Synergistic effect of nano calcium carbonate (NCC)/carbon black (CB) on the cure characteristics and physico-mechanical properties of NR/SBR blends

2017 ◽  
Author(s):  
Siti Nur Liyana Mamauod ◽  
Ahmad Zafir Romli ◽  
Mohd Ismail Rifdi Rizuan
Keyword(s):  
Mechanical Properties ◽  
Calcium Carbonate ◽  
Carbon Black ◽  
Synergistic Effect ◽  
Cure Characteristics

Influence of Filler Types on Mechanical Properties and Cure Characteristics of Natural Rubber Composites

2011 ◽  
Vol 264-265 ◽  
pp. 646-651 ◽  
Author(s):  
Wittawat Wongsorat ◽  
Nitinat Suppakarn ◽  
Kasama Jarukumjorn
Keyword(s):  
Mechanical Properties ◽  
Calcium Carbonate ◽  
Carbon Black ◽  
Natural Rubber ◽  
Sisal Fiber ◽  
Maximum Torque ◽  
Cure Characteristics ◽  
Roll Mill ◽  
Fiber Treatment ◽  
Cure Time

Natural rubber (NR) was reinforced with three types of filler: carbon black, calcium carbonate, and sisal fiber. NR composites were prepared on a two-roll mill. Filler content was 20 phr. Mechanical properties and cure characteristics of NR composites were studied. All NR composites had higher maximum torque than NR. NR filled with carbon black showed the highest maximum torque. However, scorch time and cure time of the NR composites were not much affected by filler types. In addition, influence of fiber treatment (alkalization) on mechanical properties and cure characteristics of sisal fiber-NR composites was investigated. Alkali treated sisal fiber-NR composite exhibited higher tensile properties and hardness than untreated sisal fiber- NR composite due to improved adhesion between the fiber and NR matrix. Moreover, alkali treated sisal fiber-NR composite had superior specific modulus and strength than NR composites filled with carbon black and calcium carbonate.

scholarly journals Influence of filler system on the cure characteristics and mechanical properties of butyl reclaimed rubber

BioResources ◽  
2020 ◽  
Vol 15 (3) ◽  
pp. 6045-6060
Author(s):  
Zafirah Zainal Abidin ◽  
Siti Nur Liyana Mamauod ◽  
Siti Salina Sarkawi ◽  
Nurshamimi Shahirah Binti Saimi
Keyword(s):  
Mechanical Properties ◽  
Calcium Carbonate ◽  
Carbon Black ◽  
Crosslink Density ◽  
Rubber Content ◽  
Elongation At Break ◽  
Cure Characteristics ◽  
Compression Set ◽  
Roll Mill ◽  
Mooney Viscosity

This research aimed to elucidate the effect of black and non-black filler systems on the cure characteristics and mechanical properties of butyl reclaimed rubber (BRR). In this study, BRR800 was the BRR investigated. Since reclaimed rubber is not entirely 100% rubber, actually being a mixture of rubber, carbon black, oil, zinc oxide, stearic acid and other compounding ingredients used in the original compounds, the reclaimed rubber content in each system was fixed at 161 parts per hundred (pphr). Each mixture was mixed using a two-roll mill. The fillers used in this study were carbon black and calcium carbonate. The Mooney viscosity, cure characteristics, crosslink density, and mechanical properties, such as hardness, abrasion resistance, compression set, tear strength, rebound resilience, and the tensile properties of the vulcanizates were investigated. The results showed that the Mooney viscosity of BRR800 filled with carbon black was increased effectively and had a faster curing time and higher crosslink density than BRR filled with calcium carbonate. In addition, except for compression set and elongation at break, the mechanical properties of BRR800 with a black filler system were higher than those of BRR800 with a non-black filler system.

