scholarly journals Chemical and Mechanical Properties of Experimental Dental Composites as a Function of Formulation and Postcuring Thermal Treatment

2018 ◽  
Vol 2018 ◽  
pp. 1-6 ◽  
Author(s):  
Renata A. Esteves ◽  
Letícia C. C. Boaro ◽  
Flávia Gonçalves ◽  
Luiza M. P. Campos ◽  
Cecy M. Silva ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Fracture Toughness ◽  
Elastic Modulus ◽  
Thermal Treatment ◽  
Flexural Strength ◽  
Low Cost ◽  
Chemical Properties ◽  
Degree Of Conversion ◽  
Dental Composites ◽  
Molar Ratios

This study evaluated the influence of formulation and thermal treatment on the degree of conversion, fracture toughness, flexural strength, and elastic modulus of experimental composites. Six composites were analyzed at BisGMA : TEGDMA molar ratios of 1 : 1 and 7 : 3 with filler at 30, 50, and 70 wt%. The degree of conversion was analyzed by Fourier transform infrared spectroscopy, fracture toughness was measured using the single-edge notched beam, and flexural strength and elastic modulus were measured with the 3-point bend test. For all tests, one-half of the specimens received thermal treatment at 170°C for 10 min. Data were analyzed by the Kruskal-Wallis or ANOVA/Tukey’s test (α = 5%). The 1 : 1 BisGMA : TEGDMA ratio showed higher properties than the 7 : 3 ratio. Although the material with 70% filler had a conversion lower than the one with 50%, it showed higher mechanical properties. The thermal treatment improved all properties in all materials. Therefore, the use of an equimolar ratio of BisGMA : TEGDMA can be paired with 70 wt% filler to design dental composites that possess increased advantageous physical and chemical properties. Furthermore, the simple and low-cost method of thermal treatment proposed for use in clinical dentistry has been shown to effectively improve the properties of all evaluated materials.

scholarly journals Improved Fracture Toughness and Conversion Degree of Resin-Based Dental Composites after Modification with Liquid Rubber

Materials ◽  
2020 ◽  
Vol 13 (12) ◽  
pp. 2704
Author(s):  
Krzysztof Pałka ◽  
Joanna Kleczewska ◽  
Emil Sasimowski ◽  
Anna Belcarz ◽  
Agata Przekora
Keyword(s):  
Mechanical Properties ◽  
Fracture Toughness ◽  
Dental Materials ◽  
Degree Of Conversion ◽  
Dental Composites ◽  
Conversion Degree ◽  
Matrix Resin ◽  
Ceramic Filler ◽  
Liquid Rubber ◽  
The Matrix

There are many methods widely applied in the engineering of biomaterials to improve the mechanical properties of the dental composites. The aim of this study was to assess the effect of modification of dental composites with liquid rubber on their mechanical properties, degree of conversion, viscosity, and cytotoxicity. Both flow and packable composite consisted of a mixture of Bis-GMA, TEGDMA, UDMA, and EBADMA resins reinforced with 60 and 78 wt.% ceramic filler, respectively. It was demonstrated that liquid rubber addition significantly increased the fracture toughness by 9% for flow type and 8% for condensable composite. The influence of liquid rubber on flexural strength was not statistically significant. The addition of the toughening agent significantly reduced Young’s modulus by 7% and 9%, respectively, while increasing deformation at breakage. Scanning electron microscopy (SEM) observations allowed to determine the mechanisms of toughening the composites reinforced with ceramic particles. These mechanisms included bridging the crack edges, blocking the crack tip by particles and dissipation of fracture energy by deflection of the cracks on larger particles. The degree of conversion increased after modification, mainly due to a decrease in the matrix resin viscosity. It was also shown that all dental materials were nontoxic according to ISO 10993-5, indicating that modified materials have great potential for commercialization and clinical applications.

