vol 13 (4) ◽  
pp. 1881
Author(s):  
Mei-Yu Xuan ◽  
Yi Han ◽  
Xiao-Yong Wang
Keyword(s):  
Compressive Strength ◽  
Electrical Resistivity ◽  
Experimental Studies ◽  
Autogenous Shrinkage ◽  
Ultrasonic Pulse Velocity ◽  
Ultrasonic Pulse ◽  
Pulse Velocity ◽  
Hydration Heat ◽  
Granulated Blast Furnace Slag ◽  
Binder Ratio

This study examines the hydration–mechanical–autogenous shrinkage–durability–sustainability properties of ternary composites with limestone filler (LF) and ground-granulated blast furnace slag (BFS). Four mixtures were prepared with a water/binder ratio of 0.3 and different replacement ratios varying from 0 to 45%. Multiple experimental studies were performed at various ages. The experimental results are summarized as follows: (1) As the replacement levels increased, compressive strength and autogenous shrinkage (AS) decreased, and this relationship was linear. (2) As the replacement levels increased, cumulative hydration heat decreased. At the age of 3 and 7 days, there was a linear relationship between compressive strength and cumulative hydration heat. (3) Out of all mixtures, the ultrasonic pulse velocity (UPV) and electrical resistivity exhibited a rapid increase in the early stages and tended to slow down in the latter stages. There was a crossover of UPV among various specimens. In the later stages, the electrical resistivity of ternary composite specimens was higher than plain specimens. (4) X-ray diffraction (XRD) results showed that LF and BFS have a synergistic effect. (5) With increasing replacement ratios, the CO2 emissions per unit strength reduced, indicating the sustainability of ternary composites.

Estimation of Compressive Strength of Recycled Aggregate High Strength Concrete Using Ultrasonic Pulse Velocity

2014 ◽  
Vol 605 ◽  
pp. 147-150
Author(s):  
Seong Uk Hong ◽  
Seung Hun Kim ◽  
Yong Taeg Lee
Keyword(s):  
Compressive Strength ◽  
High Strength Concrete ◽  
Coarse Aggregate ◽  
High Strength ◽  
Ultrasonic Pulse Velocity ◽  
Ultrasonic Pulse ◽  
Pulse Velocity ◽  
Recycled Aggregate ◽  
Strength Concrete ◽  
Recycled Coarse Aggregate

This study used the ultrasonic pulse velocity method, one of the non-destructive test methods that does not damage the building for maintenance of to-be-constructed concrete structures using recycled aggregates in order to estimate the compressive strength of high strength concrete structure using recycled coarse aggregate and provide elementary resources for technological establishment of ultrasonic pulse velocity method. 200 test pieces of high strength concrete 40, 50MPa using recycled coarse aggregate were manufactured by replacement rates (0, 30, 50, 100%) and age (1, 7, 28, 180days), and air curing was executed to measure compressive strength and wave velocity. As the result of compressive strength measurement, the one with age of 180day and design strength of 40MPa was 43.69MPa, recycled coarse aggregate replacement rate of 30% 50% 100% were 42.82, 41.22, 37.35MPa, and 50MPa was 52.50MPa, recycled coarse aggregate replacement rate of 30% 50% 100% were 49.02, 46.66, 45.30MPa, and while it could be seen that the test piece substituted with recycled aggregate was found to have lower strength than the test piece with natural aggregate only, but it still reached the design strength to a degree. The correlation of compressive strength and ultrasonic pulse velocity was found and regression analysis was conducted. The estimation formula for compressive strength of high strength concrete using recycled coarse aggregate was found to be Fc=0.069Vp4.05, R2=0.66

Sign in / Sign up

Export Citation Format

Share Document