Analytical High-Resolution TEM Study on Au/TiO2 Catalysts

1999 ◽  
Vol 589 ◽  
Author(s):  
T. Akita ◽  
K. Tanaka ◽  
S. Tsubota ◽  
M. Haruta
Keyword(s):  
Electron Microscope ◽  
High Resolution ◽  
Transmission Electron Microscope ◽  
Scanning Transmission Electron Microscope ◽  
Dark Field ◽  
Transmission Electron ◽  
Scanning Transmission ◽  
Annular Dark Field ◽  
High Resolution Tem ◽  
Electron Energy Loss

AbstractHRTEM(High-Resolution Transmission Electron Microscope), HAADF-STEM (High Angle Annular Dark Field Scanning Transmission Electron Microscope) and EELS(Electron Energy Loss Spectroscopy) techniques were applied for the characterization of Au/TiO2 catalysts. HAADFSTEM provides precise size distributions for Au particles smaller than ∼2nm in diameter. It was observed that many small particles under 2nm were supported on anatase TiO2 having a large surface area. The HAADF-STEM method was examined as a way to measure the shape of Au particles. EELS measurements were also used to examine the interface between Au and TiO2 support to study electronic structure effects.

Multislice Simulation of Adf Stem Images

1987 ◽  
Vol 45 ◽  
pp. 188-191
Author(s):  
E. J. Kirkland ◽  
R. F. Loane ◽  
J. Silcox
Keyword(s):  
Electron Microscope ◽  
Transmission Electron Microscope ◽  
Scattering Amplitude ◽  
Signal To Noise Ratio ◽  
Scanning Transmission Electron Microscope ◽  
Dark Field ◽  
Heavy Atoms ◽  
Transmission Electron ◽  
Scanning Transmission ◽  
Annular Dark Field

The multislice method (e.g. Goodman and Moodie) of simulating bright field conventional transmission electron microscope (BF-CTEM) images of crystalline specimens can be extended to simulation of scanning transmission electron microscope (STEM) images of similar specimens in the annular dark field (ADF) mode. According to the reciprocity theorem (Pogany and Turner and Cowley) BF-CTEM would be equivalent to BF STEM with a point detector. Such a detector (STEM) however would yield an exceedingly small signal to noise ratio. Thus, STEM has found more use in the ADF mode (e.g. Crewe et al.) exploiting the large contrast arising from heavy atoms. In BF imaging (CTEM and STEM) the constrast is roughly proportional to the scattering amplitude f α Z3/4 whereas in DF (CTEM and STEM) imaging it is roughly proportional to the scattering cross σ α Z3/2 where Z is atomic number, a form that is advantageous foatom discrimination.

ADF-STEM Imaging of Strained GaN0.045As0.955 Epitaxial Layers on (100) GaAs Substrates

2006 ◽  
Vol 982 ◽  
Author(s):  
X. Wu ◽  
M.D. Robertson ◽  
J.A. Gupta ◽  
J.-M. Baribeau ◽  
J.C. Bennett ◽  
...  
Keyword(s):  
Electron Microscope ◽  
Transmission Electron Microscope ◽  
Gaas Substrate ◽  
Misfit Strain ◽  
Scanning Transmission Electron Microscope ◽  
Dark Field ◽  
Gaas Substrates ◽  
Transmission Electron ◽  
Scanning Transmission ◽  
Annular Dark Field

ABSTRACTThe annular dark field (ADF) image contrast of a 0.92% tensile strained GaN0.045As0.955 layer on GaAs substrate was studied with a scanning transmission electron microscope (STEM) as a function of ADF detector inner semi-angles ranging from 28 mrad to 90 mrad. The GaN0.045As0.955 layers were brighter than the surrounding GaAs for the values of ADF detector semiangle up to 65 mrad, and the measured contrast decreased with increasing ADF detector inner semi-angle. For a 37 nm thick specimen, the GaN0.045As0.955 intensity is about 13% higher than that of GaAs in the 28 mrad ADF detector inner semi-angle. Multislice simulations show that the displacement around substitutional N atoms plays an important role in the observed ADF-STEM contrast, while the contribution to the contrast due to misfit strain between GaN0.045As0.955 and GaAs is small.

