ABSTRACTIn an effort to understand the origin of defects earlier found to be present in p–n junctions formed by pulsed laser annealing (PLA) of ion implanted (II) semiconducting GaAs, photoluminescence (PL) studies have been carried out. PL spectra have been obtained at 4K, 77K and 300K, for both n–and p–type GaAs, for laser energy densities 0 ≤ El ≤ 0.6 J/cm2. It is found that PLA of crystalline (c−) GaAs alters the PL spectrum and decreases the PL intensity, corresponding to an increase in density of non-radiative recombination centers with increasing El. The variation of PL intensity with El is found to be different for n– and p–type material. No PL is observed from high dose (1 or 5×1015 ions/cm2 ) Sior Zn-implanted GaAs, either before or after laser annealing. The results suggest that the ion implantation step is primarily responsible for formation of defects associated with the loss of radiative recombination, with pulsed annealing contributing only secondarily.
Near infrared laser annealing of CdTe and in-situ measurement of the evolution of structural and optical properties