Why is the Japanese Sword Curved ?

1990 ◽  
Vol 185 ◽  
Author(s):  
William N. Weins ◽  
Peter Bleed
Keyword(s):  
Residual Stresses ◽  
Cutting Edge ◽  
16Th Century ◽  
Strain Gages ◽  
Structure Property ◽  
Volumetric Expansion ◽  
Structure Property Relationships ◽  
Compressive Stresses ◽  
Residual Compression

AbstractThe history and methodology of Japanese swordmaking are reviewed with particular reference to materials and processes. In order to gain a better understanding of the structure/property relationships in Japanese swords, a 16th century katana was analyzed metallographically and by attaching strain gages and cutting to relieve the residual stresses in the blade. The results indicate that the curve in the blade can be attributed to the volumetric expansion of the untempered martensite on the cutting edge, which also causes the edge to be in a state of residual compression. The residual compressive stresses are one of the key elements of the Japanese sword which give it superior toughness and cutting ability.

scholarly journals Expanding Monomers as Anti-Shrinkage Additives

Polymers ◽  
2021 ◽  
Vol 13 (5) ◽  
pp. 806
Author(s):  
Philipp Marx ◽  
Frank Wiesbrock
Keyword(s):  
Ring Opening ◽  
Covalent Bond ◽  
Volumetric Shrinkage ◽  
Structure Property ◽  
Atomic Packing ◽  
Materials Properties ◽  
Volumetric Expansion ◽  
Structure Property Relationships ◽  
Ring Opening Reaction ◽  
Measuring Techniques

Commonly, volumetric shrinkage occurs during polymerizations due to the shortening of the equilibrium Van der Waals distance of two molecules to the length of a (significantly shorter) covalent bond. This volumetric shrinkage can have severe influence on the materials’ properties. One strategy to overcome this volumetric shrinkage is the use of expanding monomers that show volumetric expansion during polymerization reactions. Such monomers exhibit cyclic or even oligocyclic structural motifs with a correspondingly dense atomic packing. During the ring-opening reaction of such monomers, linear structures with atomic packing of lower density are formed, which results in volumetric expansion or at least reduced volumetric shrinkage. This review provides a concise overview of expanding monomers with a focus on the elucidation of structure-property relationships. Preceded by a brief introduction of measuring techniques for the quantification of volumetric changes, the most prominent classes of expanding monomers will be presented and discussed, namely cycloalkanes and cycloalkenes, oxacycles, benzoxazines, as well as thiocyclic compounds. Spiroorthoesters, spiroorthocarbonates, cyclic carbonates, and benzoxazines are particularly highlighted.

Structure-property relationships of PE/PP sandwiched films

1987 ◽  
Vol 45 ◽  
pp. 454-455
Author(s):  
J. Petermann ◽  
G. Broza ◽  
U. Rieck ◽  
A. Jaballah ◽  
A. Kawaguchi
Keyword(s):  
Mechanical Tests ◽  
Polymer Materials ◽  
Ionic Crystals ◽  
Structure Property ◽  
Polymer Systems ◽  
Structure Property Relationships ◽  
Oriented Films ◽  
Materials Used ◽  
Polymer Laminates ◽  
Heated Glass

Oriented overgrowth of polymer materials onto ionic crystals is well known and recently it was demonstrated that this epitaxial crystallisation can also occur in polymer/polymer systems, under certain conditions. The morphologies and the resulting physical properties of such systems will be presented, especially the influence of epitaxial interfaces on the adhesion of polymer laminates and the mechanical properties of epitaxially crystallized sandwiched layers.Materials used were polyethylene, PE, Lupolen 6021 DX (HDPE) and 1810 D (LDPE) from BASF AG; polypropylene, PP, (PPN) provided by Höchst AG and polybutene-1, PB-1, Vestolen BT from Chemische Werke Hüls. Thin oriented films were prepared according to the method of Petermann and Gohil, by winding up two different polymer films from two separately heated glass-plates simultaneously with the help of a motor driven cylinder. One double layer was used for TEM investigations, while about 1000 sandwiched layers were taken for mechanical tests.