Resolution in the Scanning Transmission Electron Microscope

1972 ◽  
Vol 30 ◽  
pp. 454-455
Author(s):  
M. G. R. Thomson
Keyword(s):  
Electron Microscope ◽  
Transmission Electron Microscope ◽  
Spherical Aberration ◽  
Signal To Noise Ratio ◽  
Scanning Transmission Electron Microscope ◽  
Dark Field ◽  
Objective Lens ◽  
Scanning Transmission Electron ◽  
Transmission Electron ◽  
Scanning Transmission

The variation of contrast and signal to noise ratio with change in detector solid angle in the high resolution scanning transmission electron microscope was discussed in an earlier paper. In that paper the conclusions were that the most favourable conditions for the imaging of isolated single heavy atoms were, using the notation in figure 1, either bright field phase contrast with β0⋍0.5 α0, or dark field with an annular detector subtending an angle between ao and effectively π/2.The microscope is represented simply by the model illustrated in figure 1, and the objective lens is characterised by its coefficient of spherical aberration Cs. All the results for the Scanning Transmission Electron Microscope (STEM) may with care be applied to the Conventional Electron Microscope (CEM). The object atom is represented as detailed in reference 2, except that ϕ(θ) is taken to be the constant ϕ(0) to simplify the integration. This is reasonable for θ ≤ 0.1 θ0, where 60 is the screening angle.

Design of a new objective lens for an HB-501A STEM

1991 ◽  
Vol 49 ◽  
pp. 416-417
Author(s):  
Earl J. Kirkland ◽  
Robert J. Keyse
Keyword(s):  
High Resolution ◽  
Spherical Aberration ◽  
Scanning Transmission Electron Microscope ◽  
Dark Field ◽  
Objective Lens ◽  
Specimen Holder ◽  
Transmission Electron ◽  
Scanning Transmission ◽  
Annular Dark Field ◽  
High Resolution Microscopy

An ultra-high resolution pole piece with a coefficient of spherical aberration Cs=0.7mm. was previously designed for a Vacuum Generators HB-501A Scanning Transmission Electron Microscope (STEM). This lens was used to produce bright field (BF) and annular dark field (ADF) images of (111) silicon with a lattice spacing of 1.92 Å. In this microscope the specimen must be loaded into the lens through the top bore (or exit bore, electrons traveling from the bottom to the top). Thus the top bore must be rather large to accommodate the specimen holder. Unfortunately, a large bore is not ideal for producing low aberrations. The old lens was thus highly asymmetrical, with an upper bore of 8.0mm. Even with this large upper bore it has not been possible to produce a tilting stage, which hampers high resolution microscopy.

scholarly journals Characteristics of multiwalled carbon nanotubes-rhenium nanocomposites with varied rhenium mass fractions

2017 ◽  
Vol 7 ◽  
pp. 184798041770717 ◽  
Author(s):  
Anna D Dobrzańska-Danikiewicz ◽  
Weronika Wolany ◽  
Dariusz Łukowiec ◽  
Karolina Jurkiewicz ◽  
Paweł Niedziałkowski
Keyword(s):  
Carbon Nanotubes ◽  
Electron Microscope ◽  
Multiwalled Carbon Nanotubes ◽  
Transmission Electron Microscope ◽  
Scanning Transmission Electron Microscope ◽  
Dark Field ◽  
Multiwalled Carbon ◽  
Weight Percentage ◽  
Transmission Electron ◽  
Scanning Transmission

The purpose of the article is to discuss the process of oxidation of carbon nanotubes subsequently subjected to the process of decoration with rhenium nanoparticles. The influence of functionalization in an oxidizing medium is presented and the results of investigations using Raman spectroscopy and infrared spectroscopy are discussed. Multiwalled carbon nanotubes rhenium-type nanocomposites with the weight percentage of 10%, 20% and 30% of rhenium are also presented in the article. The structural components of such nanocomposites are carbon nanotubes decorated with rhenium nanoparticles. Microscopic examinations under transmission electron microscope and scanning transmission electron microscope using the bright and dark field confirm that nanocomposites containing about 20% of rhenium have the most homogenous structure.

Sign in / Sign up

Export Citation Format

Share Document