Mechanical Properties of Machinable Zirconia Dental Composites

2007 ◽  
Vol 336-338 ◽  
pp. 1587-1589
Author(s):  
Wen Xu Li ◽  
Hua Zhao ◽  
Ying Song ◽  
Bin Su ◽  
Fu Ping Wang
Keyword(s):  
Mechanical Properties ◽  
Fracture Toughness ◽  
Calcium Phosphate ◽  
Flexural Strength ◽  
Dental Composite ◽  
The Other ◽  
Dental Composites ◽  
Composite Ceramics ◽  
Cad Cam ◽  
The Common

Ca3(PO4)2/ZrO2 dental composite ceramics using for CAD/CAM system were prepared and the effects of weak phases on microstructures and mechanical properties were studied. The results showed that intergranular spreads happened with the increasing Ca3(PO4)2 contents due to the discontinuity of weak interfaces between Zirconia and Calcium phosphate in matrix. So the flexural strength and hardness of the Ca3(PO4)2/ZrO2 composite ceramics were decreased effectively, which improved the machinability of the composites. On the other hand, strong interfaces between Zirconias increased the integrality of the ceramic structures. ZrO2 composite Ceramics with 15% Ca3(PO4)2 were sintered at 1350°C. The flexural strength is 300.44MPa, fracture toughness is 4.36 MPam1/2, and hardness is 6.69 GPa. The cutting exponent of the Ca3(PO4)2/ZrO2 composite ceramics is obviously lower than that of the common commercial Vita Mark II and Dicor MGC ceramics, which shows good mechanical properties and machinability.

scholarly journals Effect of Camphorquinone Concentration in Physical-Mechanical Properties of Experimental Flowable Resin Composites

2018 ◽  
Vol 2018 ◽  
pp. 1-10 ◽  
Author(s):  
Dayany da Silva Alves Maciel ◽  
Arnaldo Bonfim Caires-Filho ◽  
Marta Fernandez-Garcia ◽  
Camillo Anauate-Netto ◽  
Roberta Caroline Bruschi Alonso
Keyword(s):  
Mechanical Properties ◽  
Elastic Modulus ◽  
Flexural Strength ◽  
Mechanical Strength ◽  
Surface Hardness ◽  
Degree Of Conversion ◽  
Bending Test ◽  
Resin Matrix ◽  
Shrinkage Stress ◽  
Depth Of Cure

The aim of this study was to evaluate the effect of camphorquinone concentration in physical-mechanical properties of experimental flowable composites in order to find the concentration that results in maximum conversion, balanced mechanical strength, and minimum shrinkage stress. Model composites based on BISGMA/TEGDMA with 70% wt filler loading were prepared containing different concentrations of camphorquinone (CQ) on resin matrix (0.25%, 0.50%, 1%, 1.50%, and 2% by weight). Degree of conversion was determined by FTIR. Surface hardness was assessed before and after 24 h ethanol storage and softening rate was determined. Depth of cure was determined by Knoop hardness evaluation at different depths. Color was assessed by reflectance spectrophotometer, employing the CIE-Lab system. Flexural strength and elastic modulus were determined by a three-point bending test. Shrinkage stress was determined in a Universal Testing Machine in a high compliance system. Data were submitted to ANOVA and Tukey’s test (α = 0.05). The increase in CQ concentration caused a significant increase on flexural strength and luminosity of composites. Surface hardness was not affected by the concentration of CQ. Composite containing 0.25% wt CQ showed lower elastic modulus and shrinkage stress when compared to others. Depth of cure was 3 mm for composite containing 1% CQ and 2 mm for the other tested composites. Degree of conversion was inversely correlated with softening rate and directly correlated with elastic modulus and shrinkage stress. In conclusion, CQ concentration affects polymerization characteristics and mechanical strength of composites. The concentration of CQ in flowable composite for optimized polymerization and properties was 1% wt of the resin matrix, which allows adequate balance among degree of conversion, depth of cure, mechanical properties, and color characteristics of these materials.