Approaches for TEM imaging of cavitation in toughened nylon

1989 ◽  
Vol 47 ◽  
pp. 352-353
Author(s):  
Barbara A. Wood
Keyword(s):  
Morphological Characteristics ◽  
Structure Property ◽  
Polymer Systems ◽  
Selective Staining ◽  
Structure Property Relationships ◽  
Rubber Toughened ◽  
Shear Yield ◽  
Controversial Topic ◽  
Selection Of ◽  
Diamond Knife

A controversial topic in the study of structure-property relationships of toughened polymer systems is the internal cavitation of toughener particles resulting from damage on impact or tensile deformation.Detailed observations of the influence of morphological characteristics such as particle size distribution on deformation mechanisms such as shear yield and cavitation could provide valuable guidance for selection of processing conditions, but TEM observation of damaged zones presents some experimental difficulties.Previously published TEM images of impact fractured toughened nylon show holes but contrast between matrix and toughener is lacking; other systems investigated have clearly shown cavitated impact modifier particles. In rubber toughened nylon, the physical characteristics of cavitated material differ from undamaged material to the extent that sectioning of heavily damaged regions by cryoultramicrotomy with a diamond knife results in sections of greater than optimum thickness (Figure 1). The detailed morphology is obscured despite selective staining of the rubber phase using the ruthenium trichloride route to ruthenium tetroxide.

Theoretical study of the prestressing strand's stress by computer modeling methods

2020 ◽  
Vol 76 (11) ◽  
pp. 1139-1148
Author(s):  
A. G. Korchunov ◽  
E. M. Medvedeva ◽  
E. M. Golubchik
Keyword(s):  
Residual Stresses ◽  
High Strength ◽  
Pearlitic Steel ◽  
Internal Stresses ◽  
Steel Microstructure ◽  
Compressive Stresses ◽  
Wide Range ◽  
Prestressing Strands ◽  
Increasing Temperature ◽  
Wire Strand

The modern construction industry widely uses reinforced concrete structures, where high-strength prestressing strands are used. Key parameters determining strength and relaxation resistance are a steel microstructure and internal stresses. The aim of the work was a computer research of a stage-by-stage formation of internal stresses during production of prestressing strands of structure 1х7(1+6), 12.5 mm diameter, 1770 MPa strength grade, made of pearlitic steel, as well as study of various modes of mechanical and thermal treatment (MTT) influence on their distribution. To study the effect of every strand manufacturing operation on internal stresses of its wires, the authors developed three models: stranding and reducing a 7-wire strand; straightening of a laid strand, stranding and MTT of a 7-wire strand. It was shown that absolute values of residual stresses and their distribution in a wire used for strands of a specified structure significantly influence performance properties of strands. The use of MTT makes it possible to control in a wide range a redistribution of residual stresses in steel resulting from drawing and strand laying processes. It was established that during drawing of up to 80% degree, compressive stresses of 1100-1200 MPa degree are generated in the central layers of wire. The residual stresses on the wire surface accounted for 450-500 MPa and were tension in nature. The tension within a range of 70 kN to 82 kN combined with a temperature range of 360-380°С contributes to a two-fold decrease in residual stresses both in the central and surface layers of wire. When increasing temperature up to 400°С and maintaining the tension, it is possible to achieve maximum balance of residual stresses. Stranding stresses, whose high values entail failure of lay length and geometry of the studied strand may be fully eliminated only at tension of 82 kN and temperature of 400°С. Otherwise, stranding stresses result in opening of strands.

Catalyst Halogenation Enables Rapid and Efficient Polymerizations with Visible to Near-Infrared Light

2020 ◽  
Author(s):  
Alex Stafford ◽  
Dowon Ahn ◽  
Emily Raulerson ◽  
Kun-You Chung ◽  
Kaihong Sun ◽  
...  
Keyword(s):  
Near Infrared ◽  
Transient Absorption ◽  
Reaction Times ◽  
Infrared Light ◽  
Structure Property ◽  
Light Emitting ◽  
Structure Property Relationships ◽  
Nir Light ◽  
Light Intensities ◽  
Emission Quenching

