Effect of engineered cementitious composite on the bond behavior between fiber-reinforced polymer and concrete

2018 ◽  
Vol 184 ◽  
pp. 775-788 ◽  
Author(s):  
Lili Sui ◽  
Minshen Luo ◽  
Kequan Yu ◽  
Feng Xing ◽  
Pengda Li ◽  
...  
Keyword(s):  
Fiber Reinforced Polymer ◽  
Cementitious Composite ◽  
Fiber Reinforced ◽  
Bond Behavior ◽  
Engineered Cementitious Composite ◽  
Reinforced Polymer

Performance of FRP confined and unconfined engineered cementitious composite exposed to seawater

2019 ◽  
Vol 53 (28-30) ◽  
pp. 4285-4304 ◽  
Author(s):  
Alaa Mohammedameen ◽  
Abdulkadir Çevik ◽  
Radhwan Alzeebaree ◽  
Anıl Niş ◽  
Mehmet Eren Gülşan
Keyword(s):  
Mechanical Behaviour ◽  
Mechanical Performance ◽  
Basalt Fiber ◽  
Polymer Materials ◽  
Fiber Reinforced Polymer ◽  
Cementitious Composite ◽  
Fiber Reinforced ◽  
Engineered Cementitious Composite ◽  
Reinforced Polymer ◽  
Seawater Environment

Conventional concrete suffers from brittle failures under mechanical behaviour, and lack of ductility results in the loss of human life and property in earthquake zones. Therefore, the degree of ductility becomes significant in seismic regions. This paper investigates the influence of poly-vinyl alcohol fibers, basalt fiber-reinforced polymer (BFRP) and carbon fiber-reinforced polymer (CFRP) fabrics on the ductility and mechanical performance of low (LCFA) and high (HCFA) calcium fly ash-based engineered cementitious composite concrete. The study also focuses on the mechanical behaviour of the CFRP and BFRP materials using different matrix types exposed to 3.5% seawater environment. Cyclic loading and scanning electron microscopy observations were also performed to see the effect of chloride attack on mechanical performance and ductility of the specimens. In addition, utilization of CFRP and BFRP fabrics as a retrofit material is also evaluated. Results indicated that the degree of ductility and mechanical performance were found to be superior for the CFRP-engineered cementitious composite hybrid specimens under ambient environment, while LCFA-CFRP hybrid specimens showed better performance under seawater environment. The effect of matrix type was also found significant when engineered cementitious composite is used together with fiber-reinforced polymer materials. In addition, both fiber-reinforced polymer materials can be used as a retrofit material under seawater environment.

Experimental study on the behavior of carbon fiber reinforced polymer sheets bonded to concrete

2006 ◽  
Vol 33 (11) ◽  
pp. 1438-1449 ◽  
Author(s):  
Ayman S Kamel ◽  
Alaa E Elwi ◽  
Roger J.J Cheng
Keyword(s):  
Carbon Fiber ◽  
Failure Mechanism ◽  
Test Method ◽  
Fiber Reinforced Polymer ◽  
Carbon Fiber Reinforced Polymer ◽  
Fiber Reinforced ◽  
Bond Behavior ◽  
Cfrp Sheets ◽  
Reinforced Polymer ◽  
Carbon Fiber Reinforced

This paper presents a study on the interfacial behavior of carbon fiber reinforced polymer (CFRP) sheets when applied to concrete members as external reinforcement. Two bond test methods that are detailed in the paper were used in separate test series to study the bond behavior and failure mechanism of CFRP sheets bonded to concrete. A modified push-apart test method was proposed and tested. It was concluded that there existed an effective length beyond which there will be no increase in the ultimate capacity of the joint. An experimental test method to determine the effective bond length was also proposed and tested. The strains at the edge of the CFRP sheets are consistently higher than those at the center. The anchorage requirements for the CFRP sheets were also investigated in this study. Anchor sheets placed at 90° to the primary test sheets and bonded underneath the tested sheet showed better or equivalent overall bond behavior compared with those bonded on top of the tested sheet. The distance at which the anchor sheet is placed from the crack does not appear to change the bond behavior.Key words: bond, concrete, debonding, failure mechanism, carbon fiber reinforced polymer (CFRP) sheets, anchor sheets.