Enhancement of thermoelectric properties by Na doping in Te-free p-type AgSbSe2

2015 ◽  
Vol 44 (3) ◽  
pp. 1046-1051 ◽  
Author(s):  
Songting Cai ◽  
Zihang Liu ◽  
Jianyong Sun ◽  
Rui Li ◽  
Weidong Fei ◽  
...  
Keyword(s):  
Thermal Conductivity ◽  
Carrier Concentration ◽  
Thermoelectric Properties ◽  
Point Defects ◽  
Power Factor ◽  
Stacking Faults ◽  
Na Doping ◽  
P Type

Na substituting Sb in the AgSbSe2 not only improves the power factor caused by the enhanced carrier concentration, but also decreases the thermal conductivity due to point defects, nanoscale stacking faults and Na-rich precipitate. Consequently, a high ZT value of 0.92 is achieved in the AgSb0.99Na0.01Se2 sample.

scholarly journals Improving the Thermoelectric Properties of the Half-Heusler Compound VCoSb by Vanadium Vacancy

Materials ◽  
2019 ◽  
Vol 12 (10) ◽  
pp. 1637 ◽  
Author(s):  
Lihong Huang ◽  
Junchen Wang ◽  
Xiaobo Mo ◽  
Xiaobo Lei ◽  
Sude Ma ◽  
...  
Keyword(s):  
Thermal Conductivity ◽  
Seebeck Coefficient ◽  
Carrier Concentration ◽  
Thermoelectric Properties ◽  
Power Factor ◽  
Secondary Phase ◽  
Thermoelectric Performance ◽  
Heusler Compound

The effects of V vacancy on the thermoelectric performance of the half-Heusler compound VCoSb have been investigated in this study. A certain amount of CoSb secondary phase is generated in the VCoSb matrix when the content of V vacancy is more than 0.1 at%. According to the results, a ZT value of 0.6, together with a power factor of 29 μW cm−1 K−2 at 873 K, were achieved for the nonstoichiometric sample V0.9CoSb. This proved that moderate V vacancy could improve the thermoelectric (TE) properties of VCoSb. The noticeable improvements are mainly owing to the incremental Seebeck coefficient, which may benefit from the optimized carrier concentration. However, too much V vacancy will result in more CoSb impurity and deteriorate the TE performances of VCoSb owing to the increased thermal conductivity.

Fabrication and Thermoelectric Properties of p-Type Bi1Sb4Te7.5 Alloy Doped with Fe3O4

2006 ◽  
Vol 510-511 ◽  
pp. 1086-1089 ◽  
Author(s):  
Wang Kee Min ◽  
Chang Ho Lee ◽  
Yong Ho Park ◽  
Ik Min Park
Keyword(s):  
Thermal Conductivity ◽  
Electrical Conductivity ◽  
Mechanical Alloying ◽  
Seebeck Coefficient ◽  
Thermoelectric Properties ◽  
Power Factor ◽  
Hall Effect Measurement ◽  
Small Addition ◽  
Z Value ◽  
P Type

We investigated the effects of Fe3O4 (0~0.1 wt.%) on the thermoelectric properties of Bi1Sb4Te7.5 alloy prepared by mechanical alloying process. The Seebeck coefficient increased with Fe3O4 content, but the power factor decreased with Fe3O4 content because of the decreased electrical conductivity. The thermal conductivity decreased with Fe3O4. The carrier concentration measured by the Hall effect measurement decreased with Fe3O4. The thermal conductivity of 0.1 wt.% Fe3O4 alloy was 0.814 W/Km, 20%lower than that of Fe3O4 free alloy. As a result, the small addition of Fe3O4 improved the Z value owing to the decreased thermal conductivity by adding Fe3O4. The Z value of 0.01 wt.% Bi1Sb4Te7.5 alloy was 3.1×10-3 /K, the highest value among the prepared alloys.

Enhanced Thermoelectric Properties of FeSbx Nanocomposites Through Stoichiometric Adjustment

2012 ◽  
Vol 1456 ◽  
Author(s):  
Mani Pokharel ◽  
Huaizhou Zhao ◽  
Kevin Lukas ◽  
Zhifeng Ren ◽  
Cyril Opeil
Keyword(s):  
Thermal Conductivity ◽  
Electrical Resistivity ◽  
Seebeck Coefficient ◽  
Carrier Concentration ◽  
Thermoelectric Properties ◽  
Power Factor ◽  
Hall Coefficient

ABSTRACTThe Seebeck coefficient, electrical resistivity, thermal conductivity and Hall coefficient of FeSbx (x = 2.04, 2.00, and 1.96) nanocomposites hot pressed at 300 °C were measured. The power factor of FeSb1.96 was increased by 105% compared to FeSb2. Hall coefficient measurements revealed a decreased carrier concentration and increased mobility in FeSb1.96 with an overall enhancement in ZTof 45% in FeSb1.96 .