Driving rapid polymerizations with visible to near-infrared (NIR) light will enable nascent technologies in the emerging fields of bio- and composite-printing. However, current photopolymerization strategies are limited by long reaction times, high light intensities, and/or large catalyst loadings. Improving efficiency remains elusive without a comprehensive, mechanistic evaluation of photocatalysis to better understand how composition relates to polymerization metrics. With this objective in mind, a series of methine- and aza-bridged boron dipyrromethene (BODIPY) derivatives were synthesized and systematically characterized to elucidate key structure-property relationships that facilitate efficient photopolymerization driven by visible to NIR light. For both BODIPY scaffolds, halogenation was shown as a general method to increase polymerization rate, quantitatively characterized using a custom real-time infrared spectroscopy setup. Furthermore, a combination of steady-state emission quenching experiments, electronic structure calculations, and ultrafast transient absorption revealed that efficient intersystem crossing to the lowest excited triplet state upon halogenation was a key mechanistic step to achieving rapid photopolymerization reactions. Unprecedented polymerization rates were achieved with extremely low light intensities (< 1 mW/cm<sup>2</sup>) and catalyst loadings (< 50 μM), exemplified by reaction completion within 60 seconds of irradiation using green, red, and NIR light-emitting diodes.

A Review on Camptothecin Analogs with Promising Cytotoxic Profile

2019 ◽  
Vol 18 (13) ◽  
pp. 1796-1814 ◽  
Author(s):  
Sk. Abdul Amin ◽  
Nilanjan Adhikari ◽  
Tarun Jha ◽  
Shovanlal Gayen
Keyword(s):  
Cell Lines ◽  
Cancer Cell ◽  
Cancer Cell Lines ◽  
Structure Property ◽  
Cytotoxic Potential ◽  
Structure Property Relationships ◽  
Structure Activity ◽  
Camptothecin Analogs ◽  
Pharmacokinetic Properties ◽  
Quantitative Structure Activity Relationships

Camptothecin (CPT), obtained from Camptotheca acuminata (Nyssaceae), is a quinoline type of alkaloid. Apart from various traditional uses, it is mainly used as a potential cytotoxic agent acting against a variety of cancer cell lines. Though searches have been continued for last six decades, still it is a demanding task to design potent and cytotoxic CPTs. Different CPT analogs are synthesized to enhance the cytotoxic potential as well as to increase the pharmacokinetic properties of these analogs. Some of these analogs were proven to be clinically effective in different cancer cell lines. In this article, different CPT analogs have been highlighted extensively to get a detail insight about the structure-property relationships as well as different quantitative structure-activity relationships (QSARs) modeling of these analogs are also discussed. This study may be beneficial for designing newer CPT analogs in future.

Structure-property relationships in bainitic steels

1990 ◽  
Vol 21 (6) ◽  
pp. 1527-1540 ◽  
Author(s):  
D. V. Edmonds ◽  
R. C. Cochrane
Keyword(s):  
Structure Property ◽  
Structure Property Relationships ◽  
Bainitic Steels

scholarly journals Thermal Effects on Surface and Subsurface Modifications in Laser-Combined Deep Rolling

2021 ◽  
Vol 5 (2) ◽  
pp. 55
Author(s):  
Robert Zmich ◽  
Daniel Meyer
Keyword(s):  
Surface Layer ◽  
Residual Stresses ◽  
Thermal Loads ◽  
Deep Rolling ◽  
Mechanical Loads ◽  
Thermomechanical Process ◽  
Compressive Stresses ◽  
New Process ◽  
Negative Effect ◽  
Compressive Residual Stresses

Knowledge of the relationships between thermomechanical process loads and the resulting modifications in the surface layer enables targeted adjustments of the required surface integrity independent of the manufacturing process. In various processes with thermomechanical impact, thermal and mechanical loads act simultaneously and affect each other. Thus, the effects on the modifications are interdependent. To gain a better understanding of the interactions of the two loads, it is necessary to vary thermal and mechanical loads independently. A new process of laser-combined deep rolling can fulfil exactly this requirement. The presented findings demonstrate that thermal loads can support the generation of residual compressive stresses to a certain extent. If the thermal loads are increased further, this has a negative effect on the surface layer and the residual stresses are shifted in the direction of tension. The results show the optimum range of thermal loads to further increase the compressive residual stresses in the surface layer and allow to gain a better understanding of the interactions between thermal and mechanical loads.

Sign in / Sign up

Export Citation Format

Share Document