Mechanism of surface layer hardening in impact-abrasive wear of high-chromium cast iron

1990 ◽  
Vol 32 (4) ◽  
pp. 278-280 ◽  
Author(s):  
O. S. Komarov ◽  
V. V. Ivashkin ◽  
N. I. Urbanovich
Keyword(s):  
Surface Layer ◽  
Cast Iron ◽  
Abrasive Wear ◽  
High Chromium ◽  
High Chromium Cast Iron ◽  
Surface Layer Hardening ◽  
Chromium Cast Iron

The influence of retained austenite in high chromium cast iron on impact-abrasive wear

Wear ◽  
1990 ◽  
Vol 135 (2) ◽  
pp. 217-226 ◽  
Author(s):  
Tong Jian-Min ◽  
Zhou Yi-Zhong ◽  
Shen Tian-Yi ◽  
Deng Hai-Jin
Keyword(s):  
Cast Iron ◽  
Abrasive Wear ◽  
Retained Austenite ◽  
High Chromium ◽  
High Chromium Cast Iron ◽  
Chromium Cast Iron

Abrasive wear behavior and mechanism of high chromium cast iron

2015 ◽  
Vol 22 (1) ◽  
pp. 84-90 ◽  
Author(s):  
Ting Sun ◽  
Ren-bo Song ◽  
Xu Wang ◽  
Peng Deng ◽  
Chun-jing Wu
Keyword(s):  
Cast Iron ◽  
Abrasive Wear ◽  
Wear Behavior ◽  
High Chromium ◽  
High Chromium Cast Iron ◽  
Abrasive Wear Behavior ◽  
Chromium Cast Iron

scholarly journals Wear Resistance Mechanism of ZTAP/HCCI Composites with a Honeycomb Structure

Metals ◽  
2018 ◽  
Vol 8 (8) ◽  
pp. 588 ◽  
Author(s):  
Mojin Zhou ◽  
Yudong Sui ◽  
Xiaoyu Chong ◽  
YeHua Jiang
Keyword(s):  
Wear Resistance ◽  
Cast Iron ◽  
Abrasive Wear ◽  
Layer Structure ◽  
Resistance Mechanism ◽  
Honeycomb Structure ◽  
Protection Effect ◽  
High Chromium ◽  
High Chromium Cast Iron ◽  
Chromium Cast Iron

The abrasive wear resistance of zirconia toughened alumina (ZTA) ceramic particle reinforced high chromium cast iron (HCCI) composites has been systematically investigated using a moving wedge type of apparatus. The results of three-body abrasive wear show that the wear resistance of the composites with honeycomb is three times higher than that of the high chromium cast iron. The wear resistance of the composites with a honeycomb structure is close to that of the layer structure and is higher than that of the HCCI because the honeycomb wall in the cell honeycomb structure is prominent and because the honeycomb core is depressed. The wear mechanisms of the composites are mainly microcutting and fatigue fractures. The honeycomb structure forms a “macrocosmic shadow protection effect” and a “microcosmic shadow protection effect” to protect each composite and to improve the wear resistance of the composites.

scholarly journals Sintering Preparation of 15 wt% Cr Cast Iron as well as Its Mechanical Properties and Impact Abrasive Wear

2020 ◽  
Author(s):  
Liyang Xiao ◽  
Pingan Xiao ◽  
Liviu Brândușan ◽  
Jinghong Gu ◽  
Zhongtao Li ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Wear Resistance ◽  
Cast Iron ◽  
Impact Toughness ◽  
Abrasive Wear ◽  
Bending Strength ◽  
Sintering Temperature ◽  
High Chromium ◽  
High Chromium Cast Iron ◽  
Chromium Cast Iron

15 wt% Cr sintered High Chromium Cast Iron (HCCI) with full density was successfully prepared by Super-solidus Liquid Phase Sintering (SPLS) technique, with water atomized 15 wt% Cr high chromium cast iron powder as initial materials. Its densification behavior and microstructure evolution in SPLS process and mechanical properties were investigated systematically. Additionally, the impact abrasive wear resistance under different impact energies were also analyzed and compared with another sintered HCCI with 20 wt% Cr. The results indicated that sintering temperature has a strong influence on the sintered alloy’s density, hardness, impact toughness and bending strength. The M7C3 type (M is Cr and Fe) carbides were obviously coarsened as temperature increased and their rod-shaped branches were fully developed at the same time, thereby resulting in carbide network formation in the matrix. The reasonable sintering temperature range was 1195–1205 °C, and the optimum mechanical properties had the hardness of 63.9 HRC, bending strength of 2112.65 MPa and impact toughness of 7.92 J/cm2. What is more important impact abrasive wear test results indicated 15 wt% Cr sintered HCCI’s wear resistance could be comparable to 20 wt% Cr sintered HCCI under impact energy 1~3 J/cm2, and it is more cost effective.

The Study on Abrasive Wear of Carbon of High Vanadium High Speed Steel Compared With That of High Chromium Cast Iron

2005 ◽  
Author(s):  
Shizhong Wei ◽  
Jinhua Zhu ◽  
Liujie Xu ◽  
Rui Long
Keyword(s):  
Cast Iron ◽  
Abrasive Wear ◽  
High Speed ◽  
Testing Machine ◽  
High Speed Steel ◽  
Wear Testing ◽  
Wear Property ◽  
High Chromium ◽  
High Chromium Cast Iron ◽  
Chromium Cast Iron

It is studied the carbons abrasive wear property of high vanadium high speed steel compared with that of general high chromium cast iron (Cr20) in this paper. The vanadium content is 10% in the high vanadium high speed steel, and it is a kind of new wear material that has been studied in the past ten years. In the experiment the three materials were used to resist the abrasive wear of Al2O3, the wear test was conducted on a ML-10 abrasive wear-testing machine. The abrasive surfaces, cross-section and sloping -section surfaces were scanned by means of a SEM (JSM-5160LV) device. The typical morphology photos of VC and Cr7C3 were taken in course of abrasive wear, which not only describe the different abrasive wear property of the carbons in the two materials, but also make the cause of the excellent wear property of this HSS clear. The research results have showed that the service lives (V10) are three times longer than that of high chromium cast iron (Cr20). The excellent wear resistance of high vanadium high-speed steel depends on the characters of high hardness, lumpy morphology of VC which are scattered in hard matrix of HSS.