scholarly journals Electronic Transport and Thermoelectric Properties of Te-Doped Tetrahedrites Cu12Sb4-yTeyS13

2021 ◽  
Vol 59 (8) ◽  
pp. 560-566
Author(s):  
Sung-Gyu Kwak ◽  
Go-Eun Lee ◽  
Il-Ho Kim
Keyword(s):  
Thermal Conductivity ◽  
Mechanical Alloying ◽  
Carrier Concentration ◽  
Power Factor ◽  
Hot Pressing ◽  
Hole Concentration ◽  
Secondary Phases ◽  
Low Thermal Conductivity ◽  
Seebeck Coefficients ◽  
P Type

Tetrahedrite is a promising thermoelectric material mainly due to its low thermal conductivity, a consequence of its complicated crystal structure. However, tetrahedrite has a high hole concentration; therefore, optimizing carrier concentration through doping is required to maximize the power factor. In this study, Te-doped tetrahedrites Cu12Sb4-yTeyS13 (0.1 ≤ y ≤ 0.4) were prepared using mechanical alloying and hot pressing. The mechanical alloying successfully prepared the tetrahedrites doped with Te at the Sb sites without secondary phases, and the hot pressing produced densely sintered bodies with a relative density >99.7%. As the Te content increased, the lattice constant increased from 1.0334 to 1.0346 nm, confirming the successful substitution of Te at the Sb sites. Te-doped tetrahedrites exhibited p-type characteristics, which were confirmed by the positive signs of the Hall and Seebeck coefficients. The carrier concentration decreased but the mobility increased with Te content. The electrical conductivity was relatively constant at 323–723 K, and decreased with Te substitution from 2.6 × 104 to 1.6 × 104 Sm-1 at 723 K. The Seebeck coefficient increased with temperature and Te content, achieving values of 184–204 μVK-1 at 723 K. The thermal conductivity was <1.0 Wm-1K-1, and decreased with increasing Te content. Cu12Sb3.9Te0.1S13 exhibited the highest dimensionless figure of merit (ZT = 0.80) at 723 K, achieving a high power factor (0.91 mWm-1K-2) and a low thermal conductivity (0.80 Wm-1K-1).

High Thermoelectric Performance of p-Type Bi0.5Sb1.5Te3+xTe Crystals Prepared via Gradient Freezing

2012 ◽  
Vol 621 ◽  
pp. 167-171
Author(s):  
Tao Hua Liang ◽  
Shi Qing Yang ◽  
Zhi Chen ◽  
Qing Xue Yang
Keyword(s):  
Thermal Conductivity ◽  
Seebeck Coefficient ◽  
Carrier Concentration ◽  
Thermoelectric Properties ◽  
Figure Of Merit ◽  
Room Temperature ◽  
Thermoelectric Performance ◽  
Thermoelectric Figure Of Merit ◽  
Thermoelectric Figure ◽  
P Type

p-type Bi0.5Sb1.5Te3+xTe thermoelectric crystals with various percentages of Te (x = 0.00 wt.%–3.00 wt.%) excess were prepared by the gradient freeze method. By doping with different Te contents, anti-site defects, Te vacancies and hole carrier concentrations were controlled. The Seebeck coefficient, resistivity, thermal conductivity, carrier concentration, and mobility were measured. The relationships between the Te content and thermoelectric properties were investigated in detail. The results suggested that the thermoelectric figure of merit ZT of the Bi0.5Sb1.5Te3+0.09wt.% crystals was 1.36 near room temperature, the optimum carrier concentration was 1.25 × 1019 cm-3, and the mobility was 1480 cm2 V-1 S-1, respectively.

Thermoelectric Properties of PbSr(Se,Te)-Based Low Dimensional Structures

2000 ◽  
Vol 626 ◽  
Author(s):  
Harald Beyer ◽  
Joachim Nurnus ◽  
Harald Böttner ◽  
Armin Lambrecht ◽  
Lothar Schmitt ◽  
...  
Keyword(s):  
Thermal Conductivity ◽  
Thermoelectric Properties ◽  
Power Factor ◽  
Evaluation Method ◽  
Interband Transition ◽  
Multiple Quantum Well ◽  
Calculated Data ◽  
Multiple Quantum ◽  
Ir Transmission ◽  
Low Dimensional

ABSTRACTThermoelectric properties of low dimensional structures based on PbTe/PbSrTe-multiple quantum-well (MQW)-structures with regard to the structural dimensions, doping profiles and levels are presented. Interband transition energies and barrier band-gap are determined from IR-transmission spectra and compared with Kronig-Penney calculations. The influence of the data evaluation method to obtain the 2D power factor will be discussed. The thermoelectrical data of our layers show a more modest enhancement in the power factor σS2 compared with former publications and are in good agreement with calculated data from Broido et al. [5]. The maximum allowed doping level for modulation doped MQW structures is determined. Thermal conductivity measurements show that a ZT enhancement can be achieved by reducing the thermal conductivity due to interface scattering. Additionally promising lead chalcogenide based superlattices for an increased 3D figure of merit are presented.