Effect of Preheating and Fatiguing on Mechanical Properties of Bulk-fill and Conventional Composite Resin

2019 ◽  
Vol 45 (4) ◽  
pp. 387-395
Author(s):  
AA Abdulmajeed ◽  
TE Donovan ◽  
R Cook ◽  
TA Sulaiman
Keyword(s):  
Mechanical Properties ◽  
Fracture Toughness ◽  
Tensile Strength ◽  
Elastic Modulus ◽  
Flexural Strength ◽  
Composite Resin ◽  
Statistical Significance ◽  
Composite Resins ◽  
Significant Difference ◽  
Diametral Tensile Strength

Clinical Relevance Bulk-fill composite resins may have comparable mechanical properties to conventional composite resin. Preheating does not reduce the mechanical properties of composite resins. SUMMARY Statement of Problem: Bulk-fill composite resins are increasingly used for direct restorations. Preheating high-viscosity versions of these composites has been advocated to increase flowability and adaptability. It is not known what changes preheating may cause on the mechanical properties of these composite resins. Moreover, the mechanical properties of these composites after mastication simulation is lacking. Purpose: The purpose of this study was to evaluate the effect of fatiguing and preheating on the mechanical properties of bulk-fill composite resin in comparison to its conventional counterpart. Methods and Materials: One hundred eighty specimens of Filtek One Bulk Fill Restorative (FOBR; Bulk-Fill, 3M ESPE) and Filtek Supreme Ultra (FSU; Conventional, 3M ESPE) were prepared for each of the following tests: fracture toughness (International Organization for Standardization, ISO 6872), diametral tensile strength (No. 27 of ANSI/ADA), flexural strength, and elastic modulus (ISO Standard 4049). Specimens in the preheated group were heated to 68°C for 10 minutes and in the fatiguing group were cyclically loaded and thermocycled for 600,000 cycles and then tested. Two-/one-way analysis of variance followed by Tukey Honest Significant Difference (HSD) post hoc test was used to analyze data for statistical significance (α=0.05). Results: Preheating and fatiguing had a significant effect on the properties of both FSU and FOBR. Fracture toughness increased for FOBR specimens when preheated and decreased when fatigued (p=0.016). FOBR had higher fracture toughness value than FSU. Diametral tensile strength decreased significantly after fatiguing for FSU (p=0.0001). FOBR had a lower diametral tensile strength baseline value compared with FSU (p=0.004). Fatiguing significantly reduced the flexural strength of both FSU and FOBR (p=0.011). Preheating had no effect on the flexural strength of either FSU or FOBR. Preheating and fatiguing significantly decreased the elastic modulus of both composite resins equally (p>0.05). Conclusions: Preheating and fatiguing influenced the mechanical properties of composite resins. Both composites displayed similar mechanical properties. Preheating did not yield a major negative effect on their mechanical properties; the clinical implications are yet to be determined.

scholarly journals Characterization of Heat-Polymerized Monomer Formulations for Dental Infiltrated Ceramic Networks

2021 ◽  
Vol 11 (16) ◽  
pp. 7370
Author(s):  
Janine Tiu ◽  
Renan Belli ◽  
Ulrich Lohbauer
Keyword(s):  
Mechanical Properties ◽  
Fracture Toughness ◽  
Elastic Modulus ◽  
Composite Structures ◽  
Triethylene Glycol ◽  
Degree Of Conversion ◽  
Reduced Viscosity ◽  
Heat Polymerization ◽  
Urethane Dimethacrylate

(1) Objectives: This work examined properties of dental monomer formulations of an aromatic dimethacylate (BisGMA), aliphatic urethane dimethacrylate (UDMA), and triethylene glycol dimethacrylate (TEGDMA). The monomers were combined in different ratio formulations and heat-polymerized containing the initiator benzoyl peroxide (BPO) specifically for the purpose of infiltration into polymer-infiltrated composite structures. (2) Methods: The monomers were combined in different weight ratios and underwent rheological analysis (viscosity and temperature dependence), degree of conversion, and mechanical properties (elastic modulus, hardness, fracture toughness). (3) Results: Rheological properties showed Newtonian behavior for monomers with a large dependence on temperature. The addition of BPO allowed for gelation in the range of 72.0–75.9 °C. Degree of conversion was found between 74% and 87% DC, unaffected by an increase of TEGDMA (up to 70 wt%). Elastic modulus, hardness, and fracture toughness were inversely proportional to an increase in TEGDMA. Elastic modulus and hardness were found slightly increased for UDMA versus BisGMA formulations, while fracture toughness ranged between 0.26 and 0.93 MPa·m0.5 for UDMA- and 0.18 and 0.68 MPa·m0.5 for BisGMA-based formulations. (4) Significance: Heat-polymerization allows for greater range of monomer formulations based on viscosity and degree of conversion when selecting for infiltrated composite structures. Therefore, selection should be based on mechanical properties. The measured data for fracture toughness combined with the reduced viscosity at higher UDMA:TEGDMA ratios favor such formulations over BisGMA:TEGDMA mixtures.

