Controllable synthesis of NiO/Ni3S2 hybrid arrays as efficient electrocatalysts for water splitting

2018 ◽  
Vol 42 (22) ◽  
pp. 18201-18207 ◽  
Author(s):  
Xiaoqiang Du ◽  
Qibin Wang ◽  
Xiaoshuang Zhang
Keyword(s):  
Water Splitting ◽  
Current Density ◽  
Cell Voltage ◽  
Controllable Synthesis ◽  
A Cell ◽  
A Current

NiO/Ni3S2 affords a current density of 10 mA cm−2 in 1.0 M KOH at a cell voltage of 1.59 V, i.e., comparable to the commercial 20 wt% IrO2/C–40 wt% Pt/C couple (1.55 V at 10 mA cm−2).

Controllable synthesis of Cu–Ni–M (M = S, P and Se) hybrid nanoarrays for efficient water splitting reaction

2021 ◽  
Author(s):  
Nannan Chen ◽  
Yanhong Wang ◽  
Xiaoqiang Du ◽  
Xiaoshuang Zhang
Keyword(s):  
Water Splitting ◽  
Current Density ◽  
Cell Voltage ◽  
Controllable Synthesis ◽  
A Cell ◽  
A Current

The results demonstrate that Cu–Ni–S/NF//Cu–Ni–P/NF pairs show superior water splitting performance with only requiring a cell voltage of 1.50 V to achieve a current density of 20 mA cm−2.

An advanced and highly efficient Ce assisted NiFe-LDH electrocatalyst for overall water splitting

2020 ◽  
Vol 4 (1) ◽  
pp. 312-323 ◽  
Author(s):  
Harsharaj S. Jadhav ◽  
Animesh Roy ◽  
Bezawit Z. Desalegan ◽  
Jeong Gil Seo
Keyword(s):  
Water Splitting ◽  
Current Density ◽  
Room Temperature ◽  
Cell Voltage ◽  
Highly Efficient ◽  
Overall Water Splitting ◽  
A Cell ◽  
A Current

A room-temperature synthesized NiFeCe2 electrocatalyst delivered a current density of 10 mA cm−2 at a cell voltage of 1.59 V when used as the electrolyzer.

Design and synthesis of integrally structured Ni3N nanosheets/carbon microfibers/Ni3N nanosheets for efficient full water splitting catalysis

2017 ◽  
Vol 5 (19) ◽  
pp. 9377-9390 ◽  
Author(s):  
Tingting Liu ◽  
Mian Li ◽  
Chuanlai Jiao ◽  
Mehboob Hassan ◽  
Xiangjie Bo ◽  
...  
Keyword(s):  
Water Splitting ◽  
Current Density ◽  
Cell Voltage ◽  
Electrolysis Cell ◽  
Design And Synthesis ◽  
A Cell ◽  
Carbon Microfibers ◽  
A Current

A (−) Ni3N/CMFs/Ni3N‖Ni3N/CMFs/Ni3N (+) electrolysis cell requires a cell voltage of only 1.65 V to achieve a current density of 20 mA cm−2.

Oxide/sulfide-based hybrid arrays as robust electrocatalysts for water splitting

2018 ◽  
Vol 47 (30) ◽  
pp. 10273-10280 ◽  
Author(s):  
Xiaoqiang Du ◽  
Qibin Wang ◽  
Yu Li ◽  
Xiaoshuang Zhang
Keyword(s):  
Water Splitting ◽  
Current Density ◽  
Cell Voltage ◽  
A Cell ◽  
A Current

NiCo2O4/Ni3S2 affords a current density of 10 mA cm−2 in 1.0 M KOH at a cell voltage of 1.58 V, i.e., comparable to that of the commercial 20 wt% IrO2/C–40 wt% Pt/C couple (1.52 V at 10 mA cm−2).

A self-supported amorphous Ni–P alloy on a CuO nanowire array: an efficient 3D electrode catalyst for water splitting in alkaline media

2018 ◽  
Vol 54 (19) ◽  
pp. 2393-2396 ◽  
Author(s):  
Bing Chang ◽  
Shuai Hao ◽  
Zhixiang Ye ◽  
Yingchun Yang
Keyword(s):  
Water Splitting ◽  
Nanowire Array ◽  
Cell Voltage ◽  
Alkaline Media ◽  
Core Shell ◽  
Alkaline Water ◽  
A Cell ◽  
Cuo Nanowire ◽  
A Current ◽  
3D Electrode

An amorphous Ni–P alloy shell electrodeposited on a CuO nanowire array to synergistically boost the catalytic activity toward alkaline water splitting is reported, and this core@shell CuO@Ni–P nanowire array is durable with a cell voltage of only 1.71 V reaching a current density of 30 mA cm−2 using a two-electrode configuration in an alkaline water electrolyzer.