Layered tellurides: stacking faults induce low thermal conductivity in the new In2Ge2Te6 and thermoelectric properties of related compounds

2017 ◽  
Vol 5 (36) ◽  
pp. 19406-19415 ◽  
Author(s):  
Robin Lefèvre ◽  
David Berthebaud ◽  
Oleg Lebedev ◽  
Olivier Pérez ◽  
Célia Castro ◽  
...  
Keyword(s):  
Thermal Conductivity ◽  
High Temperature ◽  
Thermoelectric Properties ◽  
Stacking Faults ◽  
Layered Compound ◽  
Low Thermal Conductivity ◽  
Related Compounds

A new ternary layered compound In2Ge2Te6, belonging to the hexatellurogermanate family has been synthesized from the reaction of appropriate amounts of the pure elements at high temperature in sealed silica tubes.

Thermoelectric Properties of n-type (Bi2Se3)x(Bi2Te3)1-x Crystals Prepared by Zone Melting

2008 ◽  
Vol 368-372 ◽  
pp. 547-549
Author(s):  
Jun Jiang ◽  
Ya Li Li ◽  
Gao Jie Xu ◽  
Ping Cui ◽  
Li Dong Chen
Keyword(s):  
Thermal Conductivity ◽  
Electrical Conductivity ◽  
Seebeck Coefficient ◽  
Carrier Concentration ◽  
Thermoelectric Properties ◽  
Figure Of Merit ◽  
Zone Melting ◽  
Chemical Compositions ◽  
Melting Method ◽  
Temperature Range

In the present study, n-type (Bi2Se3)x(Bi2Te3)1-x crystals with various chemical compositions were fabricated by the zone melting method. Thermoelectric properties, including Seebeck coefficient (α), electrical conductivity (σ) and thermal conductivity (κ), were measured in the temperature range of 300-500 K. The influence of the variations of Bi2Te3 and Bi2Se3 content on thermoelectric properties was studied. The increase of Bi2Se3 content (x) caused an increase in carrier concentration and thus an increase of σ and a decrease of α. The maximum figure of merit (ZT = α2σT/κ) of 0.87 was obtained at about 325 K for the composition of 93%Bi2Te3-7%Bi2Se3 with doping TeI4.

Influence of GeP precipitates on the thermoelectric properties of P-type GeTe and Ge0.9−xPxSb0.1Te compounds

CrystEngComm ◽  
2018 ◽  
Vol 20 (41) ◽  
pp. 6449-6457 ◽  
Author(s):  
J. Rajeev Gandhi ◽  
Raja Nehru ◽  
Sheng-Ming Chen ◽  
Raman Sankar ◽  
Khasim Saheb Bayikadi ◽  
...  
Keyword(s):  
Thermoelectric Properties ◽  
Point Defects ◽  
Secondary Phase ◽  
Rich Phase ◽  
System P ◽  
Scattering Effects ◽  
P Type

The incorporation of P in GST forms the secondary GeP rich phase. The presence of secondary phase and point defects (Sb and P) enhanced the additional scattering effects in the system.

Synergistic optimization of carrier transport and thermal conductivity in Sn-doped Cu2Te

2018 ◽  
Vol 6 (39) ◽  
pp. 18928-18937 ◽  
Author(s):  
Yuchong Qiu ◽  
Ying Liu ◽  
Jinwen Ye ◽  
Jun Li ◽  
Lixian Lian
Keyword(s):  
Thermal Conductivity ◽  
Fermi Level ◽  
Carrier Concentration ◽  
Power Factor ◽  
Carrier Transport ◽  
Lone Pair ◽  
Thermoelectric Performance ◽  
Degenerate Semiconductors ◽  
Lone Pair Electrons

Doping Sn into the Cu2Te lattice can synergistically enhance the power factor and decrease thermal conductivity, leading to remarkably optimized zTs. The lone pair electrons from the 5s orbital of Sn can increase the DOS near the Fermi level of Cu2Te to promote PF and reduce κe by decreasing the carrier concentration. This study explores a scalable strategy to optimize the thermoelectric performance for intrinsically highly degenerate semiconductors.

Sign in / Sign up

Export Citation Format

Share Document