scholarly journals 3D-Printed vs. Heat-Polymerizing and Autopolymerizing Denture Base Acrylic Resins

Materials ◽  
2021 ◽  
Vol 14 (19) ◽  
pp. 5781
Author(s):  
Leila Perea-Lowery ◽  
Mona Gibreel ◽  
Pekka K. Vallittu ◽  
Lippo V. Lassila
Keyword(s):  
Mechanical Properties ◽  
Fracture Toughness ◽  
Elastic Modulus ◽  
Flexural Strength ◽  
Water Solubility ◽  
Base Material ◽  
Acrylic Resin ◽  
Denture Base ◽  
3D Printed ◽  
Work Of Fracture

The aim of this work was to investigate the effect of two post-curing methods on the mechanical properties of a 3D-printed denture base material. Additionally, to compare the mechanical properties of that 3D-printed material with those of conventional autopolymerizing and a heat-cured denture base material. A resin for 3D-printing denture base (Imprimo®), a heat-polymerizing acrylic resin (Paladon® 65), and an autopolymerizing acrylic resin (Palapress®) were investigated. Flexural strength, elastic modulus, fracture toughness, work of fracture, water sorption, and water solubility were evaluated. The 3D-printed test specimens were post-cured using two different units (Imprimo Cure® and Form Cure®). The tests were carried out after both dry and 30 days water storage. Data were collected and statistically analyzed. Resin type had a significant effect on the flexural strength, elastic modulus, fracture toughness, and work of fracture (p < 0.001). The flexural strength and elastic modulus for the heat-cured polymer were significantly the highest among all investigated groups regardless of the storage condition (p < 0.001). The fracture toughness and work of fracture of the 3D-printed material were significantly the lowest (p < 0.001). The heat-cured polymer had the lowest significant water solubility (p < 0.001). The post-curing method had an impact on the flexural strength of the investigated 3D-printed denture base material. The flexural strength, elastic modulus, fracture toughness, work of fracture of the 3D-printed material were inferior to those of the heat-cured one. Increased post-curing temperature may enhance the flexural properties of resin monomers used for 3D-printing dental appliances.

scholarly journals Saliva Influence on the Mechanical Properties of Advanced CAD/CAM Composites for Indirect Dental Restorations

Polymers ◽  
2021 ◽  
Vol 13 (5) ◽  
pp. 808
Author(s):  
Teresa Palacios ◽  
Sandra Tarancón ◽  
Cristian Abad ◽  
José Ygnacio Pastor
Keyword(s):  
Mechanical Properties ◽  
Fracture Toughness ◽  
Elastic Modulus ◽  
Flexural Strength ◽  
Mechanical Performance ◽  
Artificial Saliva ◽  
Fluorescence Analysis ◽  
Dental Restoration ◽  
Global Approximation ◽  
Cad Cam

