Relationship between fiber orientation/distribution and post-cracking behaviour in ultra-high-performance fiber-reinforced concrete (UHPFRC)

2017 ◽  
Vol 83 ◽  
pp. 66-75 ◽  
Author(s):  
Bo Zhou ◽  
Yuichi Uchida
Keyword(s):  
Reinforced Concrete ◽  
Fiber Orientation ◽  
High Performance ◽  
Orientation Distribution ◽  
Fiber Reinforced Concrete ◽  
Fiber Reinforced ◽  
Fiber Orientation Distribution ◽  
High Performance Fiber

Relationship between Fiber Orientation and Flexural Strength in Ultra-High-Performance Fiber-Reinforced Concrete Panels

2014 ◽  
Vol 629-630 ◽  
pp. 71-78 ◽  
Author(s):  
Bo Zhou ◽  
Yuichi Uchida
Keyword(s):  
Reinforced Concrete ◽  
Flexural Strength ◽  
Fiber Orientation ◽  
High Performance ◽  
Fiber Reinforced Concrete ◽  
Bending Test ◽  
Fiber Reinforced ◽  
Three Point Bending ◽  
Concrete Panels ◽  
High Performance Fiber

In this study, the influence of fiber orientation on the flexural strength of ultra-high-performance fiber-reinforced concrete (UHPFRC) was examined. To this end, a circular UHPFRC panel measuring φ1,200 × 50 mm was cast from its center, and test specimens measuring 50 × 50 × 200 mm with 10 mm notches for three-point bending tests were cut from it with angles of 0, 30, 60 and 90° between the specimen axis and the radial direction of the panel. After the bending test, fiber orientation on the ruptured surfaces of the specimens was observed. The flexural strengths of the specimens cut at angles of 60, 30 and 0° were 80, 40 and 10% of that for the specimen cut at an angle of 90°. It was also found that the flexural strength of specimens cut from a rectangular panel cast from its center point depended on their original positions and orientation within the panel. Similar fiber orientation characteristics were found in the circular and rectangular panels.

Influence of technological factors on the properties of ultra-high-performance fiber reinforced concrete

2020 ◽  
pp. 135-147
Author(s):  
Igor Chilin ◽  
Keyword(s):  
Reinforced Concrete ◽  
High Performance ◽  
Fiber Reinforced Concrete ◽  
Fiber Reinforced ◽  
Technological Factors ◽  
High Performance Fiber

Приведены результаты исследований и выполнена оценка влияния технологических факторов на реологические свойства самоуплотняющихся сталефибробетонных смесей, определены кратковременные и длительные физико-механические и деформативные характеристики сверхвысокопрочного сталефибробетона, включая определение его фактической морозостойкости.

Sign in / Sign up

Export Citation Format

Share Document