scholarly journals Modification of Surface and Tribological Properties of DLC Films by Adding Silver Content

2008 ◽  
Author(s):  
H.-S. Zhang ◽  
J. L. Endrino ◽  
A. Anders
Keyword(s):  
Thin Films ◽  
Atomic Force Microscopy ◽  
Tribological Properties ◽  
Silver Content ◽  
Diamond Like Carbon ◽  
Dlc Coatings ◽  
Force Microscopy ◽  
Atomic Force ◽  
Plasma Immersion Ion Implantation ◽  
Scratch Tests

The incorporation of silver into the diamond-like carbon (DLC) coatings has shown excellent potential in various applications; therefore the surface and tribological properties of silver-containing DLC thin films deserve to be investigated. In this study we have deposited silver-containing hydrogenated and hydrogen-free DLC coatings by plasma immersion ion implantation and deposition (PIII-D) methods. Atomic force microscopy (AFM) and nano-scratch tests were used to study the surface and tribological properties. The silver incorporation had only slight effects on hydrogenated DLC coatings. However, the incorporation of silver has significant effect on hydrogen-free DLC of smoothing the surface and increasing the surface energy. Those effects have been illustrated and explained in the context of experimental results.

Atomic force microscopy of in situ deformed nickel thin films

1999 ◽  
Vol 353 (1-2) ◽  
pp. 194-200 ◽  
Author(s):  
C. Coupeau ◽  
J.F. Naud ◽  
F. Cleymand ◽  
P. Goudeau ◽  
J. Grilhé
Keyword(s):  
Thin Films ◽  
Atomic Force Microscopy ◽  
Force Microscopy ◽  
Nickel Thin Films ◽  
Atomic Force

Nanocrystalline Solutions as Precursors to The Spray Deposition of Cdte Thin Films

1995 ◽  
Vol 382 ◽  
Author(s):  
Martin Pehnt ◽  
Douglas L. Schulz ◽  
Calvin J. Curtis ◽  
Helio R. Moutinho ◽  
Amy Swartzlander ◽  
...  
Keyword(s):  
Thin Films ◽  
Atomic Force Microscopy ◽  
Grain Size ◽  
X Ray Diffraction ◽  
X Ray ◽  
Force Microscopy ◽  
Cdte Nanoparticles ◽  
Atomic Force ◽  
Vis Spectroscopy ◽  
Cdte Thin Films

ABSTRACTIn this article we report the first nanoparticle-derived route to smooth, dense, phase-pure CdTe thin films. Capped CdTe nanoparticles were prepared by injection of a mixture of Cd(CH3)2, (n-C8H17)3 PTe and (n-C8H17)3P into (n-C8H17)3PO at elevated temperatures. The resultant nanoparticles 32-45 Å in diameter were characterized by x-ray diffraction, UV-Vis spectroscopy, transmission electron microscopy, thermogravimetric analysis and energy dispersive x-ray spectroscopy. CdTe thin film deposition was accomplished by dissolving CdTe nanoparticles in butanol and then spraying the solution onto SnO2-coated glass substrates at variable susceptor temperatures. Smooth and dense CdTe thin films were obtained using growth temperatures approximately 200 °C less than conventional spray pyrolysis approaches. CdTe films were characterized by x-ray diffraction, UV-Vis spectroscopy, atomic force microscopy, and Auger electron spectroscopy. An increase in crystallinity and average grain size as determined by x-ray diffraction was noted as growth temperature was increased from 240 to 300 °C. This temperature dependence of film grain size was further confirmed by atomic force microscopy with no remnant nanocrystalline morphological features detected. UV-Vis characterization of the CdTe thin films revealed a gradual decrease of the band gap (i.e., elimination of nanocrystalline CdTe phase) as the growth temperature was increased with bulk CdTe optical properties observed for films grown at 300 °C.