This study aims to evaluate the microstructural and mechanical properties of three commercial resin-based materials available for computer-aid design and manufacturing (CAD/CAM)-processed indirect dental restoration: LavaTM Ultimate Restorative (LU), 3M ESPE; Brilliant Crios (BC), COLTENE and CerasmartTM (CS), GC Dental Product. The three types of resin-based composite CAD/CAM materials were physically and mechanically tested under two conditions: directly as received by the manufacturer (AR) and after storage under immersion in artificial saliva (AS) for 30 days. A global approximation to microstructure and mechanical behaviour was evaluated: density, hardness and nanohardness, nanoelastic modulus, flexural strength, fracture toughness, fracture surfaces, and microstructures and fractography. Moreover, their structural and chemical composition using X-ray fluorescence analysis (XRF) and field emission scanning electron microscopy (FESEM) were investigated. As a result, LU exhibited slightly higher mechanical properties, while the decrease of its mechanical performance after immersion in AS was doubled compared to BC and CS. Tests of pristine material showed 13 GPa elastic modulus, 150 MPa flexural strength, 1.0 MPa·m1/2 fracture toughness, and 1.0 GPa hardness for LU, 11.4 GPa elastic modulus; 140 MPa flexural strength, 1.1 MPa·m1/2 fracture toughness, and 0.8 GPa hardness for BC; and 8.3 GPa elastic modulus, 140 MPa flexural strength, 0.9 MPa·m1/2 fracture toughness, and 0.7 GPa hardness for CS. These values were significantly reduced after one month of immersion in saliva. The interpretation of the mechanical results could suggest, in general, a better behaviour of LU compared with the other two despite it having the coarsest microstructure of the three studied materials. The saliva effect in the three materials was critically relevant for clinical use and must be considered when choosing the best solution for the restoration to be used.

Evaluation of flexural modulus, flexural strength and degree of conversion in BISGMA/TEGDMA resin filled with montmorillonite nanoparticles

2016 ◽  
Vol 51 (7) ◽  
pp. 927-937 ◽  
Author(s):  
Luiza MP Campos ◽  
Letícia C Boaro ◽  
Tamiris MR Santos ◽  
Pamela A Marques ◽  
Sonia RY Almeida ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Elastic Modulus ◽  
Flexural Strength ◽  
Polymer Matrix ◽  
Flexural Modulus ◽  
Degree Of Conversion ◽  
Bending Test ◽  
Similar Degree ◽  
Hybrid Filler ◽  
Barium Glass

This study had as its main objective to evaluate the flexural properties (strength and modulus) and degree of conversion of a dimethacrylate resin containing different amounts of nanoparticulated clay Montomorillonite (MMT) as filler. A series of composites containing similar amounts (in volume) of barium glass particles was also tested as control data. Eight formulations with polymeric matrix-based BisGMA/TEGDMA (Bisphenol A Bis(2-hydroxy-3 methacryloxypropyl)Ether/Triethyleneglycol Dimethacrylate), four added with MMT and four added with barium glass in the volume concentration of 20, 30, 40 and 50 vol% were studied. The degree of conversion was determined using near-IR spectroscopy. Elastic modulus and flexural strength were determined by the three-point bending test. The dispersion of MMT nanoparticles was determined by means of X-ray diffraction and transmission electron microscopy analysis. The fillers montomorillonite and barium glass interacted with polymer matrix-based BisGMA/TEGDMA in a distinct manner. Although the addition of montomorillonite nanoparticles resulted in similar degree of conversion and higher elastic modulus values at all concentrations tested, only at the 20 vol% the flexural strength was statistically higher, compared to the control groups filled with barium glass. This could be related to the need of concentration optimization of montomorillonite for each type of polymer matrix in order to adjust or improve mechanical properties. The addition of low concentrations (<l 20% vol) of montomorillonite nanoparticles in dental composites resins – such as additive or hybrid filler – should be studied, aiming to the reduction of polymerization shrinkage, better mechanical properties and improvement of a new technology for future applications.

