Low-k Dielectric Breakdown Improvement with Co(W,P) Cap Barrier

2006 ◽  
Author(s):  
Tam Tan ◽  
Jesica ◽  
Chee Gan ◽  
Nam Hwang ◽  
Jeffrey Gambino
Keyword(s):  
Dielectric Breakdown ◽  
Low K

Assessment of Reliability of cap layers used in Cu-Black DiamondTM Interconnects

2003 ◽  
Vol 766 ◽  
Author(s):  
Ahila Krishnamoorthy ◽  
N.Y. Huang ◽  
Shu-Yunn Chong
Keyword(s):  
Dielectric Layer ◽  
Dielectric Breakdown ◽  
Copper Ions ◽  
Dielectric Strength ◽  
Time Dependent ◽  
Breakdown Field ◽  
Field Range ◽  
Time Dependent Dielectric Breakdown ◽  
Voltage Ramp ◽  
Low K

AbstractBlack DiamondTM. (BD) is one of the primary candidates for use in copper-low k integration. Although BD is SiO2 based, it is vastly different from oxide in terms of dielectric strength and reliability. One of the main reliability concerns is the drift of copper ions under electric field to the surrounding dielectric layer and this is evaluated by voltage ramp (V-ramp) and time dependent dielectric breakdown (TDDB). Metal 1 and Metal 2 intralevel comb structures with different metal widths and spaces were chosen for dielectric breakdown studies. Breakdown field of individual test structures were obtained from V-ramp tests in the temperature range of 30 to 150°C. TDDB was performed in the field range 0.5 – 2 MV/cm. From the leakage between combs at the same level (either metal 1 or metal 2) Cu drift through SiC/BD or SiN/BD interface was characterized. It was found that Cu/barrier and barrier/low k interfaces functioned as easy paths for copper drift thereby shorting the lines. Cu/SiC was found to provide a better interface than Cu/SiN.

Delamination-induced dielectric breakdown in Cu/low-k interconnects

2008 ◽  
Vol 23 (6) ◽  
pp. 1802-1808 ◽  
Author(s):  
T.L. Tan ◽  
C.L. Gan ◽  
A.Y. Du ◽  
Y.C. Tan ◽  
C.M. Ng
Keyword(s):  
Activation Energy ◽  
Failure Mechanism ◽  
Thermal Process ◽  
Dielectric Breakdown ◽  
Time Dependent ◽  
Bond Breaking ◽  
Capping Layer ◽  
Time Dependent Dielectric Breakdown ◽  
Potential Failure ◽  
Low K

Delamination at an interface with the weakest adhesion strength, which is found to be between the SiC(N) capping layer and the SiOCH low-k dielectric, is a potential failure mechanism contributing to time-dependent dielectric breakdown (TDDB) reliability. Bond breaking at that interface is believed to be driven by a field-enhanced thermal process and catalyzed by leakage current through the capping layer based on physical analyses and TDDB measurements. Delamination is found to be easier in terminated tips and corners than in parallel comb lines due to the layout orientation of the Cu lines. Moreover, TDDB activation energy Ea can be an indicator of the ease of delamination, whereby a lower Ea corresponds to an easier delamination.

Impact of irregular geometries on low-k dielectric breakdown

2011 ◽  
Vol 51 (9-11) ◽  
pp. 1582-1586 ◽  
Author(s):  
Muhammad Bashir ◽  
Linda Milor ◽  
Dae Hyun Kim ◽  
Sung Kyu Lim
Keyword(s):  
Dielectric Breakdown ◽  
Irregular Geometries ◽  
Low K