Investigation on the influence of heat treatment on Inconel 718 fabricated by selective laser melting: Microstructure and high temperature tensile property

2021 ◽  
Vol 61 ◽  
pp. 35-45
Author(s):  
Qing Teng ◽  
Shuai Li ◽  
Qingsong Wei ◽  
Yusheng Shi
Keyword(s):  
Heat Treatment ◽  
High Temperature ◽  
Selective Laser Melting ◽  
Tensile Property ◽  
Inconel 718 ◽  
Laser Melting ◽  
High Temperature Tensile

Effects of Heat Treatment on High Temperature Mechanical Property and Corrosion Resistance of Hastelloy X Manufactured by Selective Laser Melting

NANO ◽  
2021 ◽  
Author(s):  
Qingxia Zhang ◽  
Lingtao Meng ◽  
Xiaotian Yin ◽  
Shenghai Wang ◽  
Yong Liu ◽  
...  
Keyword(s):  
Heat Treatment ◽  
Mechanical Property ◽  
Corrosion Resistance ◽  
High Temperature ◽  
Selective Laser Melting ◽  
Fracture Strain ◽  
Laser Melting ◽  
Hastelloy X ◽  
Mechanical Properties And Corrosion ◽  
High Temperature Tensile

In previous studies, the microstructure, mechanical properties and corrosion resistance of Hastelloy X fabricated by selective laser melting (SLM) have been investigated; however, it is hoped that heat treatment will effect on its properties. Therefore, this study is to discuss heat treatment effect on Hastelloy X fabricated by SLM. It is interestingly found that fracture strain greatly increases with heat treatment, and the yield ratio decreases, which demonstrates the material is more reliable. High temperature tensile behavior is discussed; it is worth mentioning that not only fracture strain of the HT sample increases greatly at 550∘C in comparison with SLM sample, but also ultimate tensile strength increases from 632 MPa to 639 MPa; the results show that the mechanical property can be improved at medium and high temperature by heat treatment. The corrosion resistance of HT sample deteriorates slightly, which can be explained by Cr-rich precipitates. In conclusion, the material after heat treatment is suitable for applications requiring high mechanical reliability and medium and high temperature occasions, but it is not befitting for corrosive environments.

scholarly journals The Relationship of Fracture Mechanism between High Temperature Tensile Mechanical Properties and Particle Erosion Resistance of Selective Laser Melting Ti-6Al-4V Alloy

Metals ◽  
2019 ◽  
Vol 9 (5) ◽  
pp. 501 ◽  
Author(s):  
Jun-Ren Zhao ◽  
Fei-Yi Hung ◽  
Truan-Sheng Lui ◽  
Yu-Lin Wu
Keyword(s):  
Heat Treatment ◽  
High Temperature ◽  
Selective Laser Melting ◽  
Erosion Resistance ◽  
Air Cooling ◽  
Particle Erosion ◽  
Laser Melting ◽  
Erosion Rates ◽  
High Temperature Tensile ◽  
Impact Angles

In this study, selective laser melting (SLM) Ti-6Al-4V is subjected to heat treatment for 4 h at 400 °C, 600 °C, and 800 °C, followed by air cooling. After heat treatment at 400 °C and 600 °C, the ductility was lower (strength increased). This was could be for two reasons: (1) high temperature tensile properties, and (2) particle erosion wear induced phase transformation. Finally, the particle erosion rates of as-SLM Ti-6Al-4V and heat treatment for 4 h at 800 °C (labeled 800-AC) were investigated and compared; the lamellar α + β phases in 800-AC are difficult to destroy with erosion particles, resulting in the erosion resistance of 800-AC being higher than that of the martensitic α’ needles in the as-SLM Ti-6Al-4V at all impact angles (even the hardness of the 800-AC specimen was lower). The as-SLM Ti-6Al-4V alloy needs heat treatment to have better wear resistance.

scholarly journals Effect of Post Processing Heat Treatment Routes on Microstructure and Mechanical Property Evolution of Haynes 282 Ni-Based Superalloy Fabricated with Selective Laser Melting (SLM)

Metals ◽  
2020 ◽  
Vol 10 (5) ◽  
pp. 629
Author(s):  
Anagh Deshpande ◽  
Subrata Deb Nath ◽  
Sundar Atre ◽  
Keng Hsu
Keyword(s):  
Mechanical Properties ◽  
Heat Treatment ◽  
Mechanical Property ◽  
High Temperature ◽  
Selective Laser Melting ◽  
Laser Melting ◽  
Step Heat Treatment ◽  
Microstructure And Mechanical Property ◽  
In Situ Heat Treatment

Selective laser melting (SLM) is one of the most widely used additive manufacturing technologies. Fabricating nickel-based superalloys with SLM has garnered significant interest from the industry and the research community alike due to the excellent high temperature properties and thermal stability exhibited by the alloys. Haynes-282 alloy, a γ′-phase strengthened Ni-based superalloy, has shown good high temperature mechanical properties comparable to alloys like R-41, Waspaloy, and 263 alloy but with better fabricability. A study and comparison of the effect of different heat-treatment routes on microstructure and mechanical property evolution of Haynes-282 fabricated with SLM is lacking in the literature. Hence, in this manuscript, a thorough investigation of microstructure and mechanical properties after a three-step heat treatment and hot isostatic pressing (HIP) has been conducted. In-situ heat-treatment experiments were conducted in a transmission electron microscopy (TEM) to study γ′ precipitate evolution. γ′ precipitation was found to start at 950 °C during in-situ heat-treatment. Insights from the in-situ heat-treatment were used to decide the aging heat-treatment for the alloy. The three-step heat-treatment was found to increase yield strength (YS) and ultimate tensile strength (UTS). HIP process enabled γ′ precipitation and recrystallization of grains of the as-printed samples in one single step.