Construction of a MnCo2O4@NiyMx (S and P) crosslinked network for efficient electrocatalytic water splitting

CrystEngComm ◽  
2019 ◽  
Vol 21 (47) ◽  
pp. 7293-7302 ◽  
Author(s):  
Xiaoqiang Du ◽  
Jianpeng Fu ◽  
Xiaoshuang Zhang
Keyword(s):  
Water Splitting ◽  
Current Density ◽  
Cell Voltage ◽  
A Current

Using MnCo2O4@Ni3S2 as a bifunctional water splitting catalyst, an overpotential of ∼370 mV is obtained at a very low cell voltage of 1.60 V with a current density of 10 mA cm−2 in 1.0 M KOH.

Cu–Co–M arrays on Ni foam as monolithic structured catalysts for water splitting: effects of co-doped S-P

2019 ◽  
Vol 48 (4) ◽  
pp. 1322-1331 ◽  
Author(s):  
Xiaoqiang Du ◽  
Qizhao Shao ◽  
Xiaoshuang Zhang
Keyword(s):  
Water Splitting ◽  
Current Density ◽  
Cell Voltage ◽  
Ni Foam ◽  
Structured Catalysts ◽  
A Current ◽  
Co Doped

Using Cu–Co–P-S as a bifunctional water-splitting catalyst, overpotential of ∼320 mV is obtained at a very low cell voltage of 1.55 V with a current density of 20 mA cm−2 in 1.0 M KOH.

Photothermal coupling electrolysis on Ni–W–B toward practical overall water splitting

2019 ◽  
Vol 7 (20) ◽  
pp. 12440-12445 ◽  
Author(s):  
Weiju Hao ◽  
Renbing Wu ◽  
Hongyuan Yang ◽  
Yanhui Guo
Keyword(s):  
Water Splitting ◽  
Current Density ◽  
Cell Voltage ◽  
Photothermal Effect ◽  
Carbon Cloth ◽  
Cell Temperature ◽  
Overall Water Splitting ◽  
A Current

An overall water splitting device assembled using a photothermal effect coupled Ni–W–B/carbon cloth electrode could deliver a current density of 25 mA cm−2 at an ultralow cell voltage of 1.524 V without heating the whole system, which is comparable to its performance at an elevated cell temperature of 50 °C.

Interfacial Engineering for Design of Novel 2D Cobalt Sulfide-Mxene Heterostructured Catalyst Towards Alkaline Water Splitting

2021 ◽  
Author(s):  
Phan Khanh Linh Tran ◽  
Min Sung Kim ◽  
Thanh Hai Nguyen ◽  
Thanh D Tran ◽  
Nam Hoon Kim ◽  
...  
Keyword(s):  
Water Splitting ◽  
Three Dimensional ◽  
Cell Voltage ◽  
Catalytic Performance ◽  
Cobalt Sulfide ◽  
Current Response ◽  
Interfacial Engineering ◽  
A Cell ◽  
Kinetics Of ◽  
A Current

Abstract In this work, we used an interfacial engineering method to investigate a novel hybrid of two-dimensional cobalt sulfide-Mxene (2D CoS-Mo2TiC2) heterostructure supported by a three-dimensional foam substrate. The modification electronic properties caused by unique interfacial interactions resulted in a significant increase in the number of electroactive sites and charge transfer ability, thereby accelerating kinetics of hydrogen evolution reaction (HER) and oxygen evolution reaction (OER) in an alkaline medium. The catalyst required overpotential of 248.2 and 310 mV at a current response of 50 mA cm-2 for HER and OER, respectively, along with a remarkable stability. In addition, a two-electrode electrolyzer derived from the developed 2D CoS-Mo2TiC2 catalyst showed a cell voltage of 1.74 V at 10 mA cm-2 and a good stability during 25 h continuous operation. The achieved results were associated to the formation of a unique interfacial heterostructure with the strong interaction between two material phases, which effectively modified electronic structure and surface chemistry, thereby leading to the enhancement of catalytic performance. The study offered a potential route to synthesize new catalyst for green hydrogen production via water splitting.

Controlled synthesis of Ni(OH)2/Ni3S2hybrid nanosheet arrays as highly active and stable electrocatalysts for water splitting

2018 ◽  
Vol 6 (16) ◽  
pp. 6938-6946 ◽  
Author(s):  
Xiaoqiang Du ◽  
Zhi Yang ◽  
Yu Li ◽  
Yaqiong Gong ◽  
Min Zhao
Keyword(s):  
Water Splitting ◽  
Current Density ◽  
Cell Voltage ◽  
Controlled Synthesis ◽  
Highly Active ◽  
Nanosheet Arrays ◽  
A Current

Using Ni(OH)2/Ni3S2-12h as a bifunctional water splitting catalyst, with an overpotential of ∼340 mV, which is obtained at a very low cell voltage of 1.57 V with a current density of 10 mA cm−2in 1.0 M KOH.

Sign in / Sign up

Export Citation Format

Share Document