scholarly journals High temperature oxidation resistance of nickel-/nitride composite coatings : A brief review

2021 ◽  
Author(s):  
Esmar Budi
Keyword(s):  
High Temperature ◽  
Oxidation Resistance ◽  
High Temperature Oxidation ◽  
Composite Coatings ◽  
Temperature Oxidation ◽  
Nickel Nitride

High-Temperature Oxidation Resistance of Electroless Ni-P-ZrO2 Composite Coatings

2011 ◽  
Vol 686 ◽  
pp. 569-573 ◽  
Author(s):  
Ming Feng Tan ◽  
Wan Chang Sun ◽  
Lei Zhang ◽  
Quan Zhou ◽  
Jin Ding
Keyword(s):  
High Temperature ◽  
Carbon Steel ◽  
Oxidation Resistance ◽  
High Temperature Oxidation ◽  
Steel Substrate ◽  
Composite Coatings ◽  
Low Carbon ◽  
Temperature Oxidation ◽  
P Matrix ◽  
Electroless Ni

Electroless Ni-P coating containing ZrO2particles was successfully co-deposited on low carbon steel substrate. The surface and cross-sectional micrographs of the composite coatings were observed with scanning electron microscopy (SEM). And the chemical composition of the coating was analyzed with energy dispersive spectroscopy (EDS). The oxidation resistance was evaluated by weight gains during high temperature oxidation test. The results showed that the embedded ZrO2particles with irregular shape uniformly distributed in the entire Ni-P matrix, and the coating showed a good adhesion to the substrate. The weight gain curves of Ni-P-ZrO2composite coatings and Ni-P coating at 923K oxidation experiments were in accordance with . The ZrO2particles in Ni-P matrix could significantly enhance the high temperature oxidation resistance of the carbon steel substrate as compared to pure Ni-P coating.

Microstructure and High-Temperature Oxidation of Ni-Si3N4 Composite Coatings by Pulse Electrodeposition

2015 ◽  
Vol 817 ◽  
pp. 421-425
Author(s):  
Kun Zhao ◽  
Wan Chang Sun ◽  
Chun Yu Miao ◽  
Hui Cai ◽  
Ju Mei Zhang ◽  
...  
Keyword(s):  
Aluminum Alloy ◽  
High Temperature ◽  
Oxidation Resistance ◽  
High Temperature Oxidation ◽  
Composite Coatings ◽  
X Ray Diffraction ◽  
Temperature Oxidation ◽  
Electro Deposition ◽  
X Ray ◽  
Crystallite Structure

Nickel matrix and Si3N4 micron particles were co-deposited on the aluminum alloy by pulse electro-deposition for high temperature performance. Meanwhile, the oxidation resistance was evaluated through the high temperature oxidation test. The phase structure, micrographs and components of the composite coatings were investigated by means of X-ray diffraction (XRD), scanning electron microscopy (SEM) together with energy dispersive spectroscopy (EDS) respectively. The results indicated that Si3N4 particles were uniformly distributed across the coating and there were no pores and cracks or other defects at the coating/substrate interface. Ni-Si3N4 composite coatings are characterized by pyramidal micro-crystallite structure. The thickness of Ni-Si3N4 composite coatings were up to 80 μm for 2h. The results also revealed that the Ni-Si3N4 composite coatings presented better oxidation resistance than the pure Ni coating and aluminum alloy at high temperature. After oxidation at 673 K for 8h, the oxidation resistance of Ni-Si3N4 composite coatings presented the improved oxidation resistance behavior compared to pure Ni and the aluminum alloy, respectively.

Improving the high-temperature oxidation resistance of ASME-SA213-T11 boiler tube steel by plasma spraying with CNT-reinforced alumina coatings

2018 ◽  
Vol 65 (2) ◽  
pp. 217-223 ◽  
Author(s):  
Rakesh Goyal ◽  
Buta Singh Sidhu ◽  
Vikas Chawla
Keyword(s):  
High Temperature ◽  
Oxidation Resistance ◽  
High Temperature Oxidation ◽  
Composite Coatings ◽  
Tube Steel ◽  
Boiler Tube ◽  
Alumina Coatings ◽  
Temperature Oxidation ◽  
Content Type ◽  
Boiler Tube Steel

Purpose This paper aims to discuss that a conventional Al2O3, 1.5 Wt.% carbon nanotubes (CNTs)-Al2O3, 2 Wt.% CNTs-Al2O3 and 4 Wt.% CNTs-Al2O3 composite coatings were deposited with the help of Plasma spray process. Design/methodology/approach To better understand the effect of CNT reinforcement on oxidation resistance, high-temperature oxidation behaviour of conventional Al2O3, 1.5 Wt.% CNTs-Al2O3, 2 Wt.% CNTs-Al2O3 and 4 Wt.% CNTs-Al2O3 composite coatings at 900°C was compared with the performance of the uncoated ASME-SA213-T11 boiler tube steel substrate. Findings The results showed that the CNT-reinforced alumina coatings exhibited better oxidation resistance and thermal stability than uncoated ASME-SA213-T11 boiler tube steel. The coated steel substrates had a lower mass gain rate than the substrate after different oxidation times. Originality/value Limited literature is available where the CNT have been reinforced into the composite alloy powders and has been thermally spray-deposited for various surface engineering applications. This research showed that with the increase in the percentage of CNTs into the alloy powder mixture, there is a significant reduction in weight gain and hence higher resistance to oxidation.