Investigation of surface characteristics evolution and laser damage performance of fused silica during ion-beam sputtering

2016 ◽  
Vol 58 ◽  
pp. 151-157 ◽  
Author(s):  
Mingjin Xu ◽  
Yifan Dai ◽  
Lin Zhou ◽  
Feng Shi ◽  
Wen Wan ◽  
...  
Keyword(s):  
Ion Beam ◽  
Surface Characteristics ◽  
Fused Silica ◽  
Laser Damage ◽  
Ion Beam Sputtering ◽  
Beam Sputtering

Optical characterization and laser damage of fused silica optics after ion beam sputtering

Optik ◽  
2014 ◽  
Vol 125 (2) ◽  
pp. 756-760 ◽  
Author(s):  
Zhonghua Yan ◽  
Wei Liao ◽  
Yunfei Zhang ◽  
Xia Xiang ◽  
Xiaodong Yuan ◽  
...  
Keyword(s):  
Ion Beam ◽  
Optical Characterization ◽  
Fused Silica ◽  
Laser Damage ◽  
Ion Beam Sputtering ◽  
Beam Sputtering

scholarly journals Investigation of laser-induced damage threshold improvement mechanism during ion beam sputtering of fused silica

2017 ◽  
Vol 25 (23) ◽  
pp. 29260 ◽  
Author(s):  
Mingjin Xu ◽  
Feng Shi ◽  
Lin Zhou ◽  
Yifan Dai ◽  
Xiaoqiang Peng ◽  
...  
Keyword(s):  
Ion Beam ◽  
Damage Threshold ◽  
Fused Silica ◽  
Ion Beam Sputtering ◽  
Beam Sputtering ◽  
Laser Induced Damage

Evolution mechanism of surface roughness during ion beam sputtering of fused silica

2018 ◽  
Vol 57 (20) ◽  
pp. 5566 ◽  
Author(s):  
Mingjin Xu ◽  
Yifan Dai ◽  
Lin Zhou ◽  
Xiaoqiang Peng ◽  
Shaoshan Chen ◽  
...  
Keyword(s):  
Surface Roughness ◽  
Ion Beam ◽  
Fused Silica ◽  
Ion Beam Sputtering ◽  
Evolution Mechanism ◽  
Beam Sputtering

Laser Damage Resistant Ta2O5/HfO2/SiO2 Multilayer Mirrors by Ion Beam Sputtering

2015 ◽  
Author(s):  
D. Schiltz ◽  
D. Patel ◽  
L. Emmert ◽  
C. Baumgarten ◽  
B. Reagan ◽  
...  
Keyword(s):  
Ion Beam ◽  
Laser Damage ◽  
Ion Beam Sputtering ◽  
Multilayer Mirrors ◽  
Beam Sputtering

Researches on formation mechanism of ultra-smooth surface during ion beam sputtering of fused silica

Optik ◽  
2019 ◽  
Vol 179 ◽  
pp. 957-964 ◽  
Author(s):  
Wenlin Liao ◽  
Xuqing Nie ◽  
Zongzheng Liu ◽  
Xutao Nie ◽  
Wen Wan
Keyword(s):  
Formation Mechanism ◽  
Smooth Surface ◽  
Ion Beam ◽  
Fused Silica ◽  
Ion Beam Sputtering ◽  
Beam Sputtering

Laser damage resistance of hafnia thin films deposited by electron beam deposition, reactive low voltage ion plating, and dual ion beam sputtering

2007 ◽  
Vol 47 (13) ◽  
pp. C107 ◽  
Author(s):  
Laurent Gallais ◽  
Jérémie Capoulade ◽  
Jean-Yves Natoli ◽  
Mireille Commandré ◽  
Michel Cathelinaud ◽  
...  
Keyword(s):  
Low Voltage ◽  
Ion Beam ◽  
Laser Damage ◽  
Ion Beam Sputtering ◽  
Damage Resistance ◽  
Ion Plating ◽  
Electron Beam Deposition ◽  
Beam Sputtering ◽  
Dual Ion Beam Sputtering ◽  
Beam Deposition