Characterization of Snap-On Calf Nipple Product and Development of its Compound Formulation Based on Natural Rubber

2017 ◽  
Vol 744 ◽  
pp. 282-287
Author(s):  
Sarawut Prasertsri ◽  
Sansanee Srichan
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Calcium Carbonate ◽  
Carbon Black ◽  
Natural Rubber ◽  
Soxhlet Extraction ◽  
Rubber Compound ◽  
Rubber Compounds ◽  
Rubber Component

This research aimed to develop the formulation of natural rubber filled with carbon black, silica and calcium carbonate for rubber calf nipple application. The reverse engineering was performed on the calf nipple product to analyze the rubber type and component by using Soxhlet extraction, thermogravimetric analysis (TGA) and Fourier transform infrared spectroscopy (FTIR) techniques. Furthermore, mechanical properties were examined to act as benchmark for the rubber compound design. The results showed that rubber component in the nipple product was natural rubber, whereas two filler types revealed as carbon black and calcium carbonate with 10 and 35 of the total weight. In addition, rubber nipple showed the hardness of 46±1 Shore A and tensile strength of 5.3±0.60 MPa. From the investigation of the properties of developed rubber compounds in this work, it was found that the mechanical properties depended on type and content of filler. The required mechanical properties of vulcanizates were achieved at 20 phr of carbon black (N330), 20 phr of silica and 120 phr of calcium carbonate.

Comparison of Reinforcing Efficiency between Calcium Carbonate/Carbon Black and Calcium Carbonate/Silica Hybrid Filled Natural Rubber Composites

2018 ◽  
Vol 382 ◽  
pp. 94-98 ◽  
Author(s):  
Sarawut Prasertsri ◽  
Chaiwute Vudjung ◽  
Wunchai Inthisaeng ◽  
Sansanee Srichan ◽  
Kanchana Sapprasert ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Calcium Carbonate ◽  
Carbon Black ◽  
Natural Rubber ◽  
Hybrid System ◽  
Hybrid Composites ◽  
Strength Increase ◽  
Hybrid Filler ◽  
Carbonate Carbon ◽  
Cure Time

The present research aimed to develop natural rubber (NR) hybrid composites reinforced with calcium carbonate/carbon black (CC/CB) and calcium carbonate/silica (CC/SC). The influence of CC/CB and CC/SC with various filler ratios (120/0, 90/5, 60/10, 30/15 and 0/20) on cure characteristics and mechanical properties of the vulcanizates was investigated and their reinforcing efficiency was compared. It has been found that incorporation of CB in the hybrid filler decreases the scorch time and cure time but increases crosslink density, whereas the incorporation of silica showed cure retardation. As CB or SC content increases, stiffness, tensile strength and tear strength increase, while elongation at break and compression set decrease. Scanning electron microscopy studies also reveal poor filler dispersion and poor adhesion between filler particles and matrix in the vulcanizates with increasing in CC content in a weight filler ratio which causes inferior mechanical properties. Incorporation of CB or SC content enhanced the mechanical properties of the vulcanizates, where CC/CB hybrid system exhibited higher reinforcing efficiency compared with CC/SC hybrid system.

scholarly journals Synergistic effect of CB and GO/CNT hybrid fillers on the mechanical properties and fatigue behavior of NR composites

RSC Advances ◽  
2018 ◽  
Vol 8 (19) ◽  
pp. 10573-10581 ◽  
Author(s):  
Laiyun Wei ◽  
Xuan Fu ◽  
Mingchao Luo ◽  
Zhengtian Xie ◽  
Cheng Huang ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Graphene Oxide ◽  
Carbon Nanotube ◽  
Carbon Black ◽  
Synergistic Effect ◽  
Fatigue Behavior ◽  
Crack Growth Resistance ◽  
Hybrid Fillers ◽  
Superior Mechanical Properties ◽  
Heat Build Up

Graphene oxide (GO) and carbon nanotube (CNT) hybrid fillers were used to replace partial carbon black (CB), and GO/CNT/CB/NR composites were prepared with excellent crack growth resistance, low heat build-up and superior mechanical properties.