The Improvement of Dental Composite Properties with Electromagnetically Aligned Nanofiber

2014 ◽  
Vol 1685 ◽  
Author(s):  
Tansel Uyar ◽  
Dilek Cokeliler
Keyword(s):  
Mechanical Properties ◽  
Elastic Modulus ◽  
Flexural Strength ◽  
Composite Resins ◽  
Dental Composite ◽  
Bending Test ◽  
Dental Composites ◽  
Layer By Layer ◽  
Aligned Fibers ◽  
Electrode Systems

ABSTRACTBecause of the aesthetics, handy and low cost features, acrylic resin is the main material in denture fabrication last 40 years. The purpose of this study is to improve mechanical properties of acrylic based dental composites used in dentistry by applying nanofiber approaches. Polymethylmethacrylate (PMMA) is commonly used as a base acrylic denture material with benefits of rapid and easy handling but sometime this material can be fractured or cracked in clinical use because of the strength issues that is frequently used in restorative dentistry in recent years. A wide variety of fillers that are used to produce PMMA composites draw the attention in literature. Using PMMA composite resins with electrospun polyvinylalcohol (PVA) nanofiber fillers is our first novelty. Also the producing and using aligned electrospun fibers as a filler is our second novelty of this practice. PVA was selected as composite filler because of biocompatibility and preparing easily also has non-toxic solvent. Electrospinning system is manufactured that allows manipulation of electric field used in the application of alignment in lab scale. Various auxillary electrode systems are used for different patterns of alignment with the manufactured device and electrode systems produce fibers in different range of diameter. Scanning electron microscopy (SEM) is used for physical characterization and determined the range of fiber diameters. After the optimization of concentration step non-woven and aligned fibers are also analyzed. Non-woven fiber has no unique pattern because of the nature of electrospinning but aligned fibers has crossed lines. These produced fibers structured as layer-by-layer form with different features are used in producing PMMA dental composites with different volume ratios. In the last part of the research, PMMA dental composites are produced with aligned and formless fibers that are characterized with three-point bending test. The maximum flexural strength figure shows that fiber load by weight %0.25 and above improves the maximum. The change of flexural strength, elastic modulus values and toughness are obtained and compared with formless and aligned PVA nanofiber included composite specimens. As a result, mechanical properties of PMMA dental composites are improved with using PVA nanofibers as a filler also with the usage of aligned fibers instead of the formless ones the effects of improvement gets better with maximum values as 5.1 MPa (flexural strength), 0.8 GPa (elastic modulus), 170kJ/m3 (toughness).

scholarly journals Assessment of the Rheological and Mechanical Properties of Geopolymer Concrete Comprising Fly Ash and Fluid Catalytic Cracking Residue as Aluminosilicate Precursor

2021 ◽  
Vol 11 (7) ◽  
pp. 3032
Author(s):  
Tuan Anh Le ◽  
Sinh Hoang Le ◽  
Thuy Ninh Nguyen ◽  
Khoa Tan Nguyen
Keyword(s):  
Mechanical Properties ◽  
Compressive Strength ◽  
Elastic Modulus ◽  
Fly Ash ◽  
Flexural Strength ◽  
Catalytic Cracking ◽  
Fluid Catalytic Cracking ◽  
High Alumina ◽  
Geopolymer Concrete ◽  
Sem Images

The use of fluid catalytic cracking (FCC) by-products as aluminosilicate precursors in geopolymer binders has attracted significant interest from researchers in recent years owing to their high alumina and silica contents. Introduced in this study is the use of geopolymer concrete comprising FCC residue combined with fly ash as the requisite source of aluminosilicate. Fly ash was replaced with various FCC residue contents ranging from 0–100% by mass of binder. Results from standard testing methods showed that geopolymer concrete rheological properties such as yield stress and plastic viscosity as well as mechanical properties including compressive strength, flexural strength, and elastic modulus were affected significantly by the FCC residue content. With alkali liquid to geopolymer solid ratios (AL:GS) of 0.4 and 0.5, a reduction in compressive and flexural strength was observed in the case of geopolymer concrete with increasing FCC residue content. On the contrary, geopolymer concrete with increasing FCC residue content exhibited improved strength with an AL:GS ratio of 0.65. Relationships enabling estimation of geopolymer elastic modulus based on compressive strength were investigated. Scanning electron microscope (SEM) images and X-ray diffraction (XRD) patterns revealed that the final product from the geopolymerization process consisting of FCC residue was similar to fly ash-based geopolymer concrete. These observations highlight the potential of FCC residue as an aluminosilicate source for geopolymer products.

Sign in / Sign up

Export Citation Format

Share Document