Photoluminescence study of N-rich B-doped diamonds grown in NiMnCo solvent before and after annealing

CrystEngComm ◽  
2021 ◽  
Author(s):  
Xinyuan Miao ◽  
Gang Liu ◽  
Hong-an Ma ◽  
Zhuangfei Zhang ◽  
Lijuan Zhou ◽  
...  
Keyword(s):  
High Pressure ◽  
High Temperature ◽  
Single Crystal ◽  
Diamond Single Crystal ◽  
Photoluminescence Study ◽  
Pl Spectra ◽  
Before And After

In this paper, we study PL spectra of N-rich B-doped diamond single crystal grown in NiMnCo solvent, before and after HPHT (high temperature and high pressure) annealing. The PL are...

B–C Bond in Diamond Single Crystal Synthesized with h-BN Additive at High Pressure and High Temperature

2016 ◽  
Vol 33 (2) ◽  
pp. 028101 ◽  
Author(s):  
Li Yong ◽  
Zhou Zhen-Xiang ◽  
Guan Xue-Mao ◽  
Li Shang-Sheng ◽  
Wang Ying ◽  
...  
Keyword(s):  
High Pressure ◽  
High Temperature ◽  
Single Crystal ◽  
Diamond Single Crystal

Defects of diamond single crystal grown under high temperature and high pressure

2013 ◽  
Vol 546 ◽  
pp. 457-460 ◽  
Author(s):  
Qingcai Su ◽  
Jianhua Zhang ◽  
Musen Li
Keyword(s):  
High Pressure ◽  
High Temperature ◽  
Single Crystal ◽  
Diamond Single Crystal

Crystal and powder XRD data of Mg3(PO4)2-III: High-temperature and high-pressure form

1995 ◽  
Vol 10 (4) ◽  
pp. 293-295 ◽  
Author(s):  
F. Brunet ◽  
C. Chopin ◽  
A. Elfakir ◽  
M. Quarton
Keyword(s):  
Crystal Structure ◽  
High Pressure ◽  
High Temperature ◽  
Single Crystal ◽  
Diffraction Pattern ◽  
Structure Refinement ◽  
Powder Xrd ◽  
Single Crystal Structure ◽  
Crystal Structure Refinement ◽  
Pressure Form

A new diffraction pattern of the high-temperature and high-pressure polymorph Mg3(PO4)2-III (PDF 43-500) is given and indexed on the basis of a single-crystal structure refinement. It allows diffractogram indexing of the isostructural high-temperature and high-pressure form of Co3(PO4)2 (PDF 43-499).

Structure of high-temperature nickel alloy ZhS36VI for single-crystal blades of high-pressure turbines

2008 ◽  
Vol 50 (3-4) ◽  
pp. 171-174 ◽  
Author(s):  
V. P. Kuznetsov ◽  
V. P. Lesnikov ◽  
E. V. Moroz ◽  
A. S. Koryakovtsev
Keyword(s):  
High Pressure ◽  
High Temperature ◽  
Single Crystal ◽  
Nickel Alloy ◽  
Alloy Zhs36vi ◽  
High Temperature Nickel Alloy

High-Temperature Fatigue Properties of Single Crystal Superalloys in Air and Hydrogen

2001 ◽  
Author(s):  
Nagaraj K. Arakere
Keyword(s):  
High Pressure ◽  
Shear Stress ◽  
High Temperature ◽  
Fatigue Life ◽  
Single Crystal ◽  
Room Temperature ◽  
Turbine Blades ◽  
The Core ◽  
Blade Tip ◽  
Pressure Hydrogen

Hot section components in high performance aircraft and rocket engines are increasingly being made of single crystal nickel superalloys such as PWA1480, PWA1484, CMSX-4 and Rene N-4 as these materials provide superior creep, stress rupture, melt resistance and thermomechanical fatigue capabilities over their polycrystalline counterparts. Fatigue failures in PWA1480 single crystal nickel-base superalloy turbine blades used in the Space Shuttle Main Engine (SSME) fuel turbopump are discussed. During testing many turbine blades experienced Stage II non-crystallographic fatigue cracks with multiple origins at the core leading edge radius and extending down the airfoil span along the core surface. The longer cracks transitioned from stage II fatigue to crystallographic stage I fatigue propagation, on octahedral planes. An investigation of crack depths on the population of blades as a function of secondary crystallographic orientation (β) revealed that for β = 45+/- 15 degrees tip cracks arrested after some growth or did not initiate at all. Finite element analysis of stress response at the blade tip, as a function of primary and secondary crystal orientation, revealed that there are preferential β orientations for which crack growth is minimized at the blade tip. To assess blade fatigue life and durability extensive testing of uniaxial single crystal specimens with different orientations has been tested over a wide temperature range in air and hydrogen. A detailed analysis of the experimentally determined Low Cycle Fatigue (LCF) properties for PWA1480 and SC 7-14-6 single crystal materials as a function of specimen crystallographic orientation is presented at high temperature (75 F – 1800 F) in high-pressure hydrogen and air. Fatigue failure parameters are investigated for LCF data of single crystal material based on the shear stress amplitudes on the 24 octahedral and 6 cube slip systems for FCC single crystals. The max shear stress amplitude [Δτmax] on the slip planes reduces the scatter in the LCF data and is found to be a good fatigue damage parameter, especially at elevated temperatures. The parameter Δτmax did not characterize the room temperature LCF data in high-pressure hydrogen well because of the noncrystallographic eutectic failure mechanism activated by hydrogen at room temperature. Fatigue life equations are developed for various temperature ranges and environmental conditions based on power-law curve fits of the failure parameter with LCF test data. These curve fits can be used for assessing blade fatigue life.

Sign in / Sign up

Export Citation